Optimization of decellularized human placental macroporous scaffolds for spermatogonial stem cells homing.

Decellularized scaffolds have been found to be excellent platforms for tissue engineering applications. The attempts are still being made to optimize a decellularization protocol with successful removal of the cells with minimal damages to extracellular matrix components. We examined twelve decellularization procedures using different concentrations of Sodium dodecyl sulfate and Triton X-100 (alone or in combination), and incubation time points of 15 or 30 min. Then, the potential of the decellularized scaffold as a three-dimensional substrate for colony formation capacity of mouse spermatogonial stem cells was determined. The morphological, degradation, biocompatibility, and swelling properties of the samples were fully characterized. The 0.5%/30 SDS/Triton showed optimal decellularization with minimal negative effects on ECM (P ≤ 0.05). The swelling ratios increased with the increase of SDS and Triton concentration and incubation time. Only 0.5%/15 and 30 SDS showed a significant decrease in the SSCs viability compared with other groups (P < 0.05). The SSCs colony formation was clearly observed under SEM and H&E stained slides. The cells infiltrated into the subcutaneously implanted scaffold at days 7 and 30 post-implantation with no sign of graft rejection. Our data suggest the %0.5/30 SDS/Triton as an excellent platform for tissue engineering and reproductive biology applications.

Decellularized Placental Sponge: A Platform for Coculture of Mesenchymal Stem Cells/Macrophages to Assess an M2 Phenotype and Osteogenic Differentiation In Vitro and In Vivo.

Effective communication between immune and bone-forming cells is crucial for the successful healing of bone defects. This study aimed to assess the potential of a decellularized placental sponge (DPS) as a coculture system for inducing M1/M2 polarization in macrophages and promoting osteogenic differentiation in adipose-derived mesenchymal stem cells (AD-MSCs), both in vitro and in vivo. We prepared the DPS and conducted a comprehensive characterization of its biomechanical properties, antibacterial activity, and biocompatibility. In vitro, we examined the influence of the DPS on the polarization of macrophages cocultured with AD-MSCs through nitric oxide assays, cytokine assays, phagocytosis tests, and real-time polymerase chain reaction (PCR). For in vivo assessment, we utilized micro-CT imaging, histological evaluations, and real-time PCR to determine the impact of the DPS seeded with Wharton's jelly mesenchymal stem cells (WJ-MSCs) on bone regeneration in a calvarial bone defect model. The coculture of AD-MSCs and macrophages on the DPS led to increased production of IL-10, upregulation of CD206, Arg1, and YM1 gene expression, and enhanced phagocytic capacity for apoptotic thymocytes. Concurrently, it reduced the secretion of TNF-α and nitric oxide (NO), downregulated the expression of CD86, NOS2, and IRF5 genes, and decreased macrophage phagocytosis of yeast. These results indicated polarization of macrophages toward an M2-like phenotype. In vivo, the presence of the DPS resulted in enhanced bone formation at the defect site. Immunostaining demonstrated that both the DPS and DPS + WJ-MSC constructs induced macrophage polarization toward an M2 phenotype, as compared to the control defect. In conclusion, this immunomodulatory effect, coupled with its biocompatibility and biomechanical properties resembling natural bone, positions the DPS as an attractive candidate for further exploration in the field of bone tissue engineering and regenerative medicine.

Metabolically intact nuclei are fluidized by the activity of the chromatin remodeling motor BRG1.

The structure and dynamics of the cell nucleus regulate nearly every facet of the cell. Changes in nuclear shape limit cell motility and gene expression. Although the nucleus is generally seen as the stiffest organelle in the cell, cells can nevertheless deform the nucleus to large strains by small mechanical stresses. Here, we show that the mechanical response of the cell nucleus exhibits active fluidization that is driven by the BRG 1 motor of the SWI/SNF/BAF chromatin-remodeling complex. Atomic force microscopy measurements show that the nucleus alters stiffness in response to the cell substrate stiffness, which is retained after the nucleus is isolated and that the work of nuclear compression is mostly dissipated rather than elastically stored. Inhibiting BRG 1 stiffens the nucleus and eliminates dissipation and nuclear remodeling both in isolated nuclei and in intact cells. These findings demonstrate a novel link between nuclear motor activity and global nuclear mechanics.

Electrical Stimulation of Human Mesenchymal Stem Cells on Conductive Substrates Promotes Neural Priming.

Electrical stimulation (ES) within a conductive scaffold is potentially beneficial in encouraging the differentiation of stem cells toward a neuronal phenotype. To improve stem cell-based regenerative therapies, it is essential to use electroconductive scaffolds with appropriate stiffnesses to regulate the amount and location of ES delivery. Herein, biodegradable electroconductive substrates with different stiffnesses are fabricated from chitosan-grafted-polyaniline (CS-g-PANI) copolymers. Human mesenchymal stem cells (hMSCs) cultured on soft conductive scaffolds show a morphological change with significant filopodial elongation after electrically stimulated culture along with upregulation of neuronal markers and downregulation of glial markers. Compared to stiff conductive scaffolds and non-conductive CS scaffolds, soft conductive CS-g-PANI scaffolds promote increased expression of microtubule-associated protein 2 (MAP2) and neurofilament heavy chain (NF-H) after application of ES. At the same time, there is a decrease in the expression of the glial markers glial fibrillary acidic protein (GFAP) and vimentin after ES. Furthermore, the elevation of intracellular calcium [Ca2+ ] during spontaneous, cell-generated Ca2+ transients further suggests that electric field stimulation of hMSCs cultured on conductive substrates can promote a neural-like phenotype. The findings suggest that the combination of the soft conductive CS-g-PANI substrate and ES is a promising new tool for enhancing neuronal tissue engineering outcomes.

Antibacterial smart hydrogels: New hope for infectious wound management.

Millions of people die annually due to uncured wound infections. Healthcare systems incur high costs to treat wound infections. Tt is predicted to become more challenging due to the rise of multidrug-resistant conditions. During the last decades, smart antibacterial hydrogels could attract attention as a promising solution, especially for skin wound infections. These antibacterial hydrogels are termed 'smart' due to their response to specific physical and chemical environmental stimuli. To deliver different drugs to particular sites in a controlled manner, various types of crosslinking strategies are used in the manufacturing process. Smart hydrogels are designed to provide antimicrobial agents to the infected sites or are built from polymers with inherent disinfectant properties. This paper aims to critically review recent pre-clinical and clinical advances in using smart hydrogels against skin wound infections and propose the next best thing for future trends. For this purpose, an introduction to skin wound healing and disease is presented and intelligent hydrogels responding to different stimuli are introduced. Finally, the most promising investigations are discussed in their related sections. These studies can pave the way for producing new biomaterials with clinical applications.

Conductive chitosan/polyaniline hydrogel with cell-imprinted topography as a potential substrate for neural priming of adipose derived stem cells.

Biophysical characteristics of engineered scaffolds such as topography and electroconductivity have shown potentially beneficial effects on stem cell morphology, proliferation, and differentiation toward neural cells. In this study, we fabricated a conductive hydrogel made from chitosan (CS) and polyaniline (PANI) with induced PC12 cell surface topography using a cell imprinting technique to provide both topographical properties and conductivity in a platform. The engineered hydrogel's potential for neural priming of rat adipose-derived stem cells (rADSCs) was determined in vitro. The biomechanical analysis revealed that the electrical conductivity, stiffness, and hydrophobicity of flat (F) and cell-imprinted (CI) substrates increased with increased PANI content in the CS/PANI scaffold. The conductive substrates exhibited a lower degradation rate compared to non-conductive substrates. According to data obtained from F-actin staining and AFM micrographs, both CI(CS) and CI(CS-PANI) substrates induced the morphology of rADSCs from their irregular shape (on flat substrates) into the elongated and bipolar shape of the neuronal-like PC12 cells. Immunostaining analysis revealed that both CI(CS) and CI (CS-PANI) significantly upregulated the expression of GFAP and MAP2, two neural precursor-specific genes, in rADSCs compared with flat substrates. Although the results reveal that both cell-imprinted topography and electrical conductivity affect the neural lineage differentiation, some data demonstrate that the topography effects of the cell-imprinted surface have a more critical role than electrical conductivity on neural priming of ADSCs. The current study provides new insight into the engineering of scaffolds for nerve tissue engineering.

Can Tissue Engineering Bring Hope to the Development of Human Tympanic Membrane?

The tympanic membrane (TM), more commonly known as the eardrum, consists of a thin layer of tissue in the human ear that receives sound vibrations from outside of the body and transmits them to the auditory ossicles. The TM perforations (TMPs) are a common ontological condition, which in some cases can result in permanent hearing loss. Despite the spontaneous healing capacity of the TM to regenerate in the majority of cases of acute perforation, chronic perforations require surgical interventions. However, the disadvantages of the surgical procedure include infection, anesthetic risks, and high failure of graft patency. The tissue engineering strategy, which includes the applications of a three-dimensional (3D) scaffold, cells, and biomolecules or a combination of them for the closure of chronic perforation, has been considered as an emerging treatment. Using this approach, emerging products are currently under development to regenerate the TM structure and its properties. This research aimed to highlight the problems with the current methods of TMP treatment, and critically evaluate the tissue engineering approaches, which may overcome these drawbacks. The focus of this review is on recent literature to critically discuss the emerging advanced materials used as a 3D scaffold in the development of a TM with cellular engineering, biomolecules, cells, and the fabrications of the TM and its pathway to the clinical application. In this review, we discuss the properties of TM and the advantages and disadvantages of the current clinical products for repair and replacement of the TM. Furthermore, we provide an overview of the in vitro and preclinical studies of emerging products over the past 5 years. The results of recent preclinical studies suggest that the tissue engineering field holds significant promise.

Antimicrobial peptides-loaded smart chitosan hydrogel: Release behavior and antibacterial potential against antibiotic resistant clinical isolates.

In this study, we synthesized thermo-responsive chitosan (TCTS) hydrogels, and loaded with different concentrations of antimicrobial peptide (AMP) (0, 4, 8 and 16 µg·ml-1) to fabricate an antibacterial wound dressing against resistant clinical isolates. Physico-chemical properties, release behavior, cytobiocompatibility and antibacterial activity of the AMP-TCTS hydrogels against standard strain and resistant Acinetobacter baumannii were fully determined in vitro. The TCTS-40% ß-glycerolphosphate hydrogels showed a gelation time of 15 min at 37 °C. 80% weight loss at day 35 with no changes in pH value was observed. AMP-TCTS hydrogels showed a burst release of AMP (around 40%) at day 1, and a controlled release up to day 7. A dramatic water uptake was observed at first 4 h, and then continued for 10 h in a steady manner. All the AMP-TCTS hydrogels showed excellent cytobiocompatibility for human fibroblasts. The TCTS showed no antibacterial activity against both standard strain and clinical isolates. All the AMP-TCTS hydrogels had strong antibacterial activity against standard strains, but only 16 µg·ml-1 showed antibacterial behavior against resistant A. baumannii. Our results strongly suggest the 16 µg·ml-1 AMP-TCTS hydrogel as an excellent antibacterial wound dressing against resistant A. baumannii, and now promises to proceed with pre-clinical investigations.

Thermo-responsive chitosan hydrogel for healing of full-thickness wounds infected with XDR bacteria isolated from burn patients: In vitro and in vivo animal model.

Treatment of non-healing skin wounds infected with extensively drug-resistant (XDR) bacteria remains as a big challenge. To date, different biomaterials have been applied for treatment of post-wound infections, nevertheless their efficacy for treatment of the wounds infected with XDR isolates has not been determined yet. In this study, the potential of the thermo-responsive chitosan (TCTS) hydrogel for protection of full-thickness wounds XDR bacteria isolated from burn patients was evaluated both in vitro and in vivo in a rat model. Antibacterial activity of the TCTS hydrogel against standard strain and clinical isolates of Acinetobacter baumannii, cytobiocompatibility for Hu02 fibroblast cells, degradation rate and swelling ratio were determined in vitro. MTT assay and disk diffusion test indicated no detectable cytotoxicity and antibacterial activity in vitro, respectively. In vivo study showed significant acceleration of wound healing, re-epithelialization, wound closure, and decreased colony count in the TCTS hydrogel group compared with control. This study suggests TCTS hydrogel as an excellent wound dressing for management of the wounds infected with XDR bacteria, and now promises to proceed with clinical investigations.

Physically Targeted Intravenous Polyurethane Nanoparticles for Controlled Release of Atorvastatin Calcium

Background: Intravenous drug delivery is an advantageous choice for rapid administration, immediate drug effect, and avoidance of first-pass metabolism in oral drug delivery. In this study, the synthesis, formulation, and characterization of atorvastatin-loaded polyurethane (PU) nanoparticles were investigated for intravenous route of administration. Methods: First, PU was synthesized and characterized. Second, nanoparticles were prepared in four different ratios of drug to polymer through two different techniques, including emulsion-diffusion and single-emulsion. Finally, particle size and polydispersity index, shape and surface morphology, drug entrapment efficiency (EE), drug loading, and in vitro release were evaluated by dynamics light scattering, scanning electron microscopy, and UV visible spectroscopy, respectively. Results: Within two methods, the prepared nanoparticles had a spherical shape and a smooth surface with a diversity of size ranged from 174.04 nm to 277.24 nm in emulsion-diffusion and from 306.5 nm to 393.12 in the single-emulsion method. The highest EE was 84.76%, for (1:4) sample in the emulsion-diffusion method. It has also been shown that in vitro release of nanoparticles, using the emulsion-diffusion method, was sustained up to eight days by two mechanisms: drug diffusion and polymer relaxation. Conclusion: PU nanoparticles, that were prepared by the emulsion-diffusion method, could be used as effective carriers for the controlled drug delivery of poorly water soluble drugs such as atorvastatin calcium.