Biocompatible Co-organic Composite Thin Film Deposited by VHF Plasma-Enhanced Atomic Layer Deposition at a Low Temperature.

Although metal-organic thin films are required for many biorelated applications, traditional deposition methods have proven challenging in preparing these composite materials. Here, a Co-organic composite thin film was prepared by plasma-enhanced atomic layer deposition (PEALD) with cobaltocene (Co(Cp)2) on polydimethylsiloxane (PDMS), using two very high frequency (VHF) NH3 plasmas (60 and 100 MHz), for use as a tissue culture scaffold. VHF PEALD was employed to reduce the temperature and control the thickness and composition. In the result of the VHF PEALD process, the Young's modulus of the Co-organic composite thin film ranged from 82.0 ± 28.6 to 166.0 ± 15.2 MPa, which is similar to the Young's modulus of soft tissues. In addition, the deposited Co ion on the Co-organic composite thin film was released into the cell culture media under a nontoxic level for the biological environment. The proliferation of both L929, the mouse fibroblast cell line, and C2C12, the mouse myoblast cell line, increased to 164.9 ± 23.4% during 7 days of incubation. Here, this novel bioactive Co-organic composite thin film on an elastic PDMS substrate enhanced the proliferation of L929 and C2C12 cell lines, thereby expanding the application range of VHF PEALD in biological fields.

Monolithic DNApatite: An Elastic Apatite with Sub-Nanometer Scale Organo-Inorganic Structures.

Hydroxyapatite (HA) exhibits outstanding biocompatibility, bioactivity, osteoconductivity, and natural anti-inflammatory properties. Pure HA, ion-doped HA, and HA-polymer composites are investigated, but critical limitations such as brittleness remain; numerous efforts are being made to address them. Herein, the novel self-crystallization of a polymeric single-stranded deoxyribonucleic acid (ssDNA) without additional phosphate ions for synthesizing deoxyribonucleic apatite (DNApatite) is presented. The synthesized DNApatite, DNA1Ca2.2(PO4)1.3OH2.1, has a repetitive dual phase of inorganic HA crystals and amorphous organic ssDNA at the sub-nm scale, forming nanorods. Its mechanical properties, including toughness and elasticity, are significantly enhanced compared with those of HA nanorod, with a Young's modulus similar to that of natural bone.