Wearable sensors for detection of human activities have encouraged the development of highly elastic sensors. In particular, to capture subtle and large-scale body motion, stretchable and wide-range strain sensors are highly desired, but still a challenge. Herein, a highly stretchable and transparent stain sensor based on ionic liquids and elastic polymer has been developed. The as-obtained sensor exhibits impressive stretchability with wide-range strain (from 0.1% to 400%), good bending properties and high sensitivity, whose gauge factor can reach 7.9. Importantly, the sensors show excellent biological compatibility and succeed in monitoring the diverse human activities ranging from the complex large-scale multidimensional motions to subtle signals, including wrist, finger and elbow joint bending, finger touch, breath, speech, swallow behavior and pulse wave.
Assuntos
Dispositivos Eletrônicos Vestíveis , Atividades Humanas , Humanos , Líquidos Iônicos , Movimento (Física) , PolímerosRESUMO
Large-size single crystalline nanosheets of 9,10-bis(phenylethynyl)-anthracene were prepared by a facile solution process and were fully characterized. The prototype photodetector was then fabricated on the basis of a single nanosheet and exhibited superior performance with the largest photoresponse ratio up to ca. 10(5). Moreover, the nanosheets show obvious light emission anisotropy.
RESUMO
Single-crystalline 1,2,3,4,5-pentaphenyl-1,3-cyclopentadiene (PPCP) microrods were prepared by a facile solution process. The PPCP microrods with smooth surfaces could absorb excitation light and propagate the photoluminescence (PL) emission. They showed excellent properties in the low optical loss of a single rod and feasible transfer between neighboring rods. Moreover, PPCP displayed typical aggregation-induced emission enhancement (AIEE) characteristics in the solution state.
RESUMO
Correction for 'Large-size nanosheets of 9,10-bis(phenylethynyl)anthracene with high photoresponse and light emission anisotropy' by Juan-Ye Wang et al., Phys. Chem. Chem. Phys., 2016, DOI: 10.1039/c5cp05507e.
RESUMO
Klockmannite copper selenide nanosheets (CuSe NSs) are synthesized by a facile microwave-assisted method and fully characterized. The nanosheets have smooth surface and hexagonal shape. The lateral size is 200-500 nm × 400-800 nm and the thickness is 55 ± 20 nm. The current-voltage characteristics of CuSe NS films show unique Ohmic and high-conducting behaviors, comparable to the thermally-deposited gold electrode. The high electrical conductivity of CuSe NSs implies their promising applications in printed electronics and nanodevices. Moreover, the local electrical variation is observed, for the first time, within an individual CuSe NS at low bias voltages (0.1 ~ 3 V) by conductive atomic force microscopy (C-AFM). This is ascribed to the quantum size effect of NS and the presence of Schottky barrier. In addition, the influence of the molar ratio of Cu(2+)/SeO2, reaction temperature, and reaction time on the growth of CuSe NSs is explored. The template effect of oleylamine and the intrinsic crystal nature of CuSe NS are proposed to account for the growth of hexagonal CuSe NSs.