RESUMEN
OBJECTIVES: To evaluate minimally invasive restorations' capacity to mask discolored teeth and explore the impact of ceramic thickness, translucency, and cement color. MATERIALS AND METHODS: Twenty-four assessment pairs of naturally colored and discolored bovine dentin samples were formed, using lithium disilicate specimens in six different thicknesses (0.3-0.8 mm), two different translucencies (high, low), and two cements (transparent, tooth-colored). Evaluators assessed the color differences in each assessment pair, and the threshold for detecting a color difference was determined using sequential testing and the Bonferroni-Holm method. RESULTS: A thickness of 0.6 mm effectively masked color differences using high translucent ceramic with transparent cement, detectable differences were still observed at 0.7/0.8 mm. A threshold thickness of 0.4 mm was seen using high translucent ceramic and tooth-colored cement, with color differences still discernible at 0.5 and 0.8 mm. A threshold thickness of 0.4 mm was detected using low translucent ceramic and transparent cement, while detectable differences persisted at 0.5, 0.7, and 0.8 mm. A 0.5 mm threshold thickness was observed when using low translucent ceramic and tooth-colored cement, and no detectable color differences were detected beyond this thickness. CONCLUSIONS: Masking can be achieved with a thickness of 0.4-0.5 mm using a low translucent material and tooth-colored cement. CLINICAL SIGNIFICANCE: Understanding the impact of ceramic thickness, translucency, and cement color can aid clinicians in making informed decisions for achieving the best esthetic outcomes while preserving tooth structure. Effective masking can be accomplished with ceramic thicknesses starting at 0.4 mm, especially when employing a low translucent material and tooth-colored cement. However, clinicians should be aware that discolorations may still be detectable in certain scenarios when using minimally invasive lithium disilicate restorations.
Asunto(s)
Cerámica , Porcelana Dental , Animales , Bovinos , Porcelana Dental/química , Cementos Dentales , Cementos de Ionómero Vítreo , Ensayo de Materiales , Color , Propiedades de SuperficieRESUMEN
Since Molar Incisor Hypomineralization was first described as a pathologic entity, public perception often suggests a considerable rise in prevalence of the respective disease. Since there are still considerable doubts regarding the etiology and-accordingly-prevention of MIH and respective therapeutic approaches are difficult this question is of considerable clinical and public interest. Accordingly, a systematic literature search in accordance with the PRISMA guidelines for systematic reviews on Medline, Cochrane Database, EMBASE, LILACS, Web of Science, Google scholar, Scopus was performed to retrieve original articles reporting the prevalence of MIH as defined by the European Academy of Pediatric Dentistry (EAPD). From initially 2360 retrieved titles, 344 full texts were assessed for possible inclusion and finally 167 articles of mainly moderate to high quality and based on data of 46'613 individuals were included in the meta-analysis. All studies published before 2001 had to be excluded since it was not possible to align the findings with the EAPD classification. Studies varied considerably regarding cohort size (25 to 23'320, mean 1'235)) and age (5.6-19 y, mean 9.8 y). Over all studies, the weighted mean for the prevalence for MIH was 12.8% (95% CI 11.5%-14.1%) and no significant changes with respect to either publication year or birthyear were found. A sub-analysis of eleven studies reporting on the prevalence in different age groups, however, revealed strong evidence for an increasing prevalence between the years 1992 (3%) and 2013 (13%).Therefore, based on data from cross-sectional studies a possible rise in prevalence of MIH remains unclear. Future prospective large-scale studies under standardized examination conditions with an emphasis on examiner calibration are needed to gain better understanding in the evolution of the prevalence of MIH.
Asunto(s)
Hipoplasia del Esmalte Dental , Hipomineralización Molar , Niño , Humanos , Hipoplasia del Esmalte Dental/epidemiología , Prevalencia , Estudios Transversales , Diente Molar/patología , IncisivoRESUMEN
OBJECTIVES: To simulate the abrasive potential of an interdental brush when applied with toothpastes and prophylactic gels/solutions in a novel laboratory brushing simulation set-up. METHODS: A brushing device was customized to treat dentin samples mimicking a simplified interdental space with an interdental brush (ISO 2). The brushing, that is, 7200 strokes for 1 h, was performed with artificial saliva (control), a povidone-iodine solution, and slurries of chlorhexidine and fluoride gels as well as three toothpastes with different RDA values ranging from 29 to 100, respectively. The loss of dentin was profilometrically assessed and compared with ANOVA and Fishers LSD. RESULTS: While artificial saliva as control, the solution and the gel slurries showed no measurable dentin loss, toothpastes resulted in a measurable linear surface damage with respect to the actual intrinsic RDA values and ranged from 12.6 to 26.5 µm (p < 0.001). CONCLUSIONS: Any interdental cleaning product should be tailored and carefully instructed. Any over- and misuse should be avoided, which applies especially to the use of interdental brushes in combination with abrasive toothpastes.
Asunto(s)
Abrasión de los Dientes , Erosión de los Dientes , Humanos , Pastas de Dientes/uso terapéutico , Abrasión de los Dientes/etiología , Abrasión de los Dientes/prevención & control , Saliva Artificial , Dentina , Cepillado Dental , GelesRESUMEN
OBJECTIVES: To assess the impact of the age of resin-based composite (RBC) restorations used for deep margin elevation (DME) on the marginal quality and fracture resistance of inlays. MATERIALS AND METHODS: Permanent human molars with direct RBC restorations, involving the mesial, occlusal, and distal surface (MOD), were allocated to four groups (each n = 12). Half of the teeth underwent thermomechanical loading including 240,000 occlusal load cycles and 534 thermal cycles (TML, 5 °C/55 °C; 49 N, 1.7 Hz). With RBC left in one proximal box as DME, all teeth received MOD inlays, made from lithium disilicate (LDS) or a polymer-infiltrated ceramic network material (PICN). The restored teeth underwent TML including 1.2 million occlusal cyclic loadings and 2673 thermal cycles. The marginal quality was assessed at baseline and after both runs of TML. Load-to-fracture tests were performed. The statistical analysis comprised multiple linear regressions (α = 0.05). RESULTS: Simulated aging of RBC restorations had no significant effect on the marginal quality at the interface between the RBC and the tooth and the RBC and the inlay (p ≥ 0.247). Across time points, higher percentages of non-continuous margin were observed between the inlay and the tooth than between the tooth and the RBC (p ≤ 0.039). The age of the DME did not significantly affect the fracture resistance (p ≥ 0.052). CONCLUSIONS: Artificial aging of RBC restorations used for DME had no detrimental effect on the marginal quality and fracture resistance of LDS and PICN inlays. CLINICAL RELEVANCE: This laboratory study suggests that-in select cases-intact, direct RBC restorations not placed immediately before the delivery of an indirect restoration may be used for DME.
Asunto(s)
Resinas Compuestas , Incrustaciones , Humanos , Anciano , Materiales Dentales , Porcelana Dental , Cerámica , Diseño Asistido por Computadora , Ensayo de Materiales , Análisis del Estrés DentalRESUMEN
OBJECTIVES: To assess the behavior of dual-cure and conventional bulk-fill composite materials on real-time linear shrinkage, shrinkage stress, and degree of conversion. MATERIALS AND METHODS: Two dual-cure bulk-fill materials (Cention, Ivoclar Vivadent (with ion-releasing properties) and Fill-Up!, Coltene) and two conventional bulk-fill composites (Tetric PowerFill, Ivoclar Vivadent; SDR flow + , Dentsply Sirona) were compared to conventional reference materials (Ceram.x Spectra ST (HV), Dentsply Sirona; X-flow; Dentsply Sirona). Light curing was performed for 20 s, or specimens were left to self-cure only. Linear shrinkage, shrinkage stress, and degree of conversion were measured in real time for 4 h (n = 8 per group), and kinetic parameters were determined for shrinkage stress and degree of conversion. Data were statistically analyzed by ANOVA followed by post hoc tests (α = 0.05). Pearson's analysis was used for correlating linear shrinkage and shrinkage force. RESULTS: Significantly higher linear shrinkage and shrinkage stress were found for the low-viscosity materials compared to the high-viscosity materials. No significant difference in degree of conversion was revealed between the polymerization modes of the dual-cure bulk-fill composite Fill-Up!, but the time to achieve maximum polymerization rate was significantly longer for the self-cure mode. Significant differences in degree of conversion were however found between the polymerization modes of the ion-releasing bulk-fill material Cention, which also exhibited the significantly slowest polymerization rate of all materials when chemically cured. CONCLUSIONS: While some of the parameters tested were found to be consistent across all materials studied, heterogeneity increased for others. CLINICAL RELEVANCE: With the introduction of new classes of composite materials, predicting the effects of individual parameters on final clinically relevant properties becomes more difficult.
Asunto(s)
Resinas Compuestas , Cinética , Polimerizacion , Ensayo de Materiales , Resinas Compuestas/químicaRESUMEN
PURPOSE: To investigate the effect of over-etching and subsequent use of different adhesive application approaches including active, double, preheated, and ultrasonic application on dentin bond strength. METHODS: Dentin specimens from sound human third molars were prepared and allocated into six groups (n= 10 per group). In Group 1 (negative control), the dentin specimens were over-etched with phosphoric acid for 30 seconds, and a two-step etch-and-rinse adhesive (Prime & Bond XP; Dentsply Sirona) was applied for 20 seconds according to the manufacturer's instructions. In test Groups 2-5, the application of the adhesive varied: In Group 2, the adhesive was actively rubbed into the dentin surface, whereas in Group 3, a second adhesive layer was applied after light-curing of the first one. In Group 4, the adhesive was heated to 68°C prior to application, and in Group 5, the adhesive was ultrasonically activated. Acid-etching for 15 seconds and adhesive application for 20 seconds was performed in the positive control group (Group 6) according to the manufacturer's instructions. After light-curing and composite build-up [Ceram.x Spectra ST (HV); Dentsply Sirona], microtensile bond strength and fracture types were determined. Data were statistically analyzed by Kruskal-Wallis rank test, followed by post-hoc pairwise comparisons using Conover tests and P-value adjustment according to Holm (α= 0.05). RESULTS: Active, double, preheated, or ultrasonic adhesive application showed no significant effect on dentin bond strength when compared to the control groups. Predominantly adhesive failures were observed in all groups. CLINICAL SIGNIFICANCE: A modification of adhesive application by using active, double, preheated, or ultrasonic application does not improve bonding to accidentally over-etched dentin.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos Dentales , Humanos , Recubrimientos Dentinarios/química , Resinas Compuestas/química , Dentina , Resistencia a la Tracción , Ensayo de Materiales , Cementos de Resina/químicaRESUMEN
PURPOSE: To evaluate the effect of different varnishes on dentin permeability to erosive/abrasive challenges. METHODS: 60 superficial dentin discs were randomly allocated to six groups (n=10): Duraphat, PRG Barrier Coat, Clinpro XT, Profluorid, Fluor Protector S and untreated (control). Permeability tests were carried out: after acid conditioning, after treatment, and after abrasive/erosive challenges. The abrasive-erosive challenges were performed for 5 days (citric acid and in remineralizing saliva), as well as abrasion with toothpaste slurry (Colgate Total 12). Scanning electron microscopy (SEM) images were obtained of the dentin surfaces (5,000x) after the treatments, and after the erosive/abrasive challenges. RESULTS: Kruskal-Wallis and Dunn tests showed that all the varnishes promoted a decrease in dentin permeability directly after application, with Clinpro XT showing the highest percentage (69.52%) of dentin sealing (P= 0.0188). After the erosive/abrasive challenge, only PRG Barrier Coat varnish showed dentin sealing ability with reduced dentin permeability (42.16%) (P= 0.0014). However, none of the applied varnishes promoted a statistically significant difference in the percentage of dentin sealing, compared with the control group (P> 0.05). Clinpro XT showed a higher percentage of dentin sealing, while only PRG Barrier Coat showed reduced dentin permeability after the erosive/abrasive challenge. CLINICAL SIGNIFICANCE: Varnish containing S-PRG filler has the efficacy needed to be used as a coating material to reduce dentin permeability in situations of erosive/abrasive challenges.
Asunto(s)
Ácido Cítrico , Permeabilidad de la Dentina , Pintura , Microscopía Electrónica de Rastreo , Saliva , Pastas de Dientes , DentinaRESUMEN
BACKGROUND: Reducing the necessary time to restore primary teeth improves the cooperation of paediatric patients. This study aimed to investigate the marginal integrity of restorations prepared with a bulk-fill resin-based composite (RBC) containing additional fragmentation chain transfer (AFCT) compared to a conventional RBC when light cured with a rapid high-irradiance (3 s) and a regular (10 s) curing mode. METHODS: Forty class-II cavities were prepared in 40 primary molars. The molars were randomly divided into four groups based on the applied light-curing modes (regular: 10 s @ 1200 mW/cm2 or high-irradiance: 3 s @ 3000 mW/cm2) and the used restorative material (AFCT-containing bulk-fill RBC "Power Fill" or AFCT-free conventional RBC "Prime"). After thermo-mechanical loading, the marginal integrity was analysed using scanning electron microscopy. A beta regression model and pairwise comparisons were used to statistically analyse the data. RESULTS: The mean marginal integrity (% ± SD) of the restorations for each group was as follows: Power Fill (10 s: 79.7 ± 15.6) (3 s: 77.6 ± 11.3), Prime (10 s: 69.7 ± 11.1) (3 s: 75.0 ± 9.7). The difference between the RBCs for the same light-curing mode was statistically significant (p ≤ 0.05). The difference between the light-curing modes for the same RBC was not statistically significant (p Ë 0.5). CONCLUSIONS: AFCT-containing bulk-fill RBC "Power Fill" achieves similar marginal integrity when light-cured with either high-irradiance or regular light-curing modes. "Power Fill" achieves better marginal integrity than the conventional RBC "Prime" regardless of the applied light-curing mode.
Asunto(s)
Resinas Compuestas , Restauración Dental Permanente , Niño , Humanos , Resinas Compuestas/uso terapéutico , Luces de Curación Dental , Materiales Dentales , Curación por Luz de Adhesivos Dentales , Ensayo de Materiales , Diente PrimarioRESUMEN
OBJECTIVE: The aim of this study was to investigate the resulting abrasive dentin wear using abrasive slurries with different RDA values and applying increasing brushing forces. METHODS: Forty-five bovine incisors were randomly allocated in three groups (A, B, C, n = 15). One hundred and eighty dentin samples were prepared from these incisors and allocated to twelve groups (A1-A4, B1-B4, C1-C4; n = 15). The groups were subjected to a brushing cycle (120 strokes/min, 25 min) as follows: groups A1 to A4 with an abrasive slurry (RDA = 71) applying increasing brushing forces (1, 2, 3 and 4 N). Groups B1 to B4 were brushed using an abrasive slurry (RDA = 85) and C1 to C4 (RDA = 133) applying the same above-mentioned brushing forces. Abrasive dentin wear was recorded using a stylus profilometer and compared amongst the groups using robust models. Pairwise comparisons in each model were tested and corrected after Tukey's method (α = 0.05). RESULTS: Applying 1-N brushing force resulted in the same amount of abrasive dentin wear in all groups regardless of the abrasivity of the used slurry. Increasing the brushing force to 2 N resulted in statistically significantly higher abrasive wear in all groups. This increase in abrasive wear was much higher when the slurry with high abrasivity was used (RDA = 133) compared with the lower abrasive slurry (RDA = 71). CONCLUSION: The abrasivity of the used slurry does not add to the resulting abrasive wear when the brushing force is kept at 1 N. It seems better to advise and help the patients (showing signs of non-carious cervical lesions) calibrating their brushing force to 1 N, than only to advise them to use toothpastes with lower abrasivities.
Asunto(s)
Dentífricos , Abrasión de los Dientes , Humanos , Animales , Bovinos , Abrasión de los Dientes/etiología , Cepillado Dental/efectos adversos , Pastas de Dientes , Dentina/patologíaRESUMEN
OBJECTIVES: Very little data are known about charcoal toothpastes. The aim of this study was to counteract the missing data by determining the relative dentin abrasivity (RDA) and relative enamel abrasivity (REA) values of charcoal toothpastes. METHODS: Radioactively charged dentin and enamel samples were randomly divided into groups of eight specimens. Each group was brushed with two of total 12 charcoal toothpaste slurries and with a standard abrasive with a known RDA and REA value. The measured radioactivity in counts per minute within the slurries corresponds to the amount of dentin or enamel abraded. RDA and REA values of the charcoal toothpastes were expressed relative to the known value of the standard slurry. RESULTS: The RDA and REA values of the charcoal toothpastes have a broad range of 24-166 and 0-14, respectively. CONCLUSIONS: The RDA and REA values do not differ significantly from previously tested commercially available toothpastes. However, the lack of fluoride compounds in many of the investigated charcoal toothpastes can have a less beneficial effect for the consumers. It is very important to educate patients accordingly.
Asunto(s)
Abrasión de los Dientes , Pastas de Dientes , Humanos , Pastas de Dientes/efectos adversos , Carbón Orgánico/efectos adversos , Cepillado Dental , Dentina , Esmalte DentalRESUMEN
OBJECTIVES: The aim of this study was to evaluate the in vitro effect of enamel matrix derivative (EMD) and hyaluronic acid (HA) and their synergistic combination on lipopolysaccharides (LPS)-induced inflammation in human keratinocytes and osteoblasts. MATERIAL AND METHODS: Cells were challenged with LPS (1 µg/ml) and cultured in the following treatment groups with EMD (30 mg/ml) and HA (30 mg/ml): LPS, EMD, HA, EMD + HA, EMD + LPS, HA + LPS, and EMD + HA + LPS. Cell viability, inflammatory cytokine expression, and cell migration were determined using colorimetric assay, quantitative real-time polymerase chain reaction (qPCR), and scratch wound healing assay, respectively. RESULTS: Cell viability was decreased when exposed to LPS compared to the controls. Overall, LPS treatment expressed upregulation on inflammatory cytokine tumor necrosis factor alpha (TNF-α), interleukin 1 beta (IL-1ß), and interleukin 6 (IL-6). EMD and HA reduced up to 3.0-fold the cytokine expression caused by LPS (p < 0.05). EMD and HA statistically induced higher migration in osteoblasts and keratinocytes, respectively. Migration was impaired by LPS, whereas it significantly increased after addition of EMD and HA. CONCLUSIONS: EMD and HA are advantageous biomaterials that individually generate strong directional migratory keratinocyte and osteoblast response. Their combination also enhances cell viability, and anti-inflammatory and migratory abilities to promote healing specially under LPS inflammatory stimulus. Future in vivo and animal research is necessary to further characterize the effect of EMD and HA on periodontal regeneration. CLINICAL RELEVANCE: The use of EMD in conjunction with HA resulted in a reduction of inflammation and improvement of tissue healing at wound sites. Both biomaterials combined may potentially improve the effectiveness of bone regeneration in periodontal bone defects, pointing to the potential clinical relevance of both materials in regenerative periodontal surgery.
Asunto(s)
Proteínas del Esmalte Dental , Lipopolisacáridos , Animales , Regeneración Ósea , Humanos , Ácido Hialurónico/farmacología , OsteoblastosRESUMEN
PURPOSE: To do a systematic review and meta-analysis to determine whether laser treatment affects the bond strength of resin composites to recently bleached enamel. METHODS: This report follows the Preferred Reporting Items for Systematic Reviews and Qualitative Analyses (PRISMA) statement. Medline via PubMed, Embase, Web of Science, and the Cochrane Library databases were searched with no limits on publication year. Two reviewers independently screened all titles and abstracts to perform the study selection, data extraction, and risk-of-bias assessments. A random-effects meta-analysis model was performed using Review Manager software (version 5.3, Cochrane Collaboration). RESULTS: From the 93 records identified, seven articles that met all the inclusion criteria were included in the systematic review, and six studies were included in the meta-analysis. The overall results showed a statistically significant difference in bond strength between the control group and laser-treated group (P= 0.04; mean difference: 5.27; 95% confidence interval: 0.28 to 10.27), favoring the laser-treated group. Subgroup analyses revealed that the tooth source (bovine or human teeth) contributed to the effect of laser treatment on the bleached enamel. CLINICAL SIGNIFICANCE: Laser treatment may increase the bond strength of resin composites to recently bleached enamel. Pretreatment with a laser, preferably with Nd:YAG (1 W, frequency of 10 Hz, irradiation time of 60 seconds) or CO2 lasers (0.5 W, frequency of 10 Hz, irradiation time of 60 seconds), may be recommended to restore the bond strength of recently bleached enamel.
Asunto(s)
Recubrimiento Dental Adhesivo , Láseres de Estado Sólido , Animales , Bovinos , Resinas Compuestas/química , Recubrimiento Dental Adhesivo/métodos , Esmalte Dental , Humanos , Láseres de Estado Sólido/uso terapéuticoRESUMEN
OBJECTIVE: To investigate the effect of toothbrush bristles end configuration on the abrasive dentine wear at different brushing forces. MATERIAL AND METHODS: One hundred and sixty bovine dentine samples were randomized into eight groups (n = 20). Groups (1 to 4) were brushed with tapered-end bristles at 1-, 2-, 3-, and 4-N brushing forces, respectively. Groups (5 to 8) were brushed with round-end bristles with the same brushing forces. The brushing sequence was carried out using an abrasive slurry (RDA = 121) for 25 min. Profiles were recorded using a contact profilometer. Mean and standard deviation were calculated for the abrasive dentine wear in each group. Two-way ANOVA was used to locate any significance. The significance values were corrected after Tukey (α = 0.05). RESULTS: Brushing with tapered-end bristles resulted in statistically significantly less abrasive dentine wear than round-end bristles regardless of the applied brushing force (1 N: 4.4 ± 1.5 vs. 7.7 ± 2.0 µm; 2 N: 7.7 ± 2.1 vs. 12.2 ± 2.7 µm; 3 N: 11.3 ± 2.6 vs. 19.4 ± 3.7 µm; 4 N: 11.2 ± 2.1 vs. 25.3 ± 4.8 µm). The interaction between bristle configuration and brushing force was statistically significantly (p < 0.001). CONCLUSION: Tapered-end toothbrushes might be a safer choice for patients, especially when showing signs of non-carious cervical lesion. However, other toothbrush properties should also be considered.
Asunto(s)
Abrasión de los Dientes , Cepillado Dental , Animales , Bovinos , Análisis de Varianza , Dentina , Diseño de Equipo , Abrasión de los Dientes/etiología , Cepillado Dental/efectos adversosRESUMEN
We embedded copper-doped mesoporous bioactive glass nanospheres (Cu-MBGN) with antibacterial and ion-releasing properties into experimental dental composites and investigated the effect of Cu-MBGN on the polymerisation properties. We prepared seven composites with a BisGMA/TEGDMA (60/40) matrix and 65 wt.% total filler content, added Cu-MBGN or a combination of Cu-MBGN and silanised silica to the silanised barium glass base, and examined nine parameters: light transmittance, degree of conversion (DC), maximum polymerisation rate (Rmax), time to reach Rmax, linear shrinkage, shrinkage stress (PSS), maximum PSS rate, time to reach maximum PSS rate, and depth of cure. Cu-MBGN without silica accelerated polymerisation, reduced light transmission, and had the highest DC (58.8 ± 0.9%) and Rmax (9.8 ± 0.2%/s), but lower shrinkage (3 ± 0.05%) and similar PSS (0.89 ± 0.07 MPa) versus the inert reference (0.83 ± 0.13 MPa). Combined Cu-MBGN and silica slowed the Rmax and achieved a similar DC but resulted in higher shrinkage. However, using a combined 5 wt.% Cu-MBGN and silica, the PSS resembled that of the inert reference. The synergistic action of 5 wt.% Cu-MBGN and silanised silica in combination with silanised barium glass resulted in a material with the highest likelihood for dental applications in future.
Asunto(s)
Cobre , Nanosferas , Resinas Compuestas , Materiales Dentales , Cinética , Ensayo de Materiales , Polimerizacion , Dióxido de Silicio , Propiedades de SuperficieRESUMEN
BACKGROUND: Diamond particles have recently been used as abrasives in toothpastes, which raises questions about its abrasive behaviour towards enamel. This study was carried out to investigate the abrasive enamel wear caused by three diamond-loaded toothpastes (Candida White Diamond: CWD, Swiss Smile Diamond Glow: SSDG, Emoform F Diamond: EFD) and to compare it with a traditional toothpaste with silica abrasive (Colgate Total Original CTO). METHODS: Eighty bovine enamel samples were divided into four groups (n = 20) and brushed for 21,600 cycles (60 cycles/min) for 6 h at 2.5-N brushing force. The abrasive enamel wear was recorded with a contact profilometer. The median and interquartile range (IQR) of the abrasive enamel wear was calculated in each group. Pairwise comparisons were conducted using Wilcoxon signed rank exact test and the p value was adjusted according to Holm. Significance level was set at 0.05. RESULTS: Diamond-loaded toothpastes caused statistically significantly higher abrasive wear than the traditional toothpaste (p < 0.0001). SSDG caused statistically significantly higher enamel wear (19.0 µm (11.2)) than CWD (8.4 µm (4.6)) and EFD (7.3 µm (3.9)) (p < 0.0001). CONCLUSIONS: Diamond-loaded toothpastes cause higher enamel wear than toothpastes with traditional abrasives and also exhibit different abrasivity behaviour compared to each other.
Asunto(s)
Abrasión de los Dientes , Pastas de Dientes , Animales , Bovinos , Esmalte Dental , Diamante/efectos adversos , Humanos , Fluoruro de Sodio , Abrasión de los Dientes/etiología , Cepillado Dental/efectos adversos , Pastas de Dientes/efectos adversosRESUMEN
OBJECTIVES: To assess the mechanical stability of implants after implantoplasty and thermocyclic loading, the residual thickness of the instrumented areas and neighbouring tooth injury due to implantoplasty. MATERIALS AND METHODS: Using a phantom head simulator and maxillary model implants were subjected to an implantoplasty procedure. Thirty implants were randomly assigned to receive one of three instrumentation sequences. After instrumentation, injury on neighbouring teeth was assessed. Instrumented implants and non-instrumented controls were subjected to 1.2 million cycles of thermo-mechanical loading in a chewing machine. Afterwards, maximum fracture load for all implants and an additional five pristine control implants was tested. RESULTS: Generally, damage of neighbour teeth was a frequent finding (33 ± 56% of all cases) with considerable inter-group differences. No considerable inter-group difference for the residual implant thickness was found for different areas assessed. No implant fractured during cyclic loading. Fracture load was reduced after cyclic loading of uninstrumented implants from 2,724 ± 70 N to 2,299 ± 127 N, and after implantoplasty to 1,737 ± 165 N, while no effect by the instrumentation sequence could be observed. CONCLUSIONS: Both implantoplasty and cyclic loading were shown to reduce the implants' maximum bending strength. Cyclic loading in a laboratory masticator, simulating a five-year equivalent of chewing, did not result in fractured implants. Since neighbouring tooth injury was assessed often, care should be taken with the selection of suitable instruments.
Asunto(s)
Implantes Dentales , Fracaso de la Restauración Dental , Análisis del Estrés Dental , Humanos , Masticación , Ensayo de MaterialesRESUMEN
OBJECTIVE: To compare gingival phenotype assessment methods based on soft tissue transparency on different backgrounds and assessor experience levels. METHODS: For this purpose, 24 gingival specimens were retrieved from pig jaws with tissue thicknesses from 0.2 to 1.25 mm. Three methods were assessed: periodontal probe PCP12 (thin/thick), double-ended periodontal probe DBS12 (thin/moderate/thick) and colour-based phenotype probe CBP (thin/moderate/thick/very thick). Each sample was photographed with each probe underneath and categorized whether the probe was visible or not using different coloured backgrounds. To measure experience level influence, dentists, dental undergraduate students and laypersons (n = 10/group) performed the evaluation. RESULTS: PCP12 probe showed a threshold between 0.4 and 0.5 mm. To distinct between thin and moderate thick gingiva, a comparable range for DBS12 was found while moderate thickness was between 0.5 and 0.8 mm and for thick above 0.8 mm. CBP also showed a comparable threshold of 0.5 mm for thin versus moderate as compared with the other methods; above 0.8 mm, predominantly a very thick tissue was measured. In general, the background colour had a minor impact on PCP12 and DBS12, and investigator experience showed no clear influence on GP assessment. CONCLUSION: Based on probe transparency and within the limitation of a preclinical study, we suggest GP differentiation into three entities: thin (< 0.5 mm; high risk), moderate (0.5-0.8 mm; medium risk) and thick (> 0.8 mm; low risk). CLINICAL RELEVANCE: All three GP assessment methods are easy to perform and seem to have a high predictive value with a three entities classification for DBS12 and CBP.
Asunto(s)
Encía , Maxilar , Animales , Diferenciación Celular , Humanos , Microcirugia , Fenotipo , PorcinosRESUMEN
BACKGROUND: To assess the changes of implant surfaces of different roughness after instrumentation with ultrasonic-driven scaler tips of different materials. METHODS: Experiments were performed on two moderately rough surfaces (I-Inicell® and II-SLA®), one surface without pre-treatment (III) and one smooth machined surface (IV). Scaler tips made of steel (A), PEEK (B), titanium (C), carbon (D) and resin (E) were used for instrumentation with a standardized pressure of 100 g for ten seconds and under continuous automatic motion. Each combination of scaler tip and implant surface was performed three times on 8 titanium discs. After instrumentation roughness was assessed by profilometry, morphological changes were assessed by scanning electron microscopy, and element distribution on the utmost surface by energy dispersive X-ray spectroscopy. RESULTS: The surface roughness of discs I and II were significantly reduced by instrumentation with all tips except E. For disc III and IV roughness was enhanced by tip A and C and, only for IV, by tip D. Instrumentation with tips B, D and E left extensive residuals on surface I, II and III. The element analysis of these deposits proved consistent with the elemental composition of the respective tip materials. CONCLUSION: All ultrasonic instruments led to microscopic alterations of all types of implants surfaces assessed in the present study. The least change of implant surfaces might result from resin or carbon tips on machined surfaces.
Asunto(s)
Implantes Dentales , Ultrasonido , Desbridamiento , Raspado Dental , Humanos , Microscopía Electrónica de Rastreo , Propiedades de Superficie , TitanioRESUMEN
BACKGROUND: This in-vitro-study aimed to evaluate the potential of different fluoride gels to prevent gastroesophageal reflux induced erosive tooth wear. METHODS: Surface baseline profiles of a total of 50 bovine enamel specimens [randomly assigned to five groups (G1-5)] were recorded. All specimens were positioned in a custom made artificial oral cavity and perfused with artificial saliva (0.5 ml/min). Reflux was simulated 11 times a day during 12 h by adding HCl (pH 3.0) for 30 s (flow rate 2 ml/min). During the remaining 12 h (overnight), specimens were stored in artificial saliva and brushed twice a day (morning and evening) with a toothbrush and toothpaste slurry (15 brushing strokes). While specimens in the control group (G1) did not receive any further treatment, specimens in G2-5 were coated with different fluoride gels [Elmex Gelée (G2); Paro Amin Fluor Gelée (G3); Paro Fluor Gelée Natriumfluorid (G4); Sensodyne ProSchmelz Fluorid Gelée (G5)] in the evening for 30 s. After 20 days, surface profiles were recorded again and enamel loss was determined by comparing them with the baseline profiles. The results were statistically analysed using one-way analysis of variance (ANOVA) followed by Tukey`s HSD post-hoc test. RESULTS: The overall highest mean wear of enamel (9.88 ± 1.73 µm) was observed in the control group (G1), where no fluoride gel was applied. It was significantly higher (p < 0.001) compared to all other groups. G2 (5.03 ± 1.43 µm), G3 (5.47 ± 0.63 µm, p = 0.918) and G4 (5.14 ± 0.82 µm, p > 0.999) showed the overall best protection from hydrochloric acid induced erosion. Enamel wear in G5 (6.64 ± 0.86 µm) was significantly higher compared to G2 (p = 0.028) and G4 (p = 0.047). CONCLUSIONS: After 20 days of daily application, all investigated fluoride gels are able to significantly reduce gastroesophageal reflux induced loss of enamel.
Asunto(s)
Reflujo Gastroesofágico , Abrasión de los Dientes , Erosión de los Dientes , Desgaste de los Dientes , Animales , Bovinos , Fluoruros , Reflujo Gastroesofágico/etiología , Reflujo Gastroesofágico/prevención & control , Geles , Humanos , Fluoruro de Sodio , Erosión de los Dientes/etiología , Erosión de los Dientes/prevención & controlRESUMEN
BACKGROUND: This study aims to investigate the influence of different dentin pretreatment procedures on the resulting abrasive dentin wear. METHODS: Two groups (A, B) of 60 dentin samples each were prepared. Group A was brushed with an abrasive slurry (RDA = 85) and group B with a different abrasive slurry (RDA = 174). Four subgroups in each group (n = 15) were created (A1-A4) and (B1-B4). The subgroups were pretreated as follows: A1 + B1 with 1200-grit grinding paper, A2 + B2 with 1200- and 2000-grit papers, A3 + B3 with 1200-, 2000-, and 4000-grit papers, A4 + B4 with 1200-, 2000-, 4000-grit papers and with 1000 brushing strokes with a slurry of Elmex toothpaste. All samples were brushed for 25 min at 120 strokes/min. Abrasive dentin wear was measured for each sample profilometrically and the subgroups were compared with each other within the same group. Repeated measures one-way ANOVA was conducted to compare the subgroups and pairwise contrasts were estimated for multiple testing according to Tukey (α = 0.05). RESULTS: The resulting abrasive dentin wear in group A ranged between 15.3 ± 3.4 µm and 17.3 ± 5.5 µm and between 20.3 ± 6.8 µm and 22.5 ± 2.6 µm in group B. No statistically significant difference was noticed between any subgroups within the same group (p Ë 0.05). CONCLUSIONS: Different dentin pretreatment procedures do not affect the resulting abrasive dentin wear independent of the RDA value of the employed abrasive slurry.