Dynamic Tilting of Ferroelectric Domain Walls Caused by Optically Induced Electronic Screening.

Optical excitation perturbs the balance of phenomena selecting the tilt orientation of domain walls within ferroelectric thin films. The high carrier density induced in a low-strain BaTiO_{3} thin film by an above-band-gap ultrafast optical pulse changes the tilt angle that 90° a/c domain walls form with respect to the substrate-film interface. The dynamics of the changes are apparent in time-resolved synchrotron x-ray scattering studies of the domain diffuse scattering. Tilting occurs at 298 K, a temperature at which the a/b and a/c domain phases coexist but is absent at 343 K in the better ordered single-phase a/c regime. Phase coexistence at 298 K leads to increased domain-wall charge density, and thus a larger screening effect than in the single-phase regime. The screening mechanism points to new directions for the manipulation of nanoscale ferroelectricity.

A rhombohedral ferroelectric phase in epitaxially strained Hf0.5Zr0.5O2 thin films.

Hafnia-based thin films are a favoured candidate for the integration of robust ferroelectricity at the nanoscale into next-generation memory and logic devices. This is because their ferroelectric polarization becomes more robust as the size is reduced, exposing a type of ferroelectricity whose mechanism still remains to be understood. Thin films with increased crystal quality are therefore needed. We report the epitaxial growth of Hf0.5Zr0.5O2 thin films on (001)-oriented La0.7Sr0.3MnO3/SrTiO3 substrates. The films, which are under epitaxial compressive strain and predominantly (111)-oriented, display large ferroelectric polarization values up to 34 µC cm-2 and do not need wake-up cycling. Structural characterization reveals a rhombohedral phase, different from the commonly reported polar orthorhombic phase. This finding, in conjunction with density functional theory calculations, allows us to propose a compelling model for the formation of the ferroelectric phase. In addition, these results point towards thin films of simple oxides as a vastly unexplored class of nanoscale ferroelectrics.

Periodicity-Doubling Cascades: Direct Observation in Ferroelastic Materials.

Very sensitive responses to external forces are found near phase transitions. However, transition dynamics and preequilibrium phenomena are difficult to detect and control. We have observed that the equilibrium domain structure following a phase transition in ferroelectric and ferroelastic BaTiO_{3} is attained by halving of the domain periodicity multiple times. The process is reversible, with periodicity doubling as temperature is increased. This observation is reminiscent of the period-doubling cascades generally observed during bifurcation phenomena, and, thus, it conforms to the "spatial chaos" regime earlier proposed by Jensen and Bak [Phys. Scr. T 9, 64 (1985)PHSTER0281-184710.1088/0031-8949/1985/T9/009] for systems with competing spatial modulations.

Highly Sensitive Protein Detection by Asymmetric Mach-Zehnder Interferometry for Biosensing Applications.

The sensitivity and performance of an asymmetric Mach-Zehnder interferometer (aMZI) were compared to those of quartz crystal microbalance with dissipation (QCM-D). The binding of streptavidin to sensor chips coated with poly-l-lysine (PLL), modified with biotin and oligoethyleneglycol (OEG) (PLL-biotin), was used to compare the binding signals obtained from both technologies. PLL-biotin proved to be an efficient method to add bioreceptors to both the QCM-D and aMZI chips. The final, saturated value of streptavidin binding was compared with those from aMZI (253 ng cm-2) and QCM-D (460 ng cm-2). These values were then used to evaluate that 45% of the measured streptavidin mass in the QCM-D came from hydrodynamically coupled water. Importantly, the signal-to-noise ratio of the aMZI was found to be 200 times higher than that of the QCM-D. These results indicate the potential of the aMZI platform for highly sensitive and accurate biosensing applications.

Understanding the Role of Ferroelastic Domains on the Pyroelectric and Electrocaloric Effects in Ferroelectric Thin Films.

Temperature- and electric-field-induced structural transitions in a polydomain ferroelectric can have profound effects on its electrothermal susceptibilities. Here, the role of such ferroelastic domains on the pyroelectric and electrocaloric response is experimentally investigated in thin films of the tetragonal ferroelectric PbZr0.2 Ti0.8 O3 . By utilizing epitaxial strain, a rich set of ferroelastic polydomain states spanning a broad thermodynamic phase space are stabilized. Using temperature-dependent scanning-probe microscopy, X-ray diffraction, and high-frequency phase-sensitive pyroelectric measurements, the propensity of domains to reconfigure under a temperature perturbation is quantitatively studied. In turn, the "extrinsic" contributions to pyroelectricity exclusively due to changes between the ferroelastic domain population is elucidated as a function of epitaxial strain. Further, using highly sensitive thin-film resistive thermometry, direct electrocaloric temperature changes are measured on these polydomain thin films for the first time. The results demonstrate that temperature- and electric-field-driven domain interconversion under compressive strain diminish both the pyroelectric and the electrocaloric effects, while both these susceptibilities are enhanced due to the exact-opposite effect from the extrinsic contributions under tensile strain.