Influence of the Nitrogen Content on the Carbide Transformation of AISI M42 High-Speed Steels during Annealing.
Sci Rep
; 8(1): 4328, 2018 Mar 12.
Article
en En
| MEDLINE
| ID: mdl-29531342
ABSTRACT
Attempts were made to elucidate the effect of nitrogen on primary eutectic carbides in as-cast and annealed AISI M42 high-speed steel. Particular emphasis was placed on the transformation of carbides during forging and annealing in steels with different nitrogen concentrations and the influence of final carbides on the impact toughness of the steel. Microstructural observation, electrolytic extraction method, X-ray diffraction analysis, automated inclusion analysis (INCASteel), and impact toughness measurement combined with fractographic observation were conducted on the specimens. Primary M2C carbides were found to be dominant precipitates in the as-cast ingot, with a certain amount of V(C,N). Nitrogen addition promoted the formation of fibrous M2C, whereas lamellar M2C predominated in M42 steel with a low nitrogen concentration (w[N]% = 0.006). Fibrous carbides M2C tend to decompose into more stable carbides M6C and MC during forging and annealing compared to lamellar M2C. Nitrogen alloying only affected the morphologies and dimensions of carbides, but did not change the types of carbides. These improvements in the dimensions and fractions of carbides naturally increased the impact toughness of annealed steel. Hence, it was suggested that the addition of nitrogen to AISI M42 high-speed steel was required to achieve homogeneous distribution of carbides and sufficient impact toughness.
Texto completo:
1
Colección:
01-internacional
Banco de datos:
MEDLINE
Idioma:
En
Revista:
Sci Rep
Año:
2018
Tipo del documento:
Article