RESUMO
Nanofillers in resin materials can improve their mechanical and physicochemical properties. The present work investigated the effects of zirconia nanoparticles (NPs) as fillers in commercial dental luting cements. Two dual-cured self-adhesive composites and one resin modified glass ionomer (RMGI) luting cement were employed. Film thickness (FT), flexural strength (FS), water sorption (Wsp), and shear bond strength (SBS) to monolithic zirconia were evaluated according to ISO 16506:2017 and ISO 9917-2:2017, whereas polymerization progress was evaluated with FTIR. Photopolymerization resulted in double the values of DC%. The addition of 1% wt NPs does not significantly influence polymerization, however, greater amounts do not promote crosslinking. The sorption behavior and the mechanical performance of the composites were not affected, while the film thickness increased in all luting agents, within the acceptable limits. Thermocycling (TC) resulted in a deteriorating effect on all composites. The addition of NPs significantly improved the mechanical properties of the RMGI cement only, without negatively affecting the other cements. Adhesive primer increased the initial SBS significantly, however after TC, its application was only beneficial for RMGI. The MDP containing luting cement showed higher SBS compared to the RMGI and 4-META luting agents. Future commercial adhesives containing zirconia nanoparticles could provide cements with improved mechanical properties.
Assuntos
Colagem Dentária , Zircônio , Zircônio/química , Resinas Vegetais , Resistência ao Cisalhamento , Cimentos de Ionômeros de Vidro/química , Cimentos de Resina/química , Teste de Materiais , Propriedades de Superfície , Cimentos DentáriosRESUMO
STATEMENT OF PROBLEM: Adhesive cementation is the most common bonding strategy for zirconia restorations. Although cementation with a bioactive luting agent has been proposed as an alternative, how the bond strength compares is unclear. PURPOSE: The purpose of this in vitro study was to evaluate shear bond strength after cementing a monolithic zirconia ceramic to human dentin with a bioceramic cement, compare it with a traditional cement, and evaluate its bioactive properties. MATERIAL AND METHODS: A total of 120 dentin specimens and 120 yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) (BruxZir) cylindrical specimens were used. Zirconia and dentin specimens were randomly divided into 8 study groups (n=15) based on 2 luting cement types (a bioceramic cement or glass ionomer cement as control), 2 airborne-particle abrasion protocols (50 µm or 110 µm), and 2 water storage durations (24 hours or 30 days). After the shear bond strength test using a universal machine at a crosshead speed of 1 mm/min, fracture patterns were evaluated under a stereomicroscope and a scanning electron microscope. Strength values were statistically analyzed with a 3-factor ANOVA model (α=.05). Bioactivity was evaluated in simulated body fluid (SBF). RESULTS: The control glass ionomer cement achieved significantly greater shear bond strength compared with the tested bioceramic cement. Mean bond strength values ranged from 2.52 MPa to 5.23 MPa for the bioceramic cement tested and from 4.20 MPa to 6.61 MPa for the control cement. The duration of water storage played a significant role in the bond strength, with groups stored for 30 days reaching higher bond strength values, whereas the particle size of airborne-particle abrasion did not have a significant effect. Failure types were primarily mixed. No apatite formation was recorded on the surface of the specimens even after 30 days of immersion in SBF. CONCLUSIONS: The evaluated cement did not develop apatite in SBF, and its bond strength values were below the control glass ionomer cement.
Assuntos
Colagem Dentária , Cimentos de Resina , Cimentos Dentários , Análise do Estresse Dentário , Cimentos de Ionômeros de Vidro , Humanos , Teste de Materiais , Microscopia Eletrônica de Varredura , Resistência ao Cisalhamento , Propriedades de Superfície , ZircônioRESUMO
The present study systematically reviewed the literature regarding the bond strength durability of zirconia ceramics to resin-based luting cements after application of different bonding protocols and aging conditions. Electronic searches in PubMed, Scopus, and Web of Science databases were performed for relevant literature published between January 1st 2015 and November 15th 2022. Ninety-three (93) English language in-vitro studies were included. The percentage of the mean bond strength change was recorded prior to and after artificial aging, and the weighted mean values and 95% confidence intervals were calculated. Bonding protocols were classified based on the combination of MDP/non-MDP containing cement/primer and surface pretreatment, as well as the level of artificial aging performed. Alumina sandblasting (SA) was identified as the most frequently used surface pre-treatment while an insufficient number of studies was identified for each category of alternative surface treatments. The combination of MDP cement with tribochemical silica coating (TSC) or SA yielded more durable results after aging, while the application of SA and TSC improved bond durability when a non-MDP cement and a non-MDP primer were used. TSC may lead to increased bond durability compared to SA, whereas MDP cements may act similarly when combined with SA or TSC.
RESUMO
BACKGROUND: Yttria-stabilized zirconia nanoparticles can be applied as fillers to improve the mechanical and antibacterial properties of luting cement. The aim of this study was to synthesize yttria-stabilized zirconia nanoparticles by the sol-gel method and to investigate their composition, structure, morphology and biological properties. METHODS: Nanopowders of ZrO2 7 wt% Y2O3 (nY-ZrO) were synthesized by the sol-gel method and were sintered at three different temperatures: 800, 1000 and 1200 °C, and their composition, size and morphology were investigated. The biocompatibility was investigated with human gingival fibroblasts (hGFs), while reactive oxygen species (ROS) production was evaluated through fluorescence analysis. RESULTS: All synthesized materials were composed of tetragonal zirconia, while nanopowders sintered at 800 °C and 1000 °C additionally contained 5 and 20 wt% of the cubic phase. By increasing the calcination temperature, the crystalline size of the nanoparticles increased from 12.1 nm for nY-ZrO800 to 47.2 nm for nY-ZrO1200. Nano-sized particles with good dispersion and low agglomeration were received. Cell culture studies with human gingival fibroblasts verified the nanopowders' biocompatibility and their ROS scavenging activity. CONCLUSIONS: the obtained sol-gel derived nanopowders showed suitable properties to be potentially used as nanofillers for dental luting cement.
RESUMO
New zirconia compositions with optimized esthetic properties have emerged due to the fast-growing technology in zirconia manufacturing. However, the large variety of commercial products and synthesis routes, make impossible to include all of them under the general term of "monolithic zirconia ceramics". Ultra- or high translucent monolithic formulations contain 3-8 mol% yttria, which results in materials with completely different structure, optical and mechanical properties. The purpose of this study was to provide an update to the current knowledge concerning monolithic zirconia and to review factors related to strength and aging resistance. Factors such as composition, coloring procedures, sintering method and temperature, may affect both strength and aging resistance to a more or less extend. A significant reduction of mechanical properties has been correlated to high translucent zirconia formualtions while regarding aging resistance, the findings are contradictory, necessitating more and thorough investigation. Despite the obvious advantages of contemporary monolithic zirconia ceramics, further scientific evidence is required that will eventually lead to the appropriate laboratory and clinical guidelines for their use. Until then, a safe suggestion should be to utilize high-strength partially-stabilized zirconia for posterior or long span restorations and fully-stabilized ultra-translucent zirconia for anterior single crowns and short span fixed partial dentures.
RESUMO
The purpose of this paper was to update the knowledge concerning the wear, translucency, as well as clinical performance of monolithic zirconia ceramics, aiming at highlighting their advantages and weaknesses through data presented in recent literature. New ultra-translucent and multicolor monolithic zirconia ceramics present considerably improved aesthetics and translucency, which, according to the literature reviewed, is similar to those of the more translucent lithium disilicate ceramics. A profound advantage is their high strength at thin geometries preserving their mechanical integrity. Based on the reviewed articles, monolithic zirconia ceramics cause minimal wear of antagonists, especially if appropriately polished, although no evidence still exists regarding the ultra-translucent compositions. Concerning the survival of monolithic zirconia restorations, the present review demonstrates the findings of the existing short-term studies, which reveal promising results after evaluating their performance for up to 5 or 7 years. Although a significant increase in translucency has been achieved, new translucent monolithic zirconia ceramics have to be further evaluated both in vitro and in vivo for their long-term potential to preserve their outstanding properties. Due to limited studies evaluating the wear properties of ultra-translucent material, no sound conclusions can be made, whereas well-designed clinical studies are urgently needed to enlighten issues of prognosis and long-term survival.