Trueness of removable partial denture frameworks additively manufactured with selective laser melting.
J Prosthet Dent
; 127(1): 122-127, 2022 Jan.
Article
en En
| MEDLINE
| ID: mdl-33223197
ABSTRACT
STATEMENT OF PROBLEM:
Although studies have reported on selective laser melting (SLM)-fabricated removable partial dentures (RPDs), research addressing the trueness of SLM-fabricated RPD metal frameworks is sparse.PURPOSE:
The purpose of this in vitro study was to evaluate the trueness of powdered cobalt-chromium (Co-Cr) or titanium-6 aluminum-4 vanadium (Ti-6Al-4V) alloy frameworks for RPDs fabricated by SLM. MATERIAL ANDMETHODS:
A digital scan of a Kennedy class II mandible typodont was obtained to design an RPD framework by using a computer-aided design (CAD) software program (denoted as CRF). Two experimental groups of frameworks were fabricated from the CRF by using SLM in alloys of Co-Cr (SLM-Co-Cr, n=6) and in Ti-6Al-4V (SLM-Ti-6Al-4V, n=6) while a control group was fabricated by using traditional lost-wax casting following stereolithography (CA-Co-Cr, n=6). In total, 18 RPD frameworks were digitally scanned (denoted as CRF), with each scan then superimposed on the CRF and evaluated for discrepancies by using a 3D analysis software program. A nonparametric Kruskal-Wallis test was performed to determine differences in trueness among groups (α=.05).RESULTS:
The CA-Co-Cr group showed the highest discrepancy between CEF and CRF. Statistically significant differences were found between the CA-Co-Cr and SLM-fabricated groups (P=.03 for Co-Cr, and P=.016 for Ti-6Al-4V). However, no significant difference was found between the SLM-Co-Cr and SLM-Ti-6Al-4V groups (P=.787).CONCLUSIONS:
SLM-fabricated RPD frameworks exhibited higher trueness than CA-Co-Cr fabricated ones, indicating the potential of selective laser melting to produce the geometric shapes required for accurate dental restorations.
Texto completo:
1
Colección:
01-internacional
Banco de datos:
MEDLINE
Asunto principal:
Dentadura Parcial Removible
Idioma:
En
Revista:
J Prosthet Dent
Año:
2022
Tipo del documento:
Article
País de afiliación:
China