RESUMO
The search for excellent cathodes for lithium batteries is the main topic in order to meet the requirements of low cost, high safety, and high capacity in many real applications. ß-MnO2, as a potential candidate, has attracted great attention because of its high stability and potential high capacity among all the phases. Because of the complexity of ß-MnO2, some fundamental questions at the atomic level during the charge-discharge process, remain unclear. The lithiation process of ß-MnO2 has been systematically examined by first-principles calculations along with cluster expansion techniques. Five stable configurations during the lithium intercalation process are firstly determined, and the electrochemical voltages are from 3.47 to 2.77 eV, indicating the strongly correlated effects of the ß-MnO2-LiMnO2 system. During the lithiation process, the changes in the lattice parameters are not symmetric. The analysis of electronic structures shows that Mn ions are in the mixed valence states of Mn(3+) and Mn(4+) during the lithiation process, which results in Jahn-Teller distortion in Mn(3+)O6 octahedra. Such results uncover the intrinsic origin of the asymmetric deformation during the charge-discharge process, resulting in the irreversible capacity fading during cycling. From the analysis of the thermal reduction of delithiated LixMnO2, the formation of oxygen is thermodynamically infeasible in the whole extraction process. Our results indicate that ß-MnO2 has great potential as a cathode material for high capacity Li-ion batteries.
RESUMO
Stable nanotriangles of monolayer transitional metal dichalcogenides (referred herein as MS2 mNTs) grown via ordinary deposition conditions, where M = Mo or W, exhibit a peculiar 3-fold periodic size-dependence in electronic and chemical properties. For " k" being the number of M atoms per edge, mNTs are (a) intrinsic-semiconducting when k = 3 i + 1, such as k = 7, 10, 13, 16; (b) metallic-like with no bandgap when k = 3 i; (c) n+ semiconducting when k = 3 i - 1. Besides changes in electronic properties, the catalytic properties for hydrogen evolution reaction also switch from active for k = 3 i and 3 i - 1 to inactive for k = 3 i + 1. The peculiar periodic size-dependence roots from the chemistry of edge-reconstruction and the consequential evolution of band structure. Further, such chemistry and thereby the size-dependence can be manipulated by adding or depleting the atomic concentration of sulfur atoms along the mNT edges.