Biomechanical comparison of different surface modifications for dental implants.

PURPOSE: A satisfactory clinical outcome in dental implant treatment relies on primary stability for immediate load bearing. While the geometric design of an implant contributes to mechanical stability, the nature of the implant surface itself is also critically important. Biomechanical and microcomputerized tomographic evaluation of implant osseointegration was performed to compare alternative structural, chemical and biochemical, and/or pharmaceutical surface treatments applied to an identical established implant design. MATERIALS AND METHODS: Dental implants with the same geometry but with 6 different surface treatments were tested in vivo in a sheep model (pelvis). Peri-implant bone density and removal torque were compared at 2, 4, and 8 weeks after implantation. Implant surfaces tested were: sandblasted and acid-etched titanium (Ti), sandblasted and etched zirconia, Ti coated with calcium phosphate (CaP), Ti modified via anodic plasma-chemical treatment (APC), bisphosphonate-coated Ti (Ti + Bisphos), and Ti coated with collagen containing chondroitin sulfate (CS). RESULTS: All dental implants were well integrated at the time of sacrifice. There were no significant differences observed in peri-implant bone density between implant groups. After 8 weeks of healing, removal torque values for Ti, Ti + CaP, Ti + Bisphos, and Ti + collagen + CS were significantly higher than those for zirconia and Ti + APC. CONCLUSIONS: Whereas the sandblasted/acid-etched Ti implant can still be considered the reference standard surface for dental implants, functional surface modifications such as bisphosphonate or collagen coating seem to enhance early peri-implant bone formation and should be studied further.

Short-term microvascular response of striated muscle to cp-Ti, Ti-6Al-4V, and Ti-6Al-7Nb.

Due to excellent mechanical properties and good corrosion resistance, titanium-aluminium-vanadium (Ti-6Al-4V) and titanium-aluminium-niobium (Ti-6Al-7Nb) are extensively used for orthopedic surgery. Concern has been voiced concerning the implications of the constituent vanadium in Ti-6Al-4V on the surrounding environment. Particularly in osteosynthesis where the alloys stand in direct contact to skeletal muscle, undesirable biologic reactions may have severe consequences. In a comparative study, we assessed in vivo nutritive perfusion and leukocytic response of striated muscle to the metals Ti-6Al-4V, Ti-6Al-7Nb, and commercially pure titanium (cpTi), thereby drawing conclusions on their short-term inflammatory potential. In 28 hamsters, utilizing the dorsal skinfold chamber preparation and intravital microscopy, we quantified primary and secondary leukocyte-endothelial cell interaction, leukocyte extravasation, microvascular diameter change, and capillary perfusion in collecting and postcapillary venules of skeletal muscle. A manifest discrepancy between the metals concerning impact on local microvascular parameters was not found. All metals induced an only transient and moderate inflammatory response. Only a slight increase in leukocyte recruitment and a more sluggish recuperation of inflammatory parameters in animals treated with Ti-6Al-4V compared to the other two metals suggested a minor, overall not significant discrepancy in biocompatibility. Gross toxicity of bulk Ti-6Al-4V on surrounding tissue could not be found. Conclusively, the commonly used biomaterials Ti-6Al-4V, Ti-6Al-7Nb, and cpTi induce an only transient inflammatory answer of the skeletal muscle microvascular system. Our results indicate that on the microvascular level the tested bulk Ti-alloys and cpTi do not cause adverse biologic reactions in striated muscle.