Designing High Entropy Bulk Metallic Glass (HE-BMG) by Similar Element Substitution/Addition.

In this paper, we report that two newly designed high entropy bulk metallic glasses (HE-BMGs), Ti20Hf20Cu20Ni20Be20 with a critical diameter of 2 mm, and Ti16.7Zr16.7Nb16.7Cu16.7Ni16.7Be16.7 with a critical diameter of 1.5 mm, can be fabricated by copper mold casting method. These newly developed HE-BMGs exhibited a high fracture strength over 2300 MPa. The glass forming ability and atomic size distribution characteristics of the HE-BMGs are discussed in detail. Moreover, a parameter δ' was proposed to evaluate the atomic size distribution characteristics in different HEAs. It showed that this new parameter is closely related to the degree of lattice distortion and phase selection of high-entropy alloys. Adjusting the value of δ' parameter by similar element substitution/addition would be beneficial for designing high entropy bulk metallic glasses.

High-entropy induced a glass-to-glass transition in a metallic glass.

Glass-to-glass transitions are useful for us to understand the glass nature, but it remains difficult to tune the metallic glass into significantly different glass states. Here, we have demonstrated that the high-entropy can enhance the degree of disorder in an equiatomic high-entropy metallic glass NbNiZrTiCo and elevate it to a high-energy glass state. An unusual glass-to-glass phase transition is discovered during heating with an enormous heat release even larger than that of the following crystallization at higher temperatures. Dramatic atomic rearrangement with a short- and medium-range ordering is revealed by in-situ synchrotron X-ray diffraction analyses. This glass-to-glass transition leads to a significant improvement in the modulus, hardness, and thermal stability, all of which could promote their applications. Based on the proposed high-entropy effect, two high-entropy metallic glasses are developed and they show similar glass-to-glass transitions. These findings uncover a high-entropy effect in metallic glasses and create a pathway for tuning the glass states and properties.

Porous composite architecture bestows Fe-based glassy alloy with high and ultra-durable degradation activity in decomposing azo dye.

Since the treatment of wastewater containing azo dye presents problems worldwide, it is important to seek effective materials and technology for the purification of wastewater containing azo dye. Fe-based metallic glasses have been identified as promising materials for the decomposition of dyeing wastewater due to their high chemical activity resulting from their amorphous structure. It is imperative to further improve their degradation performance, and especially their durability, for potential application in wastewater purification. Here, composite structures constructed of porous Ni and amorphous Fe78Si9B13 powder with markedly enhanced degradation performance in Orange II solution were obtained by utilizing a magnet. Due to the favorable effects of structural electrocatalysis and high dispersity of the distinctive porous architecture in addition to its self-cleaning properties, the solid-liquid interface exhibited strong, continuous electrical and mass transport, and a compelling improvement in degradation performance was achieved. Based on degradation tests and spectrum analysis, the kinetic rate was improved over 11-fold. Moreover, ultra-high durability over 100 cycles was revealed in cycling tests. The results indicate that wastewater degradation performance can be greatly enhanced by properly combining Fe-based metallic glasses with porous material.