Paper-based microfluidic devices for analysis of clinically relevant analytes present in urine and saliva.

We report the use of paper-based microfluidic devices fabricated from a novel polymer blend for the monitoring of urinary ketones, glucose, and salivary nitrite. Paper-based devices were fabricated via photolithography in less than 3 min and were immediately ready for use for these diagnostically relevant assays. Patterned channels on filter paper as small as 90 microm wide with barriers as narrow as 250 microm could be reliably patterned to permit and block fluid wicking, respectively. Colorimetric assays for ketones and nitrite were adapted from the dipstick format to this paper microfluidic chip for the quantification of acetoacetate in artificial urine, as well as nitrite in artificial saliva. Glucose assays were based on those previously demonstrated (Martinez et al., Angew Chem Int Ed 8:1318-1320, 1; Martinez et al., Anal Chem 10:3699-3707, 2; Martinez et al., Proc Nat Acad Sci USA 50:19606-19611, 3; Lu et al., Electrophoresis 9:1497-1500, 4; Abe et al., Anal Chem 18:6928-6934, 5). Reagents were spotted on the detection pad of the paper device and allowed to dry prior to spotting of samples. The ketone test was a two-step reaction requiring a derivitization step between the sample spotting pad and the detection pad, thus for the first time, confirming the ability of these paper devices to perform online multi-step chemical reactions. Following the spotting of the reagents and sample solution onto the paper device and subsequent drying, color images of the paper chips were recorded using a flatbed scanner, and images were converted to CMYK format in Adobe Photoshop CS4 where the intensity of the color change was quantified using the same software. The limit of detection (LOD) for acetoacetate in artificial urine was 0.5 mM, while the LOD for salivary nitrite was 5 microM, placing both of these analytes within the clinically relevant range for these assays. Calibration curves for urinary ketone (5 to 16 mM) and salivary nitrite (5 to 2,000 microM) were generated. The time of device fabrication to the time of test results was about 25 min.

Synthesis and characterization of a poly(dimethylsiloxane)-poly(ethylene oxide) block copolymer for fabrication of amphiphilic surfaces on microfluidic devices.

A poly(dimethylsiloxane)-poly(ethylene oxide) (PDMS-PEO) vinyl terminated block copolymer has been synthesized via a simple hydrosilylation reaction between hydride-terminated PDMS and PEO divinyl ether. This prepolymer can be subsequently cross-linked into an elastomer in a second hydrosilylation reaction involving a methylhydrosiloxane-dimethylsiloxane copolymer, forming a material suitable for the purposes of fabricating microfluidic devices. The presence of the PEO block in the prepolymer chain results in a much more hydrophilic material following cross-linking. The surface water contact angle of the PDMS-PEO material is 65 degrees +/- 3 (n = 6), as opposed to approximately 110 degrees for native PDMS. Droplets of water straddled by air within molded channels of the PDMS-PEO are concave in shape with contact angles where the fluid meets the side walls of 32 degrees +/- 4 (n = 8), while droplets in PDMS microchannels are more convex with contact angles of 95 degrees +/- 6 (n = 6). The length of the PDMS-PEO prepolymer chain and the multifunctional hydride cross-linker chains appear to dictate the durability of the elastomeric material. Young's modulus measurements yielded values of 0.94 +/- 0.08, 2.6 +/- 0.8, and 1.91 +/- 0.06 MPa for a [5% vinyl excess prepolymer and 10-fold excess of cross-linker], [10% vinyl excess prepolymer and 5-fold excess of cross-linker], and 10:1 PDMS, respectively, confirming that the elasticity of the cross-linked PDMS-PEO is similar to that of PDMS (Sylgard 184:10:1 mixture of elastomeric base to elastomer curing agent). The PDMS-PEO material still possesses enough PDMS character to allow molded channel architectures to be sealed between two pieces of the block copolymer by conformal contact. As a result of the more hydrophilic nature of the material, the channels of devices fabricated from this polymer are self-filling when using aqueous buffers, making it more user-friendly than PDMS for applications calling for background electrolytes void of organic modifiers. Different compositions of PDMS-PEO devices feature different electroosmotic flow values with the 5% vinyl excess prepolymer EOF values of 2.5 +/- 0.7 x 10(-4) and 5.7 +/- 0.8 x 10(-4) cm(2)/(V s) at pHs 6 and 9, respectively, and 1.2 +/- 0.3 x 10(-4) and 2.5 +/- 0.3 x 10(-4) cm(2)/(V s) for the 10% vinyl excess prepolymer device at pHs 6 and 9, respectively.