RESUMEN
In this study, a strategy that can result in the polyaniline (PANI) solely confined within the nanopores of a metal-organic framework (MOF) without forming obvious bulk PANI between MOF crystals is developed. A water-stable zirconium-based MOF, UiO-66-NH2 , is selected as the MOF material. The polymerization of aniline is initiated in the acidic suspension of UiO-66-NH2 nanocrystals in the presence of excess poly(sodium 4-styrenesulfonate) (PSS). Since the pore size of UiO-66-NH2 is too small to enable the insertion of the bulky PSS, the quick formation of pore-confined solid PANI and the slower formation of well dispersed PANI:PSS occur within the MOF crystals and in the bulk solution, respectively. By taking advantage of the resulting homogeneous PANI:PSS polymer solution, the bulk PANI:PSS can be removed from the PANI/UiO-66-NH2 solid by successive washing the sample with fresh acidic solutions through centrifugation. As this is the first time reporting the PANI solely confined in the pores of a MOF, as a demonstration, the obtained PANI/UiO-66-NH2 composite material is applied as the electrode material for supercapacitors. The PANI/UiO-66-NH2 thin films exhibit a pseudocapacitive electrochemical characteristic, and their resulting electrochemical activity and charge-storage capacities are remarkably higher than those of the bulk PANI thin films.
RESUMEN
In this study, proton-conducting behaviors of a cerium-based metal-organic framework (MOF), Ce-MOF-808, its zirconium-based isostructural MOF, and bimetallic MOFs with various Zr-to-Ce ratios are investigated. The significantly increased proton conductivity (σ) and decreased activation energy (Ea) are obtained by substituting Zr with Ce in the nodes of MOF-808. Ce-MOF-808 achieves a σ of 4.4 × 10-3 S/cm at 25 °C under 99% relative humidity and an Ea of 0.14 eV; this value is among the lowest-reported Ea of proton-conductive MOFs. Density functional theory calculations are utilized to probe the proton affinities of these MOFs. As the first study reporting the proton conduction in cerium-based MOFs, the finding here suggests that cerium-based MOFs should be a better platform for the design of proton conductors compared to the commonly reported zirconium-based MOFs in future studies on energy-related applications.
RESUMEN
In this study, nanocrystals of a cerium-based metal-organic framework (Ce-MOF), Ce-MOF-808, are directly grown on the surface of carboxylic acid-functionalized carbon nanotubes (CNTs) by a facile one-step solvothermal synthesis method. Ce-MOF-CNT nanocomposites with various Ce-MOF-to-CNT ratios are synthesized, and their crystallinity, morphology, porosity, and electrical conductivity are examined. The redox-hopping and electrochemical behaviors of the pristine Ce-MOF in aqueous electrolytes are investigated, suggesting that the pristine Ce-MOF is electrochemically active but possesses a limited charge-transport behavior. As a demonstration, all the Ce-MOF, CNT, and nanocomposites are used as active materials for application in aqueous-based supercapacitors. The capacitive performance of the CNT can be significantly boosted with the help of redox-active Ce-MOF-808 nanocrystals.
RESUMEN
A redox-active vanadium-based polyoxometalate, V10O28, was post-synthetically immobilized into a water-stable zirconium-based metal-organic framework, NU-902. The adsorbed V10O28 in NU-902 renders charge hopping in the framework in aqueous electrolytes, and the obtained V10O28@NU-902 can be used as a heterogeneous electrocatalyst for electrochemical dopamine sensors.