RESUMEN
Mixed-matrix membranes (MMMs) comprising NH2-MIL-53(Al) and Matrimid® or 6FDA-DAM have been investigated. The MOF loading has been varied between 5 and 20 wt%, while NH2-MIL-53(Al) with three different morphologies: nanoparticles, nanorods and microneedles have been dispersed in Matrimid®. The synthesized membranes have been tested in the separation of CO2 from CH4 in an equimolar mixture. At 3 bar and 298 K for 8 wt% MOF loading, incorporation of NH2-MIL-53(Al) nanoparticles leads to the largest improvement compared to nanorods and microneedles. The incorporation of the best performing filler, i.e. NH2-MIL-53(Al) nanoparticles, to the highly permeable 6FDA-DAM has a larger effect, and the CO2 permeability increased up to 85 % with slightly lower selectivities for 20 wt% MOF loading. Specifically, these membranes have a permeability of 660 Barrer with CO2/CH4 separation factor of 28, leading to a performance very close to the Robeson limit of 2008. Furthermore, a new non-destructive technique based on Raman spectroscopy mapping is introduced to assess the homogeneity of the filler dispersion in the polymer matrix. The MOF contribution can be calculated by modelling the spectra. The determined homogeneity of the MOF filler distribution in the polymer is confirmed by FIB-SEM analysis.
RESUMEN
The synthesis of the commercially available aluminum fumarate sample A520 has been optimized and its structure analyzed through a combination of powder diffraction, solid-state NMR spectroscopy, molecular simulation, IR spectroscopy, and thermal analysis. A520 is an analogue of the MIL-53(Al)-BDC solid, but with a more rigid behavior. The differences between the commercial and the optimized samples in terms of defects have been investigated by inâ situ IR spectroscopy and correlated to their catalytic activity for ethanol dehydration.
RESUMEN
A study integrating advanced experimental and modeling tools was undertaken to characterize the microstructural and interfacial properties of mixed matrix membranes (MMMs) composed of the zeolitic imidazolate framework ZIF-8 nanoparticles (NPs) and two polymers of intrinsic microporosity (PIM-1 and PIM-EA-TB). Analysis probed both the initial ZIF-8/PIM-1 colloidal suspensions and the final hybrid membranes. By combination of dynamic light scattering (DLS) and transmission electron microscopy (TEM) analytical and imaging techniques with small-angle X-ray scattering (SAXS), the colloidal suspensions were shown to consist mainly of two distinct kinds of particles, namely, polymer aggregates of about 200 nm in diameter and densely packed ZIF-8-NP aggregates of a few 100 nm in diameter with a 3 nm thick polymer top-layer. Such aggregates are likely to impart the granular texture of ZIF-8/PIMs MMMs as shown by SEM-XEDS analysis. At the molecular scale, modeling studies showed that the surface coverage of ZIF-8 NPs by both polymers appears not to be optimal with the presence of microvoids at the interfaces that indicates only a moderate compatibility between the polymer and ZIF-8. This study shows that the microstructure of MMMs results from a complex interplay between the ZIF-8/PIM compatibility, solvent, surface chemistry of the ZIF-8 NPs, and the physicochemical properties of the polymers such as molecular structure and rigidity.