Continuous-wave quasi-single-mode random lasing in CH3NH3PbBr3 perovskite films on patterned sapphire substrates.

We report intriguing continuous-wave quasi-single-mode random lasing in methylammonium lead bromide (CH3NH3PbBr3) perovskite films synthesized on a patterned sapphire substrate (PSS) under excitation of a 532-nm laser diode. The random laser emission evolves from a typical multi-mode to a quasi-single-mode with increasing pump fluences. The full width at half-maximum of the lasing peak is as narrow as 0.06 nm at ∼547.8 nm, corresponding to a high Q-factor of ∼9000. Such excellent random lasing performance is plausibly ascribed to the exciton resonance in optical absorption at 532 nm and the enhanced optical resonance due to the increased likelihood for randomly scattered light to re-enter the optical loops formed among the perovskite grains by multi-reflection at the perovskite/PSS interfaces. This work demonstrates the promise of single-mode perovskite random lasers by introducing the exciton resonance effect and ingeniously designed periodic nano/micro optical structure.

Durability and Aesthetics of Architectural Concrete under Chloride Attack or Carbonation.

Architectural concrete has been wildly used nowadays, and those served in an offshore environment often suffer from chloride penetration and carbonation. To assess the protection and decoration performances of architectural concrete, this study exposed architectural concrete to actual marine environments and accelerated carbonation conditions. The chloride and carbonation resistance of architectural concrete was determined to evaluate the protection performance, and the corresponding surface-color-consistency was adopted to characterize its decoration performance. The results show that the total and free chloride of concrete in the marine atmosphere zone and the tidal zone generally decreases with depth; chloride content arguments significantly with exposure time, with a chloride maximum peak near the surface. Moreover, the chloride diffusion coefficient is small throughout the measurements, indicating the superior chloride resistance of architectural concrete. Furthermore, architectural concrete also possesses excellent carbonation resistance based on the carbonation depth data obtained from the carbonation experiment. Therefore, architecture concrete served as protection covers can withstand both the chloride attack and carbonation tested in this paper. In addition, carbonation was found to have a profound influence on the aesthetics of architectural concrete. Therefore, carbonation should be carefully handled for better maintaining the aesthetic appearance of architectural concrete in long-term service.