RESUMO
A method is described for the synthesis of rigid, macroporous polymers (monoliths) to be used as stationary phases in capillary electrochromatography (CEC). The procedure reproducibly results in columns with good mechanical and chemical stability. Once the procedure was optimized, it yielded the desired CEC columns in nearly 100% of the cases. The batch-to-batch standard deviation of the migration of the electroosmotic flow (EOF) marker for nine randomly chosen columns was 5%. The polymerization is carried out inside the capillary, an aqueous phase is used as solvent. Monomers based on acrylamides with varying hydrophilicity were used to introduce the interactive moieties together with piperazine diacrylamide as cross-linker and vinylsulfonic acid as provider of the charged, EOF-producing moieties. The pore size of the monoliths was adjusted by adding varying amounts of ammonium sulfate to the reaction mixture. In this manner, the average pore size of a given monolith could be reproducibly adjusted to values ranging from 50 nm to 1.3 microm. The procedure was optimized for four particular types of monoliths, which differed in hydrophobicity. The latter was adjusted by introducing suitable co-monomers, such as alkyl chain-bearing molecules, into the monolithic structure. Attempts to systematically investigate the chromatographic behavior of the monolithic stationary phases were made, using a model mixture of aromatic compounds as sample. The standard deviations for the run-to-run reproducibility of the retention times for unretained and retained analytes were <1.5%. Flat Van Deemter curves were measured even at elevated flow-rates (2 mm/s). Plate heights between 10 and 15 microm were measured in this range. The retention order was taken as the principal indication for the chromatographic mode. The separation was found to be governed neither by pure reversed-phase nor by pure normal-phase chromatography, even on monoliths, where large amounts of C6 ligands had been introduced.