This study examined the effects of different application times of sodium ascorbate (SA) on the bond strength of composite resin to bleached dentin. Specimens with an exposed dentin surface were divided into 3 groups according to the type of bleaching agent used: Group A, mixture of sodium perborate (SP) and distilled water (DW); Group B, mixture of SP and hydrogen peroxide (HP); control group, no bleaching. Each group was classified into 10 subgroups. Subgroups IB and DB underwent immediate bonding and delayed bonding, respectively. 10% SA was applied to 3, 5, 10, and 30 minutes and 1, 24, 48, and 72 hours, respectively. Microtensile bond strength (µTBS) was measured after restoration, and the data was analyzed by one-way ANOVA and Scheffé's test. Before restoration, the dentin surfaces were examined by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). SEM showed that most dentin surfaces were filled with crystals when SA was applied to more than 24 hours. EDS revealed peaks of calcium, carbon, oxygen, and sodium. The application of SA for 5 minutes to 48 hours or for 30 minutes to 24 hours is suggested when a mixture of SP and DW or HP is used, respectively.
Assuntos
Ácido Ascórbico/metabolismo , Resinas Compostas/metabolismo , Dentina/metabolismo , Resistência à Tração , Humanos , Microscopia Eletrônica de Varredura , Espectrometria por Raios X , Propriedades de Superfície , Fatores de Tempo , Resultado do TratamentoRESUMO
OBJECTIVES: This study examined the color changes of a resin composite with different shades upon exposure to water with different pH. MATERIALS AND METHODS: Nanohybrid resin composites (Filtek Z350XT, 3M ESPE) with four different shades (A2, A3, B1, and B2) were immersed in water with three different pH (pH 3, 6, and 9) for 14 day. The CIE L*a*b* color coordinates of the specimens were evaluated before and after immersion in the solutions. The color difference (ΔE*) and the translucency parameter (TP) were calculated using the color coordinates. RESULTS: ΔE* ranged from 0.33 to 1.58, and the values were affected significantly by the pH. The specimens immersed in a pH 6 solution showed the highest ΔE* values (0.87 - 1.58). The specimens with a B1 shade showed the lowest ΔE* change compared to the other shades. TP ranged from 7.01 to 9.46 depending on the pH and resin shade. The TP difference between before and after immersion in the pH solutions was less than 1.0. CONCLUSIONS: The resulting change of color of the tested specimens did not appear to be clinically problematic because the color difference was < 1.6 in the acidic, neutral, and alkaline solutions regardless of the resin shade, i.e., the color change was imperceptible.