RESUMO
The membrane-based liquid desiccant dehumidification system is a newly developed method in the field of air dehumidification. In this study, double-layer nanofibrous membranes (DLNMs) with directional vapor transport and water repellency for liquid dehumidification were fabricated by a simple electrospinning process. Specifically, the combination of thermoplastic polyurethane nanofibrous membrane and polyvinylidene fluoride (PVDF) nanofibrous membrane forms a cone-like structure in DLNMs, resulting in directional vapor transportation. The nanoporous structure and rough surface of PVDF nanofibrous membrane provide waterproof performance for DLNMs. Compare with the commercial membranes, the proposed DLNMs have a significantly higher water vapor permeability coefficient, which is as high as 539.67 g·µm m-2·24 h·Pa. This study not only provides a new route to construct a directional vapor transport and waterproof membrane, but also demonstrates the huge application prospect of the nanofibrous membrane formed by electrospinning in the field of solution dehumidification.
RESUMO
The demand for polypropylene (PP) melt-blown materials has dramatically increased due to the COVID-19 pandemic. It has caused serious environmental problems because of the lack of effective treatment for the waste PP melt-blown materials. In this study, we propose a green and sustainable recycling method to create PP sponges from waste PP melt-blown material for oil spill cleaning by freeze-drying and thermal treatment techniques. The recycling method is simple and without secondary pollution to the environment. The developed recycling method successfully transforms 2D laminar dispersed PP microfibers into elastic sponges with a 3D porous structure, providing the material with good mechanical properties and promotes its potential application in the field of oil spill cleaning. The morphology structure, thermal properties, mechanical properties, and oil absorption properties are tested and characterized. The PP sponges with a three-dimensional porous network structure show an exceedingly low density of >0.014 g/cm3, a high porosity of <98.77 %, and a high water contact angle range of 130.4-139.9°. Moreover, the PP sponges own a good absorption capacity of <47.61 g/g for different oil and solvents. In particular, the compressive modulus of the PP sponges is 33.59-201.21 kPa, which is higher than that of most other fiber-based porous materials, indicating that the PP sponges have better durability under the same force. The excellent comprehensive performance of the PP sponges demonstrates the method developed in this study has large application potential in the field of the recycle of waste PP melt-blown materials.