We report the growth of high-quality GaN epitaxial thin films on graphene-coated c-sapphire substrates using pulsed-mode metalorganic vapor-phase epitaxy, together with the fabrication of freestanding GaN films by simple mechanical exfoliation for transferable light-emitting diodes (LEDs). High-quality GaN films grown on the graphene-coated sapphire substrates were easily lifted off by using thermal release tape and transferred onto foreign substrates. Furthermore, we revealed that the pulsed operation of ammonia flow during GaN growth was a critical factor for the fabrication of high-quality freestanding GaN films. These films, exhibiting excellent single crystallinity, were utilized to fabricate transferable GaN LEDs by heteroepitaxially growing InxGa1-xN/GaN multiple quantum wells and a p-GaN layer on the GaN films, showing their potential application in advanced optoelectronic devices.
RESUMEN
We report the growth of single-crystalline GaN microdisk arrays on graphene and their application in flexible light-emitting diodes (LEDs). Graphene layers were directly grown onc-sapphire substrates using chemical vapor deposition and employed as substrates for GaN growth. Position-controlled GaN microdisks were laterally overgrown on the graphene layers with a micro-patterned SiO2mask using metal-organic vapor-phase epitaxy. The as-grown GaN microdisks exhibited excellent single crystallinity with a uniform in-plane orientation. Furthermore, we fabricated flexible micro-LEDs by achieving heteroepitaxial growth ofn-GaN, InxGa1-xN/GaN multiple quantum wells, andp-GaN layers on graphene-coated sapphire substrates. The GaN micro-LED arrays were successfully transferred onto bendable substrates and displayed strong blue light emission under room illumination, demonstrating their potential for integration into flexible optoelectronic devices.