RESUMO
The metastable wurtzite crystal phase in gallium phosphide (WZ GaP) is a relatively new structure with little available information about its emission properties compared to the most stable zinc-blend phase. Here, the effect of growth conditions of WZ GaP nano- and microstructures obtained via chemical beam epitaxy on the optical properties was studied using power- and temperature-dependent photoluminescence (PL). We showed that the PL spectra are dominated by two strong broad emission bands at 1.68 and 1.88 eV and two relatively narrow peaks at 2.04 and 2.09 eV. The broad emissions are associated with the presence of carbon and a small number of extended crystal defects, respectively. For the sharp emissions, two main radiative recombination channels were observed with ionization energies estimated in the range of 50-80 meV and lower than 10 meV. No variation of the low-temperature PL spectra was observed for samples grown at different P precursor flows, while increasing Ga content enhanced the dominant broad emission at around 1.68 eV, suggesting that the group III organometallic precursor is the main source of impurities. Finally, Be-doped samples were grown, and their characteristic optical emission at 2.03 eV was identified. These results contribute to the understanding of impurity-related luminescence in hexagonal GaP, being useful for further crystal growth optimization required for the fabrication of optoelectronic devices.
RESUMO
To evaluate the flexural strength (FS) and flexural modulus (FM) of a commercial 3Y-TZ0P ceramic after artificial aging and either without or with two application times of non-thermal plasma treatments (NTP). In addition, changes in crystalline phase transformation and surface nano-topography after NTP application, during different aging periods, were evaluated. Ninety 3Y-TZP bars (45x4x3 mm) were made for FS and FM testing, and assigned to nine groups (n=10): no NTP/no aging (Control); no NTP/4h aging; no NTP/30h aging; 10s NTP/no aging; 10s NTP/4h aging; 10s NTP/30h aging; 60s NTP/no aging; 60s NTP/4h aging and 60s NTP/30h aging. Artificial accelerated aging was simulated using an autoclave (134º C at 2 bar) for up to 30h. FS and FM were assessed using a universal testing machine and data analyzed using a ANOVA and Tukey test (α=0.05). The volume change in zirconia monoclinic phase (MPV) was evaluated using X-ray diffraction and surface nano-topography was assessed using atomic force microscopy (baseline until 30h-aging). NTP application did not influence the FS and FM of zirconia. Compared to the Control (no NTP/no aging), the FS of zirconia samples treated for 30 hours in autoclave ("no NTP/30h aging" group) increased. Artificial aging for 30 hours significantly increased the FM of zirconia, regardless of NTP application. MPV tended to increase following the increase in aging time, which might result in the surface irregularities observed at 30h-aging. NTP did not alter the zirconia properties tested, but 30h-aging can change the zirconia FS, FM and MPV.
Assuntos
Gases em Plasma , Materiais Dentários/química , Argônio , Teste de Materiais , Propriedades de Superfície , Zircônio/química , Cerâmica/química , Ítrio/químicaRESUMO
Abstract To evaluate the flexural strength (FS) and flexural modulus (FM) of a commercial 3Y-TZ0P ceramic after artificial aging and either without or with two application times of non-thermal plasma treatments (NTP). In addition, changes in crystalline phase transformation and surface nano-topography after NTP application, during different aging periods, were evaluated. Ninety 3Y-TZP bars (45x4x3 mm) were made for FS and FM testing, and assigned to nine groups (n=10): no NTP/no aging (Control); no NTP/4h aging; no NTP/30h aging; 10s NTP/no aging; 10s NTP/4h aging; 10s NTP/30h aging; 60s NTP/no aging; 60s NTP/4h aging and 60s NTP/30h aging. Artificial accelerated aging was simulated using an autoclave (134º C at 2 bar) for up to 30h. FS and FM were assessed using a universal testing machine and data analyzed using a ANOVA and Tukey test (α=0.05). The volume change in zirconia monoclinic phase (MPV) was evaluated using X-ray diffraction and surface nano-topography was assessed using atomic force microscopy (baseline until 30h-aging). NTP application did not influence the FS and FM of zirconia. Compared to the Control (no NTP/no aging), the FS of zirconia samples treated for 30 hours in autoclave ("no NTP/30h aging" group) increased. Artificial aging for 30 hours significantly increased the FM of zirconia, regardless of NTP application. MPV tended to increase following the increase in aging time, which might result in the surface irregularities observed at 30h-aging. NTP did not alter the zirconia properties tested, but 30h-aging can change the zirconia FS, FM and MPV.
Resumo Avaliar a resistência à flexão (FS) e o módulo de flexão (FM) de uma cerâmica comercial 3Y-TZP após envelhecimento artificial, e com ou sem dois tempos de aplicação de plasma não térmico (NTP). Além disso, a transformação de fase cristalina e a nano-topografia de superfície após a aplicação de NTP, durante diferentes períodos de envelhecimento, foram avaliadas. Noventa barras 3Y-TZP (45x4x3 mm) foram feitas para testes de FS e FM, e distribuídas em nove grupos (n=10): sem NTP/sem envelhecimento (Controle); sem NTP/4h de envelhecimento; sem NTP/30h de envelhecimento; 10sNTP/sem envelhecimento; 10sNTP/4h; 10sNTP/30h; 60sNTP/sem envelhecimento; 60sNTP/4h e 60sNTP/30h. O envelhecimento artificial acelerado foi simulado em autoclave (134º C a 2 bar) por até 30 horas. FS e FM foram avaliados em máquina de ensaio universal e os dados analisados pela ANOVA e teste de Tukey (α = 0,05). A mudança de volume da fase monoclínica de zircônia (MPV) foi avaliada usando difração de raios-X e nano-topografia de superfície foi avaliada utilizando microscopia de força atômica (baseline até 30h). A aplicação do NTP não influenciou a FS e FM da zircônia. Comparado ao Controle ("sem NTP/sem envelhecimento"), a FS das amostras de zircônia tratadas por 30 horas em autoclave ("sem NTP/30h de envelhecimento") aumentou. O envelhecimento artificial por 30 horas aumentou significativamente a FM da zircônia, independente do tempo de aplicação do NTP. O MPV tendeu a aumentar em função do aumento do tempo de envelhecimento para todos os grupos, que pode ter resultado nas irregularidades superficiais observadas com 30 horas de envelhecimento. O NTP não afetou as propriedades da zircônia testadas, mas o envelhecimento por 30 horas pode alterar a FS, FM e MPV da zircônia.
RESUMO
The adhesion force between the tip of an atomic force microscope cantilever derivatized with nimodipine (a calcium blocker, from the dihydropyridine class, currently used in clinical medicine for hypertension) and living cells of Saccharomyces cerevisiae (unicellular eukaryotes which portray ultrastructural features characteristic of higher eukaryotic cells) was measured. This methodology allowed us to locate (and visualize) pores on the cell surface which may be responsible for calcium transportation in the living cells. The interaction of the cantilever derivatized with the calcium blocker and a pore, which can be a calcium channel, is more intense than a non-derivatized cantilever and the pore. Outside the pore (on the rest of cell surface), a derivatized or a non-derivatized cantilever has the same pattern of adhesion force. The information obtained with this method is very important for the design of new, more potent and less toxic drugs for pharmacological use.
Assuntos
Bloqueadores dos Canais de Cálcio/metabolismo , Canais de Cálcio/metabolismo , Microscopia de Força Atômica/métodos , Nimodipina/metabolismo , Técnicas Biossensoriais , Sinalização do Cálcio , Adesão Celular , Membrana Celular/metabolismo , Receptores de Droga/metabolismo , Saccharomyces cerevisiae/metabolismo , Saccharomyces cerevisiae/ultraestruturaRESUMO
Superfícies de aço inoxidável com especificações determinadas pela American Society for Testing and Materials (ASTM) são usadas em testes in vitro para simular a formação e a remoção de biofilmes. Muitas vezes estas superfícies são reutilizadas nos ensaios de formação de biofilmes. O objetivo deste trabalho foi avaliar se cupons de aço inoxidável anteriormente utilizados para formação de biofilmes multiespécies podem ser reutilizados em novos ensaios. Assim, cupons submetidos a diferentes procedimentos de higienização foram analisados por microscopia eletrônica de varredura (MEV) e perfilometria . A reutilização das superfícies em novos experimentos deve ser realizada com cautela, aplicando procedimentos que removam as células bacterianas e a substância polimérica extracelular (EPS) aderidas na superfície. Além disso, observações da superfície (topografia e rugosidade) devem ser avaliadas, comprovando as especificações da ASTM.