Identification and Catalysis of the Potential-Limiting Step in Lithium-Sulfur Batteries.

The Li-S chemistry is thermodynamically promising for high-density energy storage but kinetically challenging. Over the past few years, many catalyst materials have been developed to improve the performance of Li-S batteries and their catalytic role has been increasingly accepted. However, the classic catalytic behavior, i.e., reduction of reaction barrier, has not been clearly observed. Crucial mechanistic questions, including what specific step is limiting the reaction rate, whether/how it can be catalyzed, and how the catalysis is sustained after the catalyst surface is covered by solid products, remain unanswered. Herein, we report the first identification of the potential-limiting step of Li-S batteries operating under lean electrolyte conditions and its catalysis that conforms to classic catalysis principles, where the catalyst lowers the kinetic barrier of the potential-limiting step and accelerates the reaction without affecting the product composition. After carefully examining the electrochemistry under lean electrolyte conditions, we update the pathway of the Li-S battery reaction: S8 solid is first reduced to Li2S8 and Li2S4 molecular species sequentially; the following reduction of Li2S4 to a Li2S2-Li2S solid with an almost constant ratio of 1:4 is the potential-limiting step; the previously believed Li2S2-to-Li2S solid-solid conversion does not occur; and the recharging reaction is relatively fast. We further demonstrate that supported cobalt phthalocyanine molecules can effectively catalyze the potential-limiting step. After Li2S2/Li2S buries the active sites, it can self-catalyze the reaction and continue driving the discharging process.

Investigation of Ca Insertion into α-MoO3 Nanoparticles for High Capacity Ca-Ion Cathodes.

Calcium-ion batteries (CIBs) are a promising alternative to lithium-ion batteries (LIBs) due to the low redox potential of calcium metal and high abundance of calcium compounds. Due to its layered structure, α-MoO3 is regarded as a promising cathode host lattice. While studies have reported that α-MoO3 can reversibly intercalate Ca ions, limited electrochemical activity has been noted, and its reaction mechanism remains unclear. Here, we re-examine Ca insertion into α-MoO3 nanoparticles with a goal to improve reaction kinetics and clarify the storage mechanism. The α-MoO3 electrodes demonstrated a specific capacity of 165 mA h g-1 centered near 2.7 V vs Ca2+/Ca, stable long-term cycling, and good rate performance at room temperature. This work demonstrates that, under the correct conditions, layered oxides can be a promising host material for CIBs and renews prospects for CIBs.

Understanding Electrochemical Reaction Mechanisms of Sulfur in All-Solid-State Batteries through Operando and Theoretical Studies.

Due to its outstanding safety and high energy density, all-solid-state lithium-sulfur batteries (ASLSBs) are considered as a potential future energy storage technology. The electrochemical reaction pathway in ASLSBs with inorganic solid-state electrolytes is different from Li-S batteries with liquid electrolytes, but the mechanism remains unclear. By combining operando Raman spectroscopy and ex situ X-ray absorption spectroscopy, we investigated the reaction mechanism of sulfur (S8 ) in ASLSBs. Our results revealed that no Li2 S8, Li2 S6, and Li2 S4 were formed, yet Li2 S2 was detected. Furthermore, first-principles structural calculations were employed to disclose the formation energy of solid state Li2 Sn (1≤n≤8), in which Li2 S2 was a metastable phase, consistent with experimental observations. Meanwhile, partial S8 and Li2 S2 remained at the full lithiation stage, suggesting incomplete reaction due to sluggish reaction kinetics in ASLSBs.

Tailoring Solution-Processable Li Argyrodites Li6+xP1-xMxS5I (M = Ge, Sn) and Their Microstructural Evolution Revealed by Cryo-TEM for All-Solid-State Batteries.

Owing to their high Li+ conductivities, mechanical sinterability, and solution processability, sulfide Li argyrodites have attracted much attention as enablers in the development of high-performance all-solid-state batteries with practicability. However, solution-processable Li argyrodites have been developed only for a composition of Li6PS5X (X = Cl, Br, I) with insufficiently high Li+ conductivities (∼10-4 S cm-1). Herein, we report the highest Li+ conductivity of 0.54 mS cm-1 at 30 °C (Li6.5P0.5Ge0.5S5I) for solution-processable iodine-based Li argyrodites. A comparative investigation of three iodine-based argyrodites of unsubstituted and Ge- and Sn-substituted solution-processed Li6PS5I with varied heat-treatment temperature elucidates the effect of microstructural evolution on Li+ conductivity. Notably, local nanostructures consisting of argyrodite nanocrystallites in solution-processed Li6.5P0.5Ge0.5S5I have been directly captured by cryogenic transmission electron microscopy, which is a first for sulfide solid electrolyte materials. Specifically, the promising electrochemical performances of all-solid-state batteries at 30 °C employing LiCoO2 electrodes tailored by the infiltration of Li6.5P0.5Ge0.5S5I-ethanol solutions are successfully demonstrated.

Introducing Fe2+ into Nickel-Iron Layered Double Hydroxide: Local Structure Modulated Water Oxidation Activity.

Exploring materials with regulated local structures and understanding how the atomic motifs govern the reactivity and durability of catalysts are a critical challenge for designing advanced catalysts. Herein we report the tuning of the local atomic structure of nickel-iron layered double hydroxides (NiFe-LDHs) by partially substituting Ni2+ with Fe2+ to introduce Fe-O-Fe moieties. These Fe2+ -containing NiFe-LDHs exhibit enhanced oxygen evolution reaction (OER) activity with an ultralow overpotential of 195 mV at the current density of 10 mA cm-2 , which is among the best OER catalytic performance to date. In-situ X-ray absorption, Raman, and electrochemical analysis jointly reveal that the Fe-O-Fe motifs could stabilize high-valent metal sites at low overpotentials, thereby enhancing the OER activity. These results reveal the importance of tuning the local atomic structure for designing high efficiency electrocatalysts.

Explore the Effects of Microstructural Defects on Voltage Fade of Li- and Mn-Rich Cathodes.

Li- and Mn-rich (LMR) cathode materials have been considered as promising candidates for energy storage applications due to high energy density. However, these materials suffer from a serious problem of voltage fade. Oxygen loss and the layered-to-spinel phase transition are two major contributors of such voltage fade. In this paper, using a combination of X-ray diffraction (XRD), pair distribution function (PDF), X-ray absorption (XAS) techniques, and aberration-corrected scanning transmission electron microscopy (STEM), we studied the effects of micro structural defects, especially the grain boundaries, on the oxygen loss and layered-to-spinel phase transition through prelithiation of a model compound Li2Ru0.5Mn0.5O3. It is found that the nanosized micro structural defects, especially the large amount of grain boundaries created by the prelithiation can greatly accelerate the oxygen loss and voltage fade. Defects (such as nanosized grain boundaries) and oxygen release form a positive feedback loop, promote each other during cycling, and accelerate the two major voltage fade contributors: the transition metal reduction and layered-to-spinel phase transition. These results clearly demonstrate the important relationships among the oxygen loss, microstructural defects and voltage fade. The importance of maintaining good crystallinity and protecting the surface of LMR material are also suggested.

Quantification of Honeycomb Number-Type Stacking Faults: Application to Na3Ni2BiO6 Cathodes for Na-Ion Batteries.

Ordered and disordered samples of honeycomb-lattice Na3Ni2BiO6 were investigated as cathodes for Na-ion batteries, and it was determined that the ordered sample exhibits better electrochemical performance, with a specific capacity of 104 mA h/g delivered at plateaus of 3.5 and 3.2 V (vs Na(+)/Na) with minimal capacity fade during extended cycling. Advanced imaging and diffraction investigations showed that the primary difference between the ordered and disordered samples is the amount of number-type stacking faults associated with the three possible centering choices for each honeycomb layer. A labeling scheme for assigning the number position of honeycomb layers is described, and it is shown that the translational shift vectors between layers provide the simplest method for classifying different repeat patterns. It is demonstrated that the number position of honeycomb layers can be directly determined in high-angle annular dark-field scanning transmission electron microscopy (STEM-HAADF) imaging studies. By the use of fault models derived from STEM studies, it is shown that both the sharp, symmetric subcell peaks and the broad, asymmetric superstructure peaks in powder diffraction patterns can be quantitatively modeled. About 20% of the layers in the ordered monoclinic sample are faulted in a nonrandom manner, while the disordered sample stacking is not fully random but instead contains about 4% monoclinic order. Furthermore, it is shown that the ordered sample has a series of higher-order superstructure peaks associated with 6-, 9-, 12-, and 15-layer periods whose existence is transiently driven by the presence of long-range strain that is an inherent consequence of the synthesis mechanism revealed through the present diffraction and imaging studies. This strain is closely associated with a monoclinic shear that can be directly calculated from cell lattice parameters and is strongly correlated with the degree of ordering in the samples. The present results are broadly applicable to other honeycomb-lattice systems, including Li2MnO3 and related Li-excess cathode compositions.

Unveiling surface redox charge storage of interacting two-dimensional heteronanosheets in hierarchical architectures.

Two-dimensional (2D) heteronanosheets are currently the focus of intense study due to the unique properties that emerge from the interplay between two low-dimensional nanomaterials with different properties. However, the properties and new phenomena based on the two 2D heteronanosheets interacting in a 3D hierarchical architecture have yet to be explored. Here, we unveil the surface redox charge storage mechanism of surface-exposed WS2 nanosheets assembled in a 3D hierarchical heterostructure using in situ synchrotron X-ray absorption and Raman spectroscopic methods. The surface dominating redox charge storage of WS2 is manifested in a highly reversible and ultrafast capacitive fashion due to the interaction of heteronanosheets and the 3D connectivity of the hierarchical structure. In contrast, compositionally identical 2D WS2 structures fail to provide a fast and high capacitance with different modes of lattice vibration. The distinctive surface capacitive behavior of 3D hierarchically structured heteronanosheets is associated with rapid proton accommodation into the in-plane W-S lattice (with the softening of the E2g bands), the reversible redox transition of the surface-exposed intralayers residing in the electrochemically active 1T phase of WS2 (with the reversible change in the interatomic distance and peak intensity of W-W bonds), and the change in the oxidation state during the proton insertion/deinsertion process. This proposed mechanism agrees with the dramatic improvement in the capacitive performance of the two heteronanosheets coupled in the hierarchical structure.

Fundamental mechanistic insights into the catalytic reactions of Li─S redox by Co single-atom electrocatalysts via operando methods.

Lithium-sulfur batteries represent an attractive option for energy storage applications. A deeper understanding of the multistep lithium-sulfur reactions and the electrocatalytic mechanisms are required to develop advanced, high-performance batteries. We have systematically investigated the lithium-sulfur redox processes catalyzed by a cobalt single-atom electrocatalyst (Co-SAs/NC) via operando confocal Raman microscopy and x-ray absorption spectroscopy (XAS). The real-time observations, based on potentiostatic measurements, indicate that Co-SAs/NC efficiently accelerates the lithium-sulfur reduction/oxidation reactions, which display zero-order kinetics. Under galvanostatic discharge conditions, the typical stepwise mechanism of long-chain and intermediate-chain polysulfides is transformed to a concurrent pathway under electrocatalysis. In addition, operando cobalt K-edge XAS studies elucidate the potential-dependent evolution of cobalt's oxidation state and the formation of cobalt-sulfur bonds. Our work provides fundamental insights into the mechanisms of catalyzed lithium-sulfur reactions via operando methods, enabling a deeper understanding of electrocatalysis and interfacial dynamics in electrical energy storage systems.

Boosting the interfacial superionic conduction of halide solid electrolytes for all-solid-state batteries.

Designing highly conductive and (electro)chemical stable inorganic solid electrolytes using cost-effective materials is crucial for developing all-solid-state batteries. Here, we report halide nanocomposite solid electrolytes (HNSEs) ZrO2(-ACl)-A2ZrCl6 (A = Li or Na) that demonstrate improved ionic conductivities at 30 °C, from 0.40 to 1.3 mS cm-1 and from 0.011 to 0.11 mS cm-1 for Li+ and Na+, respectively, compared to A2ZrCl6, and improved compatibility with sulfide solid electrolytes. The mechanochemical method employing Li2O for the HNSEs synthesis enables the formation of nanostructured networks that promote interfacial superionic conduction. Via density functional theory calculations combined with synchrotron X-ray and 6Li nuclear magnetic resonance measurements and analyses, we demonstrate that interfacial oxygen-substituted compounds are responsible for the boosted interfacial conduction mechanism. Compared to state-of-the-art Li2ZrCl6, the fluorinated ZrO2-2Li2ZrCl5F HNSE shows improved high-voltage stability and interfacial compatibility with Li6PS5Cl and layered lithium transition metal oxide-based positive electrodes without detrimentally affecting Li+ conductivity. We also report the assembly and testing of a Li-In||LiNi0.88Co0.11Mn0.01O2 all-solid-state lab-scale cell operating at 30 °C and 70 MPa and capable of delivering a specific discharge of 115 mAh g-1 after almost 2000 cycles at 400 mA g-1.

Simulated sulfur K-edge X-ray absorption spectroscopy database of lithium thiophosphate solid electrolytes.

X-ray absorption spectroscopy (XAS) is a premier technique for materials characterization, providing key information about the local chemical environment of the absorber atom. In this work, we develop a database of sulfur K-edge XAS spectra of crystalline and amorphous lithium thiophosphate materials based on the atomic structures reported in Chem. Mater., 34, 6702 (2022). The XAS database is based on simulations using the excited electron and core-hole pseudopotential approach implemented in the Vienna Ab initio Simulation Package. Our database contains 2681 S K-edge XAS spectra for 66 crystalline and glassy structure models, making it the largest collection of first-principles computational XAS spectra for glass/ceramic lithium thiophosphates to date. This database can be used to correlate S spectral features with distinct S species based on their local coordination and short-range ordering in sulfide-based solid electrolytes. The data is openly distributed via the Materials Cloud, allowing researchers to access it for free and use it for further analysis, such as spectral fingerprinting, matching with experiments, and developing machine learning models.

Carbon-free high-performance cathode for solid-state Li-O2 battery.

The development of a cathode for solid-state lithium-oxygen batteries has been hindered in practice by a low capacity and limited cycle life despite their potential for high energy density. Here, a previously unexplored strategy is proposed wherein the cathode delivers a specific capacity of 200 milliampere hour per gram over 665 discharge/charge cycles, while existing cathodes achieve only ~50 milliampere hour per gram and ~100 cycles. A highly conductive ruthenium-based composite is designed as a carbon-free cathode by first-principles calculations to avoid the degradation associated with carbonaceous materials, implying an improvement in stability during the electrochemical cycling. In addition, water vapor is added into the main oxygen gas as an additive to change the discharge product from growth-restricted lithium peroxide to easily grown lithium hydroxide, resulting in a notable increase in capacity. Thus, the proposed strategy is effective for developing reversible solid-state lithium-oxygen batteries with high energy density.

Understanding the Roles of the Electrode/Electrolyte Interface for Enabling Stable Li∥Sulfurized Polyacrylonitrile Batteries.

Sulfurized polyacrylonitrile (SPAN) is a promising high-capacity cathode material. In this work, we use spatially resolved X-ray absorption spectroscopy combined with X-ray fluorescence (XRF) microscopy, X-ray photoelectron spectroscopy, and scanning electron microscopy to examine the structural transformation of SPAN and the critical role of a robust cathode-electrolyte interface (CEI) on the electrode. LiSx species forms during the cycling of SPAN. However, in carbonate-based electrolytes and ether-based electrolytes with LiNO3 additives, these species are well protected by the CEI and do not dissolve into the electrolytes. In contrast, in an ether-based electrolyte without the LiNO3 additive, LiSx species dissolve into the electrolyte, resulting in the shuttle effect and capacity loss. Examination of the Li anode by XRF and SEM reveals dense spherical Li morphology in ether-based electrolytes, but sulfur is present in the absence of the LiNO3 additive. In contrast, porous dendritic Li is found in the carbonate electrolyte. These analyses established that an ether-based electrolyte with LiNO3 is a superior choice that enables stable cycling of both electrodes. Based on these insights, we successfully demonstrate the stable cycling of high areal loading SPAN cathode (>6.5 mA h cm-2) with lean electrolyte amounts, showing promising Li∥SPAN cell performance under practical conditions.

Identification of LiH and nanocrystalline LiF in the solid-electrolyte interphase of lithium metal anodes.

A comprehensive understanding of the solid-electrolyte interphase (SEI) composition is crucial to developing high-energy batteries based on lithium metal anodes. A particularly contentious issue concerns the presence of LiH in the SEI. Here we report on the use of synchrotron-based X-ray diffraction and pair distribution function analysis to identify and differentiate two elusive components, LiH and LiF, in the SEI of lithium metal anodes. LiH is identified as a component of the SEI in high abundance, and the possibility of its misidentification as LiF in the literature is discussed. LiF in the SEI is found to have different structural features from LiF in the bulk phase, including a larger lattice parameter and a smaller grain size (<3 nm). These characteristics favour Li+ transport and explain why an ionic insulator, like LiF, has been found to be a favoured component for the SEI. Finally, pair distribution function analysis reveals key amorphous components in the SEI.

Hierarchical nickel valence gradient stabilizes high-nickel content layered cathode materials.

High-nickel content cathode materials offer high energy density. However, the structural and surface instability may cause poor capacity retention and thermal stability of them. To circumvent this problem, nickel concentration-gradient materials have been developed to enhance high-nickel content cathode materials' thermal and cycling stability. Even though promising, the fundamental mechanism of the nickel concentration gradient's stabilization effect remains elusive because it is inseparable from nickel's valence gradient effect. To isolate nickel's valence gradient effect and understand its fundamental stabilization mechanism, we design and synthesize a LiNi0.8Mn0.1Co0.1O2 material that is compositionally uniform and has a hierarchical valence gradient. The nickel valence gradient material shows superior cycling and thermal stability than the conventional one. The result suggests creating an oxidation state gradient that hides the more capacitive but less stable Ni3+ away from the secondary particle surfaces is a viable principle towards the optimization of high-nickel content cathode materials.

Structural Stabilization of P2-type Sodium Iron Manganese Oxides by Electrochemically Inactive Mg Substitution: Insights of Redox Behavior and Voltage Decay.

Layered P2-type Na0.8 Mn0.5 Fe0.5 O2 cathode material is a promising candidate for next-generation sodium-ion batteries due to the economical and environmentally benign characteristics of Mn and Fe. The poor cycling stability of the material, however, is still a problem that must be solved. To address the problem, electrochemically inactive Mg2+ was introduced into the structure by substituting some of the Fe ions. It was shown that Mg substitution led to a smoother voltage profile with improved cycling performance and rate capability. These observations were attributed to the suppressed structural changes during electrochemical processes. Detailed redox mechanisms, associated local structural changes, and phase transitions were investigated by X-ray absorption spectroscopy and X-ray diffraction. From the detailed analysis of electrochemical behaviors, it was also identified how the redox reactions and structural disordering occurred in the high- and low-voltage regions and how Mg substitution stabilized the structure.

Revealing Reaction Pathways of Collective Substituted Iron Fluoride Electrode for Lithium Ion Batteries.

Metal fluorides present a high redox potential among the conversion-type compounds, which make them specially work as cathode materials of lithium ion batteries. To mitigate the notorious cycling instability of conversion-type materials, substitutions of anion and cation have been proposed but the role of foreign elements in reaction pathway is not fully assessed. In this work, we explored the lithiation pathway of a rutile-Fe0.9Co0.1OF cathode with multimodal analysis, including ex situ and in situ transmission electron microscopy and synchrotron X-ray techniques. Our work revealed a prolonged intercalation-extrusion-cation disordering process during phase transformations from the rutile phase to rocksalt phase, which microscopically corresponds to topotactic rearrangement of Fe/Co-O/F octahedra. During this process, the diffusion channels of lithium transformed from 3D to 2D while the corner-sharing octahedron changed to edge-sharing octahedron. DFT calculations indicate that the Co and O cosubstitution of the Fe0.9Co0.1OF cathode can improve its structural stability by stabilizing the thermodynamic semistable phases and reducing the thermodynamic potentials. We anticipate that our study will inspire further explorations on untraditional intercalation systems for secondary battery applications.

Understanding the Mechanism of High Capacitance in Nickel Hexaaminobenzene-Based Conductive Metal-Organic Frameworks in Aqueous Electrolytes.

Recently, intrinsically conductive metal-organic frameworks (MOFs) have demonstrated promising performance in fast-charging energy storage applications and may outperform some current electrode materials (e.g., porous carbons) for supercapacitors in terms of both gravimetric and volumetric capacitance. In this report, we examine the mechanism of high capacitance in a nickel hexaaminobenzene-based MOF (NiHAB). Using a combination of in situ Raman and X-ray absorption spectroscopies, as well as detailed electrochemical studies in a series of aqueous electrolytes, we demonstrate that the charge storage mechanism is, in fact, a pH-dependent surface pseudocapacitance, and unlike typical inorganic systems, where transition metals change oxidation state during charge/discharge cycles, NiHAB redox activity is ligand-centered.

Anionic redox reaction in layered NaCr2/3Ti1/3S2 through electron holes formation and dimerization of S-S.

The use of anion redox reactions is gaining interest for increasing rechargeable capacities in alkaline ion batteries. Although anion redox coupling of S2- and (S2)2- through dimerization of S-S in sulfides have been studied and reported, an anion redox process through electron hole formation has not been investigated to the best of our knowledge. Here, we report an O3-NaCr2/3Ti1/3S2 cathode that delivers a high reversible capacity of ~186 mAh g-1 (0.95 Na) based on the cation and anion redox process. Various charge compensation mechanisms of the sulfur anionic redox process in layered NaCr2/3Ti1/3S2, which occur through the formation of disulfide-like species, the precipitation of elemental sulfur, S-S dimerization, and especially through the formation of electron holes, are investigated. Direct structural evidence for formation of electron holes and (S2)n- species with shortened S-S distances is obtained. These results provide valuable information for the development of materials based on the anionic redox reaction.

Optimizing PtFe intermetallics for oxygen reduction reaction: from DFT screening to in situ XAFS characterization.

Rational designing of catalysts to promote the sluggish kinetics of the cathode oxygen reduction reaction in proton exchange membrane fuel cells is still challenging, yet of crucial importance to its commercial application. In this work, on the basis of theoretical DFT calculations which suggest that order structured fct-phased PtFe (O-PtFe) with an atomic Pt shell exhibits superior electrocatalytic performance towards the ORR, the desired structure was prepared by using a scalable impregnation-reduction method. The as-prepared O-PtFe delivered enhanced activity (0.68 A mg-1Pt) and stability (73% activity retention after 10 000 potential cycles) compared with the corresponding disordered PtFe alloy (D-PtFe) and Pt. To confirm the excellent durability, in situ X-ray absorption fine structure spectroscopy was conducted to probe the local and electronic structure changes of O-PtFe during 10 000 cycle accelerated durability testing. We hope that this facile synthesis method and the in situ XAFS experiment could be readily adapted to other catalyst systems, facilitating the screening of highly efficient ORR catalysts for fuel cell application.