RESUMO
Metal-organic frameworks (MOFs) containing redox active linkers have led to hybrid compounds exhibiting high electrical conductivity, which enables their use in applications in electronics and electrocatalysis. While many computational studies predict two-dimensional (2D) MOFs to be metallic, the majority of experiments show decreasing conductivity on cooling, indicative of a gap in the electronic band structure. To date, only a handful of MOFs have been reported that exhibit increased electrical conductivity upon cooling indicative of a metallic character, which highlights the need for a better understanding of the origin of the conductivity. A 2D MOF containing iron bis(dithiolene) motifs was recently reported to exhibit semiconducting behavior with record carrier mobility. Herein, we report that high crystallinity and the elimination of guest species results in an iron 2,3,6,7,10,11-tripheylenehexathiolate (THT) MOF, FeTHT, exhibiting a complex transition from semiconducting to metallic upon cooling, similar to what was shown for the analogous CoTHT. Remarkably, exposing the FeTHT to air significantly influences the semiconducting-to-metallic transition temperature (100 to 300 K) and ultimately results in a material showing metallic-like character at, and above, room temperature. This study indicates these materials can tolerate a substantial degree of doping that ultimately results in charge delocalization and metallic-like conductivity, an important step toward enabling their use in chemiresistive sensing and optoelectronics.
RESUMO
Two-dimensional (2D) metal-organic frameworks (MOFs) have received a great deal of attention due to their relatively high charge carrier mobility and low resistivity. Here we report on the temperature-dependent charge transport properties of a 2D cobalt 2,3,6,7,10,11-triphenylenehexathiolate framework. Variable temperature resistivity studies reveal a transition from a semiconducting to a metallic phase with decreasing temperature, which is unprecedented in MOFs. We find this transition to be highly dependent on the film thickness and the amount of solvent trapped in the pores, with density functional theory calculations of the electronic-structure supporting the complex metallic conductivity of the material. These results identify the first experimentally observed MOF that exhibits band-like metallic conductivity.
RESUMO
Hydrogen production through the reduction of water has emerged as an important strategy for the storage of renewable energy in chemical bonds. One attractive scenario for the construction of efficient devices for electrochemical splitting of water requires the attachment of stable and active hydrogen evolving catalysts to electrode surfaces, which remains a significant challenge. We demonstrate here the successful integration of cobalt dithiolene catalysts into a metal-organic surface to generate very active electrocatalytic cathode materials for hydrogen generation from water. These surfaces display high catalyst loadings and remarkable stability even under very acidic aqueous solutions.
RESUMO
Diphenylaminodiazidophosphane (C6H5)2NP(N3)2 was synthesized from the corresponding dihalides (C6H5)2NPX2 (X = F, Cl) and (CH3)3SiN3, and was characterized by vibrational and multinuclear NMR spectroscopy. The intermediate compound (C6H5)2NPF(N3) was also observed by NMR spectroscopy in solution. Some physical properties and reactions of all these compounds are discussed.
RESUMO
Recent discoveries involving the roles of nitric oxide in humans have stimulated intense interest in transition metal nitrosyl complexes. A series of dinitrosyl iron complexes with the formula [(DPPX)Fe(NO)2], {DPPX = 1,2-bis(diphenylphosphino)benzene (1), 1,3-bis(diphenylphosphino)propane (2), and cis-1,2-bis(diphenylphosphino)ethylene (3)} has been prepared and characterized through a combination of FT-IR, NMR, UV-vis, X-ray crystallography, and electrochemical techniques. Infrared spectroscopy showed NO shifts to the region of 1723 and 1674 cm-1 for complexes 1 and 3, and 1708 and 1660 cm-1 for 2, indicating that ligand 2 acts as a stronger σ-donor. The X-ray crystallographic data showed that 1 and 3 possess the rare repulso conformation while 2 has the attracto conformation. CV studies on compounds 1, 2 and 3 display two quasi-reversible oxidations with the E°1/2 values at 0.101 and 0.186 V, 0.121 and 0.184 V, and 0.019 and 0.342 V, respectively. The larger ΔE value for compound 2 compared with that of 1 and 3 is attributed to the lack of π-bonds between the two phosphorus atoms. Theoretical calculations using density functional theory were carried out on the synthesized compounds and model compounds and the results are consistent with the experimental data. The calculated HOMO-LUMO gaps for compounds 1, 2 and 3 are 3.736, 4.060, and 3.669 eV, respectively, which supports the stronger back-donation for compound 2 than that of compounds 1 and 3.
RESUMO
Synthesis and isolation of molecular building blocks of metal-organic frameworks (MOFs) can provide unique opportunities for characterization that would otherwise be inaccessible due to the heterogeneous nature of MOFs. Herein, we report a series of trinuclear cobalt complexes incorporating dithiolene ligands, triphenylene-2,3,6,7,10,11-hexathiolate (THT) (13+), and benzene hexathiolate (BHT) (23+), with 1,1,1,-tris(diphenylphosphinomethyl)ethane (triphos) employed as the capping ligand. Single crystal X-ray analyses of 13+ and 23+ display three five-coordinate cobalt centers bound to the triphos and dithiolene ligands in a distorted square pyramidal geometry. Cyclic voltammetry studies of 13+ and 23+ reveal three redox features associated with the formation of mixed valence states due to the sequential reduction of the redox-active metal centers (CoIII/II). Using this electrochemical data, the comproportionality values were determined for 1 and 2 (log Kc = 1.4 and 1.5 for 1, and 4.7 and 5.8 for 2), suggesting strong resonance-stabilized coupling of the metal centers, with stronger electronic coupling observed for complex 2 compared to that for complex 1. Cyclic voltammetry studies were also performed in solvents of varying polarity, whereupon the difference in the standard potentials (ΔE1/2) for 1 and 2 was found to shift as a function of the polarity of the solvent, indicating a negative correlation between the dielectric constant of the electrochemical medium and the stability of the mixed valence species. Spectroelectrochemical studies of in situ generated multi-valent (MV) states of complexes 1 and 2 display characteristic NIR intervalence charge transfer (IVCT) bands, and analysis of the IVCT transitions for complex 2 suggests a weakly coupled class II multi-valent species and relatively large electronic coupling factors (1700 cm-1 for the first multi-valent state of 22+, and 1400 and 4000 cm-1 for the second multi-valent state of 2+). Density functional theory (DFT) calculations indicate a significant deviation in relative energies of the frontier orbitals of complexes 13+, 23+, and 3+ that contrasts those calculated for the analogous trinuclear cobalt dithiolene complexes employing pentamethylcyclopentadienyl (Cp*) as the capping ligand (Co3Cp*3THT and Co3Cp*3BHT, respectively), and may be a result of the cationic nature of complexes 13+, 23+, and 3+.
RESUMO
The design of earth-abundant catalysts for the electrochemical production of H2 from water is important for the realization of a sustainable energy future. Incorporation of molecular catalysts into extended frameworks has emerged as a viable strategy for improving catalytic performance and durability while maintaining a high degree of control over the structure and properties of the catalytic active site. Here, we investigate benzenehexathiolate (BHT) coordination frameworks as electrocatalysts for the hydrogen evolution reaction (HER) in pH 1.3 aqueous solutions. The electrocatalytic HER activity of BHT-based coordination frameworks follows the order of CoBHT > NiBHT > FeBHT. CoBHT operates at an overpotential of 185 mV, the lowest observed overpotential of the reported metal dithiolene-based metal organic frameworks and coordination polymers to date. To further understand the properties that dictate electrocatalytic activity, the effect of film thickness on the HER performance of CoBHT, a parameter that has not been extensively explored for electrocatalytic coordination frameworks, was examined. As the thickness was increased to â¼1 µm, charge and proton transfer through CoBHT was hindered, the number of electrochemically accessible active sites decreased, and the mechanical robustness of the modified electrode was diminished. The observed thickness-dependent HER activity of CoBHT highlights the importance of practical electrode construction and offers insight into how to optimize proton and electron transfer properties and active site densities within coordination frameworks without reducing the mechanical robustness of the immobilized catalysts.
RESUMO
The growth of crystalline compound semiconductors on amorphous and non-epitaxial substrates is a fundamental challenge for state-of-the-art thin-film epitaxial growth techniques. Direct growth of materials on technologically relevant amorphous surfaces, such as nitrides or oxides results in nanocrystalline thin films or nanowire-type structures, preventing growth and integration of high-performance devices and circuits on these surfaces. Here, we show crystalline compound semiconductors grown directly on technologically relevant amorphous and non-epitaxial substrates in geometries compatible with standard microfabrication technology. Furthermore, by removing the traditional epitaxial constraint, we demonstrate an atomically sharp lateral heterojunction between indium phosphide and tin phosphide, two materials with vastly different crystal structures, a structure that cannot be grown with standard vapor-phase growth approaches. Critically, this approach enables the growth and manufacturing of crystalline materials without requiring a nearly lattice-matched substrate, potentially impacting a wide range of fields, including electronics, photonics, and energy devices.