Wiring-up carbon single wall nanotubes to polycrystalline inorganic semiconductor thin films: low-barrier, copper-free back contact to CdTe solar cells.

We have discovered that films of carbon single wall nanotubes (SWNTs) make excellent back contacts to CdTe devices without any modification to the CdTe surface. Efficiencies of SWNT-contacted devices are slightly higher than otherwise identical devices formed with standard Au/Cu back contacts. The SWNT layer is thermally stable and easily applied with a spray process, and SWNT-contacted devices show no signs of degradation during accelerated life testing.

Enhanced Grain Size, Photoluminescence, and Photoconversion Efficiency with Cadmium Addition during the Two-Step Growth of CH3NH3PbI3.

Control over grain size and crystallinity is important for preparation of methylammonium lead iodide (MAPbI3) solar cells. We explore the effects of using small concentrations of Cd2+ and unusually high concentrations of methylammonium iodide during the growth of MAPbI3 in the two-step solution process. In addition to improved crystallinity and an enhancement in the size of the grains, time-resolved photoluminescence measurements indicated a dramatic increase in the carrier lifetime. As a result, devices constructed with the Cd-modified perovskites showed nearly a factor of 2 improvement in the power conversion efficiency (PCE) relative to similar devices prepared without Cd addition. The grains also showed a higher degree of orientation in the ⟨110⟩ direction, indicating a change in the growth mechanism, and the films were compact and smooth. We propose a Cd-modified film growth mechanism that invokes a critical role for low-dimensional Cd perovskites to explain the experimental observations.

Improving the Performance of Formamidinium and Cesium Lead Triiodide Perovskite Solar Cells using Lead Thiocyanate Additives.

Formamidinium lead triiodide (FAPbI3 ) is considered as an alternative to methylammonium lead triiodide (MAPbI3 ) because of its lower band gap and better thermal stability. However, owing to the large size of FA cations, it is difficult to synthesize high-quality FAPbI3 thin films without the formation of an undesirable yellow phase. Smaller sized cations, such as MA and Cs, have been successfully used to suppress the formation of the yellow phase. Whereas FA and MA lead triiodide perovskite solar cells (PVSCs) have achieved power conversion efficiencies (PCEs) higher than 20 %, the PCEs of formamidinium and cesium lead triiodide (FA1-x Csx PbI3 ) PVSCs have been only approximately 16.5 %. Herein, we report our examination of the main factors limiting the PCEs of (FA1-x Csx PbI3 ) PVSCs. We find that one of the main limiting factors could be the small grain sizes (≈120 nm), which leads to relatively short carrier lifetimes. We further find that adding a small amount of lead thiocyanate [Pb(SCN)2 ] to the precursors can enlarge the grain size of (FA1-x Csx PbI3 ) perovskite thin films and significantly increase carrier lifetimes. As a result, we are able to fabricate (FA1-x Csx PbI3 ) PVSCs with significantly improved open-circuit voltages and fill factors and, therefore, enhanced PCEs. With an optimal 0.5 mol % Pb(SCN)2 additive, the average PCE is increased from 16.18±0.50 (13.45±0.78) % to 18.16±0.54 (16.86±0.63) % for planar FA0.8 Cs0.2 PbI3 PVSCs if measured under reverse (forward) voltage scans. The champion cell registers a PCE of 19.57 (18.12) % if measured under a reverse (forward) voltage scan, which is comparable to that of the best-performing MA-containing planar FA-based lead halide PVSCs.

High speed, intermediate resolution, large area laser beam induced current imaging and laser scribing system for photovoltaic devices and modules.

We have developed a laser beam induced current imaging tool for photovoltaic devices and modules that utilizes diode pumped Q-switched lasers. Power densities on the order of one sun (100 mW/cm2) can be produced in a ∼40 µm spot size by operating the lasers at low diode current and high repetition rate. Using galvanostatically controlled mirrors in an overhead configuration and high speed data acquisition, large areas can be scanned in short times. As the beam is rastered, focus is maintained on a flat plane with an electronically controlled lens that is positioned in a coordinated fashion with the movements of the mirrors. The system can also be used in a scribing mode by increasing the diode current and decreasing the repetition rate. In either mode, the instrument can accommodate samples ranging in size from laboratory scale (few cm2) to full modules (1 m2). Customized LabVIEW programs were developed to control the components and acquire, display, and manipulate the data in imaging mode.