Effective Nonstoichiometric Strategy Combined Post-annealing Process for Boosting Thermoelectric Properties in n-Type PbTe.
ACS Appl Mater Interfaces
; 16(15): 19048-19056, 2024 Apr 17.
Article
en En
| MEDLINE
| ID: mdl-38578807
ABSTRACT
The intrinsic low electrical properties have hindered the enhancement of thermoelectric performance for n-type PbTe over a long period of time, primarily due to the generation of intrinsic Pb vacancies and other defects. In this work, PbTe samples with nonstoichiometric excess Pb atoms were successfully prepared by a melting reaction followed by spark plasma sintering. First, the introduction of precisely controlled excess Pb atoms has effectively eliminated the typical p-n transition phenomenon in PbTe systems by suppressing the generation of Pb vacancies. Further, the vacuum annealing process employed in nonstoichiometric samples increases the carrier mobility significantly because of the improved crystallinity and the lowered holes. Thus, the Hall mobility was optimized from 754.3 to 1215.9 cm2 V-1 s-1, while the power factor was ultimately elevated from 3087.8 to 4565.7 µW m-1 K-2 for the Pb1.03Te sample at 323 K. Benefited from the enhanced electrical transport properties near room temperature, an average zT â¼ 1.03 ranging from 323 to 723 K was achieved, demonstrating an outstanding performance in n-type nondoped PbTe. This work provides guidance for optimizing the thermoelectric performance of n-type PbTe and relevant telluride by reducing vacancies and other defects.
Texto completo:
1
Colección:
01-internacional
Banco de datos:
MEDLINE
Idioma:
En
Revista:
ACS Appl Mater Interfaces
Asunto de la revista:
BIOTECNOLOGIA
/
ENGENHARIA BIOMEDICA
Año:
2024
Tipo del documento:
Article
País de afiliación:
China