For Tb3+-doped green phosphors, the energy transfer from Ce3+ to Tb3+ can largely enhance the absorption of excitation; however, obtaining phosphors that exhibit both high quantum efficiency and thermal stability continues to pose a significant challenge. Herein, we established a paradigm to achieve novel silicate BaY4Si5O17 (BYSO):Ce3+,Tb3+. The near-ultraviolet light efficiently excites the BYSO:Ce3+ material, causing it to emit light at a wavelength of 408 nm. The photoluminescence of BYSO:0.12Ce3+ exhibits a relatively small Stokes shift and a thermal stability of 89.8% of the 303 K emission intensity at 423 K (89.8%@423 K). The energy transfer (ET) from Ce3+ to Tb3+ ions can be readily constructed in BYSO:Ce3+,Tb3+ utilizing the overlap between the Ce3+ emission and the Tb3+ excitation. The ET efficiency from the Ce3+ to Tb3+ ions reached 83.8% at y = 1.2 and a maximum of 94.6%. Finally, the optimized phosphor BYSO:0.12Ce3+,1.2Tb3+ had an internal quantum efficiency of 94.4% and had excellent thermal stability (96.1%@423 K). Our work pointed out the avenue to novel green phosphors with high efficiency and thermal stability by choosing appropriate host and construct efficient ET.
RESUMEN
Phosphors with intrinsic white light emission are of great potential in constructing high-quality white LEDs (WLEDs). In this work, we propose the use of energy transfer from Bi3+ to Eu3+ ions for white light emission. A unique Bi3+-activated phosphor LaGdO3 (LGO):Bi3+ was generated using the conventional high-temperature solid-state process. An energy transfer was established by introducing Eu3+ into the phosphor composition. The emission colour of LGO:Bi3+,Eu3+ phosphors changes from cyan to white to orange-red depending on the Bi3+/Eu3+ doping proportion. The energy transfer between the Bi3+ and Eu3+ ions results from the dipole-dipole interaction. The LGO:Bi3+,Eu3+ phosphors were combined with a near-ultraviolet chip to successfully create a single-component WLED device with a colour-rendering index of 92.4. Our work demonstrates the energy transfer as a route for single-component white light emission and makes LGO:Bi3+,Eu3+ phosphors one of the candidate materials for near-ultraviolet lighting.