Effect of heat treatment on the morphology of carbon fibers doped with Co2p nanoparticles.

ABSTRACT: Carbon fibers (CFs) decorated by Co2P nanoparticles and carbon nanotubes were prepared via needle-less electrospinning technique. Formation of catalytically active Co2P nanoparticles and growth of carbon nanotubes were monitored in open and closed sintering environment at different sintering exposure times. Higher porosity, important in the catalytic reaction for easier penetration of electrolyte into the CFs, was achieved by mixing two immiscible polymers with natrium dodecyl sulfate and subsequent heat treatment process. Structure and morphology of the prepared modified carbon fibers were characterized by XRD, SEM and TEM. The time of heat exposure at the sintering temperature of 1200 °C and closure of the sintering space showed distinct effect on the growth and shape of carbon nanotubes. SEM and Raman spectroscopy revealed that closure of the system led to the formation of carbon nanotubes with smaller diameters and less structural disorder. Comparing of as-prepared CFs revealed that CFs with Co2P sintered in the closed system exhibited the best electrocatalytic activity for hydrogen evolution reaction due to lower overpotential and smaller Tafel slope in acidic solution.

Novel Cu(II)-based metal-organic framework STAM-1 as a sulfur host for Li-S batteries.

Due to the increasing demand for energy storage devices, the development of high-energy density batteries is very necessary. Lithium-sulfur (Li-S) batteries have gained wide interest due to their particularly high-energy density. However, even this type of battery still needs to be improved. Novel Cu(II)-based metal-organic framework STAM-1 was synthesized and applied as a composite cathode material as a sulfur host in the lithium-sulfur battery with the aim of regulating the redox kinetics of sulfur cathodes. Prepared STAM-1 was characterized by infrared spectroscopy at ambient temperature and after in-situ heating, elemental analysis, X-ray photoelectron spectroscopy and textural properties by nitrogen and carbon dioxide adsorption at - 196 and 0 °C, respectively. Results of the SEM showed that crystals of STAM-1 created a flake-like structure, the surface was uniform and porous enough for electrolyte and sulfur infiltration. Subsequently, STAM-1 was used as a sulfur carrier in the cathode construction of a Li-S battery. The charge/discharge measurements of the novel S/STAM-1/Super P/PVDF cathode demonstrated the initial discharge capacity of 452 mAh g-1 at 0.5 C and after 100 cycles of 430 mAh g-1, with Coulombic efficiency of 97% during the whole cycling procedure at 0.5 C. It was confirmed that novel Cu-based STAM-1 flakes could accelerate the conversion of sulfur species in the cathode material.