Development of Quaternary InAlGaN Barrier Layer for High Electron Mobility Transistor Structures.

A quaternary lattice matched InAlGaN barrier layer with am indium content of 16.5 ± 0.2% and thickness of 9 nm was developed for high electron mobility transistor structures using the metalorganic chemical-vapor deposition method. The structural, morphological, optical and electrical properties of the layer were investigated planning realization of microwave power and terahertz plasmonic devices. The measured X-ray diffraction and modeled band diagram characteristics revealed the structural parameters of the grown In0.165Al0.775Ga0.06N/Al0.6Ga0.4N/GaN heterostructure, explaining the origin of barrier photoluminescence peak position at 3.98 eV with the linewidth of 0.2 eV and the expected red-shift of 0.4 eV only. The thermally stable density of the two-dimension electron gas at the depth of 10.5 nm was experimentally confirmed to be 1.2 × 1013 cm-2 (1.6 × 1013 cm-2 in theory) with the low-field mobility values of 1590 cm2/(V·s) and 8830 cm2/(V·s) at the temperatures of 300 K and 77 K, respectively.

AlGaN/GaN on SiC Devices without a GaN Buffer Layer: Electrical and Noise Characteristics.

We report on the high-voltage, noise, and radio frequency (RF) performances of aluminium gallium nitride/gallium nitride (AlGaN/GaN) on silicon carbide (SiC) devices without any GaN buffer. Such a GaN-SiC hybrid material was developed in order to improve thermal management and to reduce trapping effects. Fabricated Schottky barrier diodes (SBDs) demonstrated an ideality factor n at approximately 1.7 and breakdown voltages (fields) up to 780 V (approximately 0.8 MV/cm). Hall measurements revealed a thermally stable electron density at N2DEG = 1 × 1013 cm-2 of two-dimensional electron gas in the range of 77-300 K, with mobilities µ = 1.7 × 103 cm2/V∙s and µ = 1.0 × 104 cm2/V∙s at 300 K and 77 K, respectively. The maximum drain current and the transconductance were demonstrated to be as high as 0.5 A/mm and 150 mS/mm, respectively, for the transistors with gate length LG = 5 µm. Low-frequency noise measurements demonstrated an effective trap density below 1019 cm-3 eV-1. RF analysis revealed fT and fmax values up to 1.3 GHz and 6.7 GHz, respectively, demonstrating figures of merit fT × LG up to 6.7 GHz × µm. These data further confirm the high potential of a GaN-SiC hybrid material for the development of thin high electron mobility transistors (HEMTs) and SBDs with improved thermal stability for high-frequency and high-power applications.