Nb-based catalysts supported on porous silica with different textural properties have been synthesized, characterized, and tested in the one-pot reaction of furfural to obtain valuable chemicals. The catalytic results reveal that the presence of fluoride in the synthesis, which limits the growing of the porous silica, limits diffusional problems of the porous silica, obtaining higher conversion values at shorter reaction times. On the other hand, the incorporation of NbOx species in the porous silica provides Lewis acid sites and a small proportion of Brönsted acid sites, in such a way that the main products are alkyl furfuryl ethers, which can be used as fuel additives.
Asunto(s)
Furaldehído , Niobio , Furaldehído/química , Hidrogenación , Dióxido de Silicio/química , CatálisisRESUMEN
Zr-doped mesoporous silicas with different textural parameters have been synthesized in the presence of structure-modifying agents, and then characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), N2 adsorption-desorption at -196 °C, NH3 thermoprogrammed desorption (NH3â»TPD), CO2 thermoprogrammed desorption (CO2â»TPD), and X-ray photoelectron spectroscopy (XPS). These porous materials were evaluated in the furfural hydrogenation through the Meerwein-Ponndorf-Verley (MPV) reaction. The catalytic results indicate that the catalyst synthesized under hydrothermal conditions and adding a pore expander agent is more active and selective to furfuryl alcohol. However, the Zr-doped porous silica catalysts that were synthesized at room temperature, which possess narrow pore sizes, tend to form i-propyl furfuryl and difurfuryl ethers, coming from etherification between furfuryl alcohol (FOL) and isopropanol molecules (used as H-donor) by a SN2 mechanism.
Asunto(s)
Furaldehído/química , Furanos/química , Dióxido de Silicio/química , Adsorción , Catálisis , Hidrogenación/efectos de los fármacos , Microscopía Electrónica de Transmisión , Espectroscopía de Fotoelectrones , Porosidad , Difracción de Rayos XRESUMEN
Three chitosans with different morphologies have been used (commercial chitosan powder, chitosan in film form and chitosan in globular form synthesized by the freeze-dried method) for the synthesis of biochars. The pyrolytic treatment has revealed that the biochar synthesized from the chitosan formed by the freeze-dried method reaches the highest CO2-adsorption capacity (4.11 mmol/g at 0 °C and a pressure of 1 bar) due to this adsorbent is highly microporous. Moreover, this biochar is more resistant to the pyrolytic treatment in comparison to the biochars obtained from the commercial chitosan and chitosan in the form of film. CO2-adsorption studies at different temperatures have also shown that the adsorption capacity diminishes as the adsorption temperature increases, thus suggesting that the adsorption takes place by a physical process.
RESUMEN
Increasing worldwide biodiesel production has led to the generation of an important glycerol surplus, which needs to be valorized in order to improve the economic and environmental sustainability of the biodiesel industry. In this context, glycerol dehydration to acrolein by acid catalysis appears to be a potential route of glycerol valorization, since acrolein is an important intermediate for many chemical industries. The main drawback of this catalytic process is catalyst deactivation. Different alternatives have been proposed for overcoming it, such as the use of mesoporous materials in order to facilitate the diffusion of glycerol and reaction products, thus minimizing deactivation. This review compiles the main achievements of the use of mesoporous silica-containing materials that have been deployed either as a catalyst or for support in glycerol dehydration to acrolein. Thus, the effect of mesoporosity on both catalytic performance and deactivation will be discussed, as well as the blocking of pores by coke deposition.
RESUMEN
Copper species have been incorporated in mesoporous silica (MS) through complexation with the amine groups of dodecylamine, which was used as a structure-directing agent in the synthesis. A series of Cu/SiO2 catalysts (xCu-MS) with copper loadings (x) from 2.5 to 20â wt % was synthesized and evaluated in the gas-phase hydrogenation of furfural (FUR). The most suitable catalytic performance in terms of 2-methylfuran yield was obtained with an intermediate copper content (10â wt %). This 10Cu-MS catalyst exhibits a 2-methylfuran yield higher than 95â mol % after 5â h time-on-stream (TOS) at a reaction temperature of 210 °C with a H2 /FUR molar ratio of 11.5 and a weight hourly space velocity (WHSV) of 1.5â h-1 . After 14â h TOS, this catalyst still showed a yield of 80â mol %. In all cases, carbonaceous deposits on the external surface were the cause of the catalyst deactivation, although sintering of the copper particles was observed for higher copper loadings. This intermediate copper loading (10â wt %) offered a suitable balance between resistance to sintering and tendency to form carbonaceous deposits.