Study on the Strength and Hydration Behavior of Sulfate-Resistant Cement in High Geothermal Environment.
Materials (Basel)
; 15(8)2022 Apr 11.
Article
em En
| MEDLINE
| ID: mdl-35454484
ABSTRACT
The hydration process and compressive strength and flexural strength development of sulphate-resistant Portland cement (SRPC) curing at 20 °C, 40 °C, 50 °C, and 60 °C were studied. In addition, MIP, XRD, SEM, and a thermodynamic simulation (using Gibbs Energy Minimization Software (GEMS)) were used to study the pore structure, the types, contents, and transformations of hydration products, and the changes in the internal micro-morphology. The results indicate that, compared with normal-temperature curing (20 °C), the early compressive strength (1, 3, and 7 d) of SRPC cured at 40~60 °C increased by 10.1~57.4%, and the flexural strength increased by 1.8~21.3%. However, high-temperature curing was unfavorable for the development of compressive strength and flexural strength in the later period (28~90 d), as they were reduced by 1.5~14.6% and 1.1~25.5%, respectively. With the increase in the curing temperature and curing age, the internal pores of the SRPC changed from small pores to large pores, and the number of harmful pores (>50 nm) increased significantly. In addition, the pore structure was further coarsened after curing at 60 °C for 90 d, and the number of multiple harmful pores (>200 nm) increased by 17.9%. High-temperature curing had no effect on the types of hydration products of the SRPC but accelerated the formation rate of hydration products. The production of the hydration products C-S-H increased by 13.5%, 18.6%, and 22.8% after curing at 40, 50, and 60 °C for 3 d, respectively. The stability of ettringite (AFt) reduced under high-temperature curing, and its diffraction peak was not observed in the XRD patterns. When the curing temperature was higher than 50 °C, AFt began to transform into monosulfate, which consumed more tricalcium aluminate hydrate and inhibited the formation of "delayed ettringite". Under high-temperature curing, the compactness of the internal microstructure of the SRPC decreased, and the distribution of hydration products was not uniform, which affected the growth in its strength during the later period.
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Idioma:
En
Revista:
Materials (Basel)
Ano de publicação:
2022
Tipo de documento:
Article
País de afiliação:
China