RESUMEN
To avoid the agglomeration of iron NPs and improve the dispersion of Fe SAs, we employed a mixed-ligand strategy to regulate the iron content in PCN-224(ZnxFey) and PCN-222(ZnxFey). Thanks to the sublimation of Zn and the Kirkendall effect, uniform dispersions of Fe SAs with 1.04-1.06 wt% were obtained in the pyrolysis products Zn0.5Fe0.5-N-C-224 and Zn0.5Fe0.5-N-C-222 with excellent CO2 â CO activity, super-stability, and recyclability.
RESUMEN
The eCO2RR activity is correlated to the internal structural character of the catalyst. We employed two types of structural models of porphyrin-based MOFs of PCN-222(Cu) and PCN-224(Cu) into heterogeneous catalysis to illustrate the effect of structural factors on the eCO2RR performance. The composite catalyst PCN-222(Cu)/C displays better activity and selectivity (η = 450 mV, FEHCOOH = 44.3%, j = 3.2 mA cm-2) than PCN-224(Cu)/C (η = 450 mV, FEHCOOH = 34.1%, j = 2.4 mA cm-2) for the CO2 reduction to HCOOH in the range of -0.7--0.9 V (vs. RHE) due to its higher BET surface area, CO2 uptake, and a larger pore diameter. It is interesting that PCN-224(Cu)/C displays better performance in the range of -0.4--0.6 V (vs. RHE) due to its greater heat of adsorption, Qst and a higher affinity for CO2 molecule, which could promote the capture of CO2 onto the exposed active sites. As a result, PCN-224(Cu)/C exhibits better stability for the long-term electrolysis.