The toxicity of viologens can be significantly reduced by including them in tight [2]rotaxane structures alongside ß-cyclodextrin, thus turning them into candidates of pharmaceutical interest. Here, we report a synthesis pathway for a benign viologen, by capping a small ß-cyclodextrin-caged molecule, the 4,4'-bipyridine, with minimal-length presynthesized axle-stopper segments of the propyl-3-pentamethyldisiloxane type. After 90 min from the oral administration to laboratory mice, the product concentration in the bloodstream reaches a value equivalent to 0.634% of the initial dose of 800 mg·kg(-1). As compared to the nude viologen having the same structure, which proved to be lethal in doses of 40 mg·kg(-1), the product induces reversible morphological changes in the liver, kidney, lung, and cerebellum, up to a dose of 400 mg·kg(-1), with higher dosages giving rise to a chronic slow evolution.

Evaluation of Compatibility between Beetle-Killed Lodgepole Pine (Pinus Contorta var. Latifolia) Wood with Portland Cement.

The compatibility of wood from mountain pine beetle (Dendroctonus ponderosa) killed lodgepole pine (Pinus contorta var. latifolia) with Portland cement was investigated based on time-since-death as a quantitative estimator, and the presence of blue-stained sapwood, brown rot, or white rot as qualitative indicators. The exothermic behavior of cement hydration, maximum heat rate, time to reach this maximum, and total heat released within a 3.5-24 h interval were used for defining a new wood-cement compatibility index (CX). CX was developed and accounted for large discrepancies in assessing wood-cement compatibility compared to the previous methods. Using CX, no significant differences were found between fresh or beetle-killed wood with respect to the suitability for cement; except for the white rot samples which reached or exceeded the levels of incompatibility. An outstanding physicochemical behavior was also found for blue-stained sapwood and cement, producing significantly higher compatibility indices.