RESUMEN
The 660-km seismic discontinuity, which is a significant structure in the Earth's mantle, is generally interpreted as the post-spinel transition, as indicated by the decomposition of ringwoodite to bridgmanite + ferropericlase. All precise high-pressure and high-temperature experiments nevertheless report 0.5-2 GPa lower transition pressures than those expected at the discontinuity depth (i.e. 23.4 GPa). These results are inconsistent with the post-spinel transition hypothesis and, therefore, do not support widely accepted models of mantle composition such as the pyrolite and CI chondrite models. Here, we present new experimental data showing post-spinel transition pressures in complete agreement with the 660-km discontinuity depth obtained by high-resolution in situ X-ray diffraction in a large-volume high-pressure apparatus with a tightly controlled sample pressure. These data affirm the applicability of the prevailing mantle models. We infer that the apparently lower pressures reported by previous studies are experimental artefacts due to the pressure drop upon heating. The present results indicate the necessity of reinvestigating the position of mantle mineral phase boundaries previously obtained by in situ X-ray diffraction in high-pressure-temperature apparatuses.
RESUMEN
Glasses and single crystals have traditionally been used as optical windows. Recently, there has been a high demand for harder and tougher optical windows that are able to endure severe conditions. Transparent polycrystalline ceramics can fulfill this demand because of their superior mechanical properties. It is known that polycrystalline ceramics with a spinel structure in compositions of MgAl2O4 and aluminum oxynitride (γ-AlON) show high optical transparency. Here we report the synthesis of the hardest transparent spinel ceramic, i.e. polycrystalline cubic silicon nitride (c-Si3N4). This material shows an intrinsic optical transparency over a wide range of wavelengths below its band-gap energy (258 nm) and is categorized as one of the third hardest materials next to diamond and cubic boron nitride (cBN). Since the high temperature metastability of c-Si3N4 in air is superior to those of diamond and cBN, the transparent c-Si3N4 ceramic can potentially be used as a window under extremely severe conditions.
RESUMEN
Silicon dioxide has eight stable crystalline phases at conditions of the Earth's rocky parts. Many metastable phases including amorphous phases have been known, which indicates the presence of large kinetic barriers. As a consequence, some crystalline silica phases transform to amorphous phases by bypassing the liquid via two different pathways. Here we show a new pathway, a fracture-induced amorphization of stishovite that is a high-pressure polymorph. The amorphization accompanies a huge volume expansion of ~100% and occurs in a thin layer whose thickness from the fracture surface is several tens of nanometers. Amorphous silica materials that look like strings or worms were observed on the fracture surfaces. The amount of amorphous silica near the fracture surfaces is positively correlated with indentation fracture toughness. This result indicates that the fracture-induced amorphization causes toughening of stishovite polycrystals. The fracture-induced solid-state amorphization may provide a potential platform for toughening in ceramics.