Structure, Surface Morphology, Chemical Composition, and Sensing Properties of SnO2 Thin Films in an Oxidizing Atmosphere.

We conducted experiments on SnO2 thin layers to determine the dependencies between the stoichiometry, electrochemical properties, and structure. This study focused on features such as the film structure, working temperature, layer chemistry, and atmosphere composition, which play a crucial role in the oxygen sensor operation. We tested two kinds of resistive SnO2 layers, which had different grain dimensions, thicknesses, and morphologies. Gas-sensing layers fabricated by two methods, a rheotaxial growth and thermal oxidation (RGTO) process and DC reactive magnetron sputtering, were examined in this work. The crystalline structure of SnO2 films synthesized by both methods was characterized using XRD, and the crystallite size was determined from XRD and AFM measurements. Chemical characterization was carried out using X-ray photoelectron (XPS) and Auger electron (AES) spectroscopy for the surface and the near-surface film region (in-depth profiles). We investigated the layer resistance for different oxygen concentrations within a range of 1-4%, in a nitrogen atmosphere. Additionally, resistance measurements within a temperature range of 423-623 K were analyzed. We assumed a flat grain geometry in theoretical modeling for comparing the results of measurements with the calculated results.

ZnO@TiO2 Core Shell Nanorod Arrays with Tailored Structural, Electrical, and Optical Properties for Photovoltaic Application.

ZnO has prominent electron transport and optical properties, beneficial for photovoltaic application, but its surface is prone to the formation of defects. To overcome this problem, we deposited nanostructured TiO2 thin film on ZnO nanorods to form a stable shell. ZnO nanorods synthesized by wet-chemistry are single crystals. Three different procedures for deposition of TiO2 were applied. The influence of preparation methods and parameters on the structure, morphology, electrical and optical properties were studied. Nanostructured TiO2 shells show different morphologies dependent on deposition methods: (1) separated nanoparticles (by pulsed laser deposition (PLD) in Ar), (2) a layer with nonhomogeneous thickness (by PLD in vacuum or DC reactive magnetron sputtering), and (3) a homogenous thin layer along the nanorods (by chemical deposition). Based on the structural study, we chose the preparation parameters to obtain an anatase structure of the TiO2 shell. Impedance spectroscopy shows pure electron conductivity that was considerably better in all the ZnO@TiO2 than in bare ZnO nanorods or TiO2 layers. The best conductivity among the studied samples and the lowest activation energy was observed for the sample with a chemically deposited TiO2 shell. Higher transparency in the visible part of spectrum was achieved for the sample with a homogenous TiO2 layer along the nanorods, then in the samples with a layer of varying thickness.

Indium-Zinc-Tin-Oxide Film Prepared by Reactive Magnetron Sputtering for Electrochromic Applications.

This paper reports on the fabrication of indium-zinc-tin-oxide (IZTO) transparent conductive film deposited by direct current (DC) reactive magnetron sputtering. The electrical, structural, and optical properties of IZTO film were investigated by Hall measurement, X-ray diffraction (XRD), and optical transmission spectroscopy with various sputtering powers. The IZTO film prepared used power at 100 W showed the lowest resistivity of 5.2 × 10-4 Ω cm. To accomplish rapid switching and high optical modulation, we have fabricated an electrochromic device (ECD) consisting of an working electrode (WO3 electrode film deposited on IZTO/ITO/glass) and a counter-electrode (Pt mesh) in 0.2 M LiClO4/PC liquid solution. The device demonstrated an optical contrast of 44% and switching times of 4.6 s and 8.1 s for the coloring and bleaching state, respectively, at the wavelength of 550 nm.