Synthesis of a graphene oxide/agarose/hydroxyapatite biomaterial with the evaluation of antibacterial activity and initial cell attachment.

Various materials are used in bone tissue engineering (BTE). Graphene oxide (GO) is a good candidate for BTE due to its antibacterial activity and biocompatibility. In this study, an innovative biomaterial consists of GO, agarose and hydroxyapatite (HA) was synthesized using electrophoresis system. The characterization of the synthesized biomaterial showed that needle-like crystals with high purity were formed after 10 mA/10 h of electrophoresis treatment. Furthermore, the calcium-phosphate ratio was similar to thermodynamically stable HA. In the synthesized biomaterial with addition of 1.0 wt% of GO, the colony forming units test showed significantly less Staphylococcus aureus. Initial attachment of MC3T3-E1 cells on the synthesized biomaterial was observed which showed the safety of the synthesized biomaterial for cell viability. This study showed that the synthesized biomaterial is a promising material that can be used in BTE.

Electrophoresis-Aided Biomimetic Mineralization System Using Graphene Oxide for Regeneration of Hydroxyapatite on Dentin.

Graphene oxide (GO) is an emerging luminescent carbon nanomaterial with the ability to foster hydroxyapatite (HA). A specially designed electrophoresis system can be used to accelerate the mineralization process. The aim of this study was to promote HA crystal growth on demineralized dentin using a GO incorporated electrophoresis system. GO was successfully synthesized by carbonization of citric acid and its presence was confirmed by Fourier transform infrared and UV-visible spectrophotometry evaluation. Dentin slices were placed in demineralized solution and divided into control (without the electrophoresis system) and experimental group. Demineralized dentin slices in the experimental group were remineralized using the electrophoresis system for 8 h/1.0 mA, with one subgroup treated without GO and the other with GO. Energy dispersive spectroscopy evaluation showed that the calcium/phosphate ratio of the crystal formed in control and experimental group with addition of GO was close to natural hydroxyapatite. However, scanning electron microscopy evaluation showed that the exposed dentinal tubules were occluded with rod-like crystals, which is similar to native enamel morphology, in the experimental group with addition of GO compared to the flake-like crystal in the control group. Mechanical evaluation revealed that the nanohardness and modulus of remineralized dentin were significantly higher in the experimental group. In conclusion, GO is a promising material to remineralize dentin and the introduction of an electrophoresis system can accelerate its process.