We report on infrared supercontinuum generation extending over more than one octave of bandwidth, from 850 nm to 2.35 µm, produced in a single spatial mode from a robust, compact, composite chalcogenide glass nanotaper. A picosecond laser at 1.55 µm pumps a high-index-contrast, all-solid nanotaper that strongly confines the field to a 480 nm diameter core, while a thermally compatible built-in polymer jacket lends the nanotaper mechanical stability.
RESUMO
Physical vapor deposition of organic explosives enables growth of polycrystalline films with a unique microstructure and morphology compared to the bulk material. This study demonstrates the ability to control crystal orientation and porosity in pentaerythritol tetranitrate films by varying the interfacial energy between the substrate and the vapor-deposited explosive. Variation in density, porosity, surface roughness, and optical properties is achieved in the explosive film, with significant implications for initiation sensitivity and detonation performance of the explosive material. Various surface science techniques, including angle-resolved X-ray photoelectron spectroscopy and multiliquid contact angle analysis, are utilized to characterize interfacial characteristics between the substrate and explosive film. Optical microscopy and scanning electron microscopy of pentaerythritol tetranitrate surfaces and fracture cross sections illustrate the difference in morphology evolution and the microstructure achieved through surface energy modification. X-ray diffraction studies with the Tilt-A-Whirl three-dimensional pole figure rendering and texture analysis software suite reveal that high surface energy substrates result in a preferred (110) out-of-plane orientation of pentaerythritol tetranitrate crystallites and denser films. Low surface energy substrates create more randomly textured pentaerythritol tetranitrate and lead to nanoscale porosity and lower density films. This work furthers the scientific basis for interfacial engineering of polycrystalline organic explosive films through control of surface energy, enabling future study of dynamic and reactive detonative phenomena at the microscale. Results of this study also have potential applications to active pharmaceutical ingredients, stimuli-responsive polymer films, organic thin film transistors, and other areas.