RESUMO
The high exciton binding energy (Eb) and sluggish surface reaction kinetics have severely limited the photocatalytic hydrogen production activity of carbon nitride (CN). Herein, a hybrid system consisting of nitrogen defects and Pt single atoms is constructed through a facile self-assembly and photodeposition strategy. Due to the acceleration of exciton dissociation and regulation of local electron density of Pt single atoms along with the introduction of nitrogen defects, the optimized Pt-MCT-3 exhibits a hydrogen production rate of 172.0 µmol h-1 (λ ≥ 420 nm), ≈41 times higher than pristine CN. The apparent quantum yield for the hydrogen production is determined to be 27.1% at 420 nm. The experimental characterizations and theoretical calculations demonstrate that the nitrogen defects act as the electron traps for the exciton dissociation, resulting in a decrease of Eb from 86.92 to 43.20 meV. Simultaneously, the stronger interaction between neighboring nitrogen defects and Pt single atoms directionally drives free electrons to aggregate around Pt single atoms, and tailors the d-band electrons of Pt, forming a moderate binding strength between Pt atoms and H* intermediates.
RESUMO
To promote interfacial charge transfer process and accelerate surface water oxidation reaction kinetics for photoelectrochemical (PEC) water splitting over n-type Silicon (n-Si) based photoanodes, herein, starting with surface stabilized n-Si/CoOx , a NiOx /NiFeOOH composite overlayer was coated by atomic layer deposition and spray coating to fabricate the multilayer structured n-Si/CoOx /NiOx /NiFeOOH photoanode. Encouragingly, the obtained n-Si/CoOx /NiOx /NiFeOOH photoanode exhibits much increased PEC activity for water splitting, with onset potential cathodically shifted to ~0.96â V vs. RHE and photocurrent density increased to 22.6â mA cm-2 at 1.23â V vs. RHE for OER, as compared to n-Si/CoOx , even significantly surpassing the counterpart n-Si/CoOx /NiOx /FeOOH and n-Si/CoOx /NiOx /NiOOH photoanodes. Photophysical and electrochemical characterizations evidence that the deposited CoOx /NiOx /NiFeOOH composite overlayer would create large band bending and strong built-in electric field at the introduced cascading interfaces, thereby producing a large photovoltage of 650â mV to efficiently accelerate charge transfer from the n-Si substrate to the electrolyte for water oxidation. Furthermore, the surface oxygen vacancy enriched NiFeOOH overlayer could effectively catalyze the water oxidation reaction by thermodynamically reducing the energy barrier of rate determining step for OER.
RESUMO
The recombination of photogenerated charge carriers severely limits the performance of photoelectrochemical (PEC) H2 production. Here, we demonstrate that this limitation can be overcome by optimizing the charge transfer dynamics at the solid-liquid interface via molecular catalyst design. Specifically, the surface of a p-Si photocathode is modulated using molecular catalysts with different metal atoms and organic ligands to improve H2 production performance. Co(pda-SO3H)2 is identified as an efficient and durable catalyst for H2 production through the rational design of metal centers and first/second coordination spheres. The modulation with Co(pda-SO3H)2, which contains an electron-withdrawing -SO3H group in the second coordination sphere, elevates the flat-band potential of the polished p-Si photocathode and nanoporous p-Si photocathode by 81â mV and 124â mV, respectively, leading to the maximized energy band bending and the minimized interfacial carrier transport resistance. Consequently, both the two photocathodes achieve the Faradaic efficiency of more than 95 % for H2 production, which is well maintained during 18â h and 21â h reaction, respectively. This work highlights that the band-edge engineering by molecular catalysts could be an important design consideration for semiconductor-catalyst hybrids toward PEC H2 production.
RESUMO
To solve surface carrier recombination and sluggish water oxidation kinetics of hematite (α-Fe2 O3 ) photoanodes, herein, an attractive surface modification strategy is developed to successively deposit ultrathin CoOx overlayer and Ni single atoms on titanium (Ti)-doped α-Fe2 O3 (Ti:Fe2 O3 ) nanorods through a two-step atomic layer deposition (ALD) and photodeposition process. The collaborative decoration of ultrathin CoOx overlayer and Ni single atoms can trigger a big boost in photo-electrochemical (PEC) performance for water splitting over the obtained Ti:Fe2 O3 /CoOx /Ni photoanode, with the photocurrent density reaching 1.05 mA cm-2 at 1.23 V vs. reversible hydrogen electrode (RHE), more than three times that of Ti:Fe2 O3 (0.326 mA cm-2 ). Electrochemical and electronic investigations reveal that the surface passivation effect of ultrathin CoOx overlayer can reduce surface carrier recombination, while the catalysis effect of Ni single atoms can accelerate water oxidation kinetics. Moreover, theoretical calculations evidence that the synergy of ultrathin CoOx overlayer and Ni single atoms can lower the adsorption free energy of OH* intermediates and relieve the potential-determining step (PDS) for oxygen evolution reaction (OER). This work provides an exemplary modification through rational engineering of surface electrochemical and electronic properties for the improved PEC performances, which can be applied in other metal oxide semiconductors as well.
RESUMO
Efficient charge-carrier separation and their utilization are the key factors in overcoming sluggish four-electron reaction kinetics involved in photocatalytic oxygen evolution. Here, a novel study demonstrates the significance of Na2 S2 O8 as a sacrificial agent in comparison to AgNO3 . Resultantly, BiFeO3 (BFO) and titanium doped-oxygen deficient BiFeO3 (Ti-BFO-R) nanostructures achieve ≈64 and 44.5 times higher O2 evolution in the presence of Na2 S2 O8 compared to AgNO3 as a sacrificial agent, respectively. Furthermore, the presence of Co single atoms (Co-SAs) deposited via immersion method on BFO and Ti-BFO-R nanostructures led to achieving outstanding O2 evolution at a rate of 16.11 and 23.89 mmol g-1 h-1 , respectively, which is 153 and 227.5 times higher compared to BFO (in the presence of AgNO3 ), the highest O2 evolution observed for BFO-based materials to date. The successful deposition of Co-SAs is confirmed by aberration-corrected high-angle annular dark-field scanning transmission electron microscopy (AC HAADF-STEM) and X-ray absorption near-edge structure (XANES). The charge transfer investigations confirm the significance of Co-SAs on BFO-based photocatalysts for improved charge-carrier separation, transport, and utilization. This novel study validates the excellent role of Na2 S2 O8 as a sacrificial agent and Co-SAs as a cocatalyst for BFO-based nanostructures for efficient O2 evolution.
RESUMO
In the development of photoelectrochemical cells for water splitting or CO2 reduction, a major challenge is O2 evolution at photoelectrodes that, in behavior, mimic photosystem II. At an appropriate semiconductor electrode, a water oxidation catalyst must be integrated with a visible light absorber in a stable half-cell configuration. Here, we describe an electrode consisting of a light absorber, an intermediate electron donor layer, and a water oxidation catalyst for sustained light driven water oxidation catalysis. In assembling the electrode on nanoparticle SnO2/TiO2 electrodes, a Ru(II) polypyridyl complex was used as the light absorber, NiO was deposited as an overlayer, and a Ru(II) 2,2'-bipyridine-6,6'-dicarboxylate complex as the water oxidation catalyst. In the final electrode, addition of the NiO overlayer enhanced performance toward water oxidation with the final electrode operating with a 1.1 mA/cm2 photocurrent density for 2 h without decomposition under one sun illumination in a pH 4.65 solution. We attribute the enhanced performance to the role of NiO as an electron transfer mediator between the light absorber and the catalyst.
RESUMO
Oxide-derived Cu (OD-Cu) featured with surface located sub-20â nm nanoparticles (NPs) created via surface structure reconstruction was developed for electrochemical CO2 reduction (ECO2 RR). With surface adsorbed hydroxyls (OHad ) identified during ECO2 RR, it is realized that OHad , sterically confined and adsorbed at OD-Cu by surface located sub-20â nm NPs, should be determinative to the multi-carbon (C2 ) product selectivity. In situ spectral investigations and theoretical calculations reveal that OHad favors the adsorption of low-frequency *CO with weak C≡O bonds and strengthens the *CO binding at OD-Cu surface, promoting *CO dimerization and then selective C2 production. However, excessive OHad would inhibit selective C2 production by occupying active sites and facilitating competitive H2 evolution. In a flow cell, stable C2 production with high selectivity of â¼60 % at -200â mA cm-2 could be achieved over OD-Cu, with adsorption of OHad well steered in the fast flowing electrolyte.
RESUMO
Electrochemical CO2 reduction reaction (ECO2 RR) with controlled product selectivity is realized on Ag-Cu bimetallic surface alloys, with high selectivity towards C2 hydrocarbons/alcohols (≈60 % faradaic efficiency, FE), C1 hydrocarbons/alcohols (≈41 % FE) and CO (≈74 % FE) achieved by tuning surface compositions and applied potentials. In situ spectral investigations and theoretical calculations reveal that surface-composition-dependent d-band center could tune *CO binding strengths, regulating the *CO subsequent reaction pathways and then the product selectivity. Further adjusting the applied potentials will alter the energy of participated electrons, which leads to controlled ECO2 RR selectivity towards desired products. A predominant region map, with an indicator proposed to evaluate the thermodynamic predominance of the *CO subsequent reactions, is then provided as a reliable theoretical guidance for the controllable ECO2 RR product selectivity over bimetallic alloys.
RESUMO
In fabricating an artificial photosynthesis (AP) electrode for water oxidation, we have devised a semiconductor-mediator-catalyst structure that mimics photosystem II (PSII). It is based on a surface layer of vertically grown nanorods of Fe2 O3 on fluorine doped tin oxide (FTO) electrodes with a carbazole mediator base and a Ru(II) carbene complex on a nanolayer of TiO2 as a water oxidation co-catalyst. The resulting hybrid assembly, FTO|Fe2 O3 |-carbazole|TiO2 |-Ru(carbene), demonstrates an enhanced photoelectrochemical (PEC) water oxidation performance compared to an electrode without the added carbaozle base with an increase in photocurrent density of 2.2-fold at 0.95â V vs. NHE and a negatively shifted onset potential of 500â mV. The enhanced PEC performance is attributable to carbazole mediator accelerated interfacial hole transfer from Fe2 O3 to the Ru(II) carbene co-catalyst, with an improved effective surface area for the water oxidation reaction and reduced charge transfer resistance.
Assuntos
Fotossíntese , Água , Catálise , Oxirredução , Semicondutores , Água/químicaRESUMO
Herein, we have demonstrated the control over the structure of precatalysts to tune the properties of the active catalysts and their water oxidation activity. The reaction of K3 [Fe(CN)6 ] and Na2 [Fe(CN)5 (NO)] with Co(OH)2 @CC produced precatalysts PC-1 and PC-2, respectively, with distinct structural and electronic features. The replacement of the -CN group with strong π-acceptor -NO modulates the electronic and atomic structure of PC-2. As a result, a facile electrochemical transformation of PC-2 into active catalyst Fe-Co(OH)2 -Co(O)OH (AC-2) has been attained only in 15â CV cycles while 600â CV cycles are required for the electrochemical activation of PC-1 into AC-1. The X-ray absorption studies reveal the contraction of the Co-O and Fe-O bond in AC-2 because of the presence of a higher amount of Co3+ and Fe3+ than in AC-1. The high valent Co3+ and Fe3+ modulates the electronic properties of AC-2 and assists in the O-O bond formation, leading to the improved water oxidation activity.
RESUMO
Single-atom nickel catalysts hold great promise for photocatalytic water splitting due to their plentiful active sites and cost-effectiveness. Herein, we adopt a reactive-group guided strategy to prepare atomically dispersed nickel catalysts on red phosphorus. The hydrothermal treatment of red phosphorus leads to the formation of P-H and P-OH groups, which behave as the reactive functionalities to generate the dual structure of single-atom P-Ni and P-O-Ni catalytic sites. The produced single-atom sites provide two different functions: P-Ni for water reduction and P-O-Ni for water oxidation. Benefitting from this specific Janus structure, Ni-red phosphorus shows an elevated hydrogen evolution rate compared to Ni nanoparticle-modified red phosphorus under visible-light irradiation. The hydrogen evolution rate was additionally enhanced with increased reaction temperature, reaching 91.51â µmol h-1 at 70 °C, corresponding to an apparent quantum efficiency of 8.9 % at 420â nm excitation wavelength.
RESUMO
Oxygen evolution reaction (OER) is an obstacle to the electrocatalytic water splitting due to its unique four-proton-and-electron-transfer reaction process. Many methods, such as engineering heterostructure and introducing oxygen vacancy, have been used to improve the catalytic performance of electrocatalysts for OER. Herein, the above two kinds of regulation are simultaneously realized in a catalyst by using unique ion irradiation technology. A nanosheet structured NiO/NiFe2 O4 heterostructure with rich oxygen vacancies converted from nickel-iron layered double hydroxides by Ar+ ions irradiation shows significant enhancement in both OER and hydrogen evolution reaction performance. Density functional theory (DFT) calculations reveal that the construction of NiO/NiFe2 O4 can optimize the free energy of O* to OOH* process during OER reaction. The oxygen vacancy-rich NiO/NiFe2 O4 nanosheets have an overpotential of 279 mV at 10 mA cm-2 and a low Tafel slope of 42 mV dec-1 . Moreover, this NiO/NiFe2 O4 electrode shows an excellent long-term stability at 100 mA cm-2 for 450 h. The synergetic effects between NiO and NiFe2 O4 make NiO/NiFe2 O4 heterostructure have high conductivity and fast charge transfer, abundant active sites, and high catalytic reactivity, contributing to its excellent performance.
RESUMO
A novel Co/Ni bimetallic nanoparticle supported by nitrogen-doped porous carbon (NPC), Co5/Ni@NPC-700, exhibits high conversion, chemoselectivity, and recyclability in the hydrogenation of 16 different nitro compounds into desired amines with hydrazine hydrate under mild conditions. The synergistic effects of Co/Ni bimetal nanoparticles and the NPC-supported porous honeycomb structure with more accessible active sites may be responsible for the high catalytic hydrogenation performance.
RESUMO
Engineering the interface and surface structures of semiconductor-based photoelectrodes for improved charge transfer dynamics and promoted water redox reaction kinetics is essential to achieve efficient photoelectrochemical (PEC) water splitting. In this work, α-Fe2O3 nanorods, successively coated with TiO2 and CoOx thin layers, were reported as the photoanode for solar-driven water oxidation. The obtained α-Fe2O3/TiO2/CoOx photoanode exhibits superior PEC performance as compared to bare α-Fe2O3, with a 3.3-time improvement in photocurrent density at 1.23 V vs reversible hydrogen electrode. This significant enhancement results from the formed heterojunction between α-Fe2O3 and TiO2 for the accelerated photogenerated charge separation and transfer as well as the passivated surface defects by the TiO2 overlayer for reduced charge recombination. Additionally, the existence of CoOx as the oxygen evolution catalyst significantly facilitates the surface reaction kinetics and thus reduces the overpotential for water oxidation. This study demonstrates a collaborative strategy of interface and surface engineering to design novel structures of α-Fe2O3 based photoanodes for highly efficient solar water oxidation.
RESUMO
Red phosphorus is a promising photocatalyst with wide visible-light absorption up to 700â nm, but the fast charge recombination limits its photocatalytic hydrogen evolution reaction (HER) activity. Now, [001]-oriented Hittorf's phosphorus (HP) nanorods were successfully grown on polymeric carbon nitride (PCN) by a chemical vapor deposition strategy. Compared with the bare PCN and HP, the optimized PCN@HP hybrid exhibited a significantly enhanced photocatalytic activity, with HER rates reaching 33.2 and 17.5â µmol h-1 from pure water under simulated solar light and visible light irradiation, respectively. It was theoretically and experimentally indicated that the strong electronic coupling between PCN and [001]-oriented HP nanorods gave rise to the enhanced visible light absorption and the greatly accelerated photoinduced electron-hole separation and transfer, which benefited the photocatalytic HER performance.
RESUMO
Artificial photosynthesis for solar water splitting and CO2 reduction to produce hydrogen and hydrocarbon fuels has been considered as one of the most promising ways to solve increasingly serious energy and environmental problems. As a well-documented metal-free semiconductor, polymeric carbon nitride (PCN) has been widely used and intensively investigated for photocatalytic water splitting and CO2 reduction, owing to its physicochemical stability, visible-light response, and facile synthesis. However, PCN as a photocatalyst still suffers from the fast recombination of electron-hole pairs and poor water redox reaction kinetics, greatly restricting its activity for artificial photosynthesis. Among the various modification approaches developed so far, decorating PCN with metals in different existences of nanoparticles, single atoms and molecular complexes, has been evidently very effective to overcome these limitations to improve photocatalytic performances. In this Review article, a systematic introduction to the state-of-the-art metal/PCN photocatalyst systems is given, with metals in versatility of nanoparticles, single atoms, and molecular complexes. Then, the recent processes of the metal/PCN photocatalyst systems in the applications of artificial photosynthesis, e.g., water splitting and CO2 reduction, are reviewed. Finally, the remaining challenges and opportunities for the development of high efficiency metal/PCN photocatalyst systems are presented and prospected.
RESUMO
Non-noble metal catalysts for high-active electrocatalytic oxygen evolution reaction (OER) are essential in large-scale application for water splitting. Herein, tricomponent metal phosphides with hollow structures are synthesized from cobalt-contained metal organic frameworks (MOFs), i.e., ZIF-67, by tailoring the feeding ratios of Ni and Fe, followed by a high-temperature reduction and a subsequent phosphidation process. Excellent OER activity and long-time stability are achieved in 1 m NaOH aqueous solution, with an overpotential of 329 mV at 10 mA cm-2 and Tafel slope of 48.2 mV dec-1 , even superior to the noble metal-based catalyst. It is evidenced that the formed (oxyhydr)oxide/phosphate species by in situ electrochemical surface oxidation are responsible for active OER. Accordingly, the simultaneous introduction of external Ni and Fe elements significantly influences the electronic structures of the parent metal phosphides, leading to the in situ electrochemical formation of surface active layer with decreased OER activation energy for greatly improved water oxidation performance. This electronic structure tuning strategy by introducing multicomponent metals demonstrates a versatile method to use MOFs as precursors for synthesizing high-efficient water splitting electrocatalysts.
RESUMO
The photoelectrochemical (PEC) water splitting activity of Nb and Ta-doped hematite (α-Fe2O3) nanorods was investigated with reference to electronic structures by in situ synchrotron x-ray absorption spectroscopy (XAS). Current density-potential measurements demonstrate that the PEC activity of α-Fe2O3 nanorods depends strongly on the species and concentrations of dopants. The doping of α-Fe2O3 nanorods with a low level of Nb or Ta can improve their electrical conductivity and thereby facilitate charge transport and reduced electron-hole recombination therein. The photoconversion effects of Nb and Ta-doped α-Fe2O3 by in situ XAS in the dark and under illumination revealed opposite evolutions of the spectral intensities of the Fe L-edge and Nb/Ta L-edge, indicating that charge transfer and a conduction pathway are involved in the photoconversion. Analytic in situ XAS results reveal that the α-Fe2O3 that is doped with a low level of Nb has a greater photoconversion efficiency than that doped with Ta because Nb sites are more active than Ta sites in α-Fe2O3. The correlation between PEC activity and the electronic structure of Nb/Ta-doped α-Fe2O3 is examined in detail using in situ XAS and helps to elucidate the mechanism of PEC water splitting in terms of the electronic structure.
RESUMO
With the intense interest in inorganic cesium lead halide perovskites and their nanostructures for optoelectronic applications, high-quality crystalline nanomaterials with controllable morphologies and growth directions are desirable. Here, we report a vapor-phase epitaxial growth of horizontal single-crystal CsPbX3 (X = Cl, Br, I) nanowires (NWs) and microwires (MWs) with controlled crystallographic orientations on the (001) plane of phlogopite and muscovite mica. Moreover, single NWs, Y-shaped branches, interconnected NW or MW networks with 6-fold symmetry, and, eventually, highly dense epitaxial network of CsPbBr3 with nearly continuous coverage were controllably obtained by varying the growth time. Detailed structural study revealed that the CsPbBr3 wires grow along the [001] directions and have the (100) facets exposed. The incommensurate heteroepitaxial lattice match between the CsPbBr3 and mica crystal structures and the growth mechanism of these horizontal wires due to asymmetric lattice mismatch were proposed. Furthermore, the photoluminescence waveguiding and good performance from the photodetector device fabricated with these CsPbBr3 networks demonstrated that these well-connected CsPbBr3 NWs could serve as straightforward platforms for fundamental studies and optoelectronic applications.
RESUMO
High-quality metal halide perovskite single crystals have low defect densities and excellent photophysical properties, yet thin films are the most sought after material geometry for optoelectronic devices. Perovskite single-crystal thin films (SCTFs) would be highly desirable for high-performance devices, but their growth remains challenging, particularly for inorganic metal halide perovskites. Herein, we report the facile vapor-phase epitaxial growth of cesium lead bromide perovskite (CsPbBr3) continuous SCTFs with controllable micrometer thickness, as well as nanoplate arrays, on traditional oxide perovskite SrTiO3(100) substrates. Heteroepitaxial single-crystal growth is enabled by the serendipitous incommensurate lattice match between these two perovskites, and overcoming the limitation of island-forming Volmer-Weber crystal growth is critical for growing large-area continuous thin films. Time-resolved photoluminescence, transient reflection spectroscopy, and electrical transport measurements show that the CsPbBr3 epitaxial thin film has a slow charge carrier recombination rate, low surface recombination velocity (104 cm s-1), and low defect density of 1012 cm-3, which are comparable to those of CsPbBr3 single crystals. This work suggests a general approach using oxide perovskites as substrates for heteroepitaxial growth of halide perovskites. The high-quality halide perovskite SCTFs epitaxially integrated with multifunctional oxide perovskites could open up opportunities for a variety of high-performance optoelectronics devices.