Structurally engineered highly efficient electrocatalytic performance of 3-dimensional Mo/Ni chalcogenides for boosting overall water splitting performance.

Hydrogen production from water splitting combined with renewable electricity can provide a viable solution to the energy crisis. A novel MoS2/NiS2/Ni3S4 heterostructure is designed as a bifunctional electrocatalyst by facile hydrothermal method to demonstrate excellent electrocatalytic performance towards overall water splitting applications. MoS2/NiS2/Ni3S4 heterostructure necessitates a low overpotential of 81 mV and 210 mV to attain a current density of 10 mA cm-2 during the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER), respectively. Consequently, the MoS2/NiS2/Ni3S4 heterostructure-based electrolyzer shows a low cell voltage of 1.54 V at 10 mA cm-2. The present work highlights the significance of the heterostructure configuration of transition metal sulfide-based electrocatalysts for electrochemical overall water splitting applications.

Defect engineered ternary metal spinel-type Ni-Fe-Co oxide as bifunctional electrocatalyst for overall electrochemical water splitting.

Transition metal spinel oxides were engineered with active elements as bifunctional water splitting electrocatalysts to deliver superior intrinsic activity, stability, and improved conductivity to support green hydrogen production. In this study, we reported the ternary metal Ni-Fe-Co spinel oxide electrocatalysts prepared by defect engineering strategy with rich and deficient Na+ ions, termed NFCO-Na and NFCO, which suggest the formation of defects with Na+ forming tensile strain. The Na-rich NiFeCoO4 spinel oxide reveals lattice expansion, resulting in the formation of a defective crystal structure, suggesting higher electrocatalytic active sites. The spherical NFCO-Na electrocatalysts exhibit lower OER and HER overpotentials of 248 mV and 153 mV at 10 mA cm-2 and smaller Tafel slope values of about 78 mV dec-1 and 129 mV dec-1, respectively. Notably, the bifunctional NFCO-Na electrocatalyst requires a minimum cell voltage of about 1.67 V to drive a current density of 10 mA cm-2. The present work highlights the significant electrochemical activity of defect-engineered ternary metal oxides, which can be further upgraded as highly active electrocatalysts for water splitting applications.