Piezoelectric actuators transform electrical energy into mechanical energy, and because of their compactness, quick response time and accurate displacement, they are sought after in many applications. Polycrystalline piezoelectric ceramics are technologically more appealing than single crystals due to their simpler and less expensive processing, but have yet to display electrostrain values that exceed 1%. Here we report a material design strategy wherein the efficient switching of ferroelectric-ferroelastic domains by an electric field is exploited to achieve a high electrostrain value of 1.3% in a pseudo-ternary ferroelectric alloy system, BiFeO3-PbTiO3-LaFeO3. Detailed structural investigations reveal that this electrostrain is associated with a combination of several factors: a large spontaneous lattice strain of the piezoelectric phase, domain miniaturization, a low-symmetry ferroelectric phase and a very large reverse switching of the non-180° domains. This insight for the design of a new class of polycrystalline piezoceramics with high electrostrains may be useful to develop alternatives to costly single-crystal actuators.
RESUMO
Lead-free BiFeO3-BaTiO3 (BF-BT) piezoceramics have sparked considerable interest in recent years due to their high piezoelectric performance and high Curie temperature. In this paper, we show how the addition of highly aligned porosity (between 40 and 60 vol %) improves the piezoelectric performance, sensing, and energy harvesting figures of merit in freeze-cast 0.70BiFeO3-0.30BaTiO3 piezoceramics compared to conventionally processed, nominally dense samples of the same composition. The dense and porous BF-BT ceramics had similar longitudinal piezoelectric coefficients (d33) immediately after poling, yet the dense samples were observed to age faster than those of porous ceramics. After 24 h, for example, the porous samples had significantly higher d33 values ranging from 112 to 124 pC/N, compared to 85 pC/N for the dense samples. Porous samples exhibited 3 and 5 times higher longitudinal piezoelectric voltage coefficient g33 and energy harvesting figure of merit d33g33 than dense samples due to the unexpected increase in d33 and decrease in relative permittivity with porosity. Spontaneous polarization (Ps) and remnant polarization (Pr) decrease as the porosity content increased from 37 to 59 vol %, as expected due to the lower volume of active material; however, normalized polarization values with respect to porosity level showed a slight increase in the porous materials relative to the dense BF-BT. Furthermore, the porous ceramics showed improved temperature-dependent strain-field response compared to the dense. As a result, these porous materials show excellent potential for use in high temperature sensing and harvesting applications.