Phase analysis of tungsten and phonon behavior of beryllium layers in W/Be periodic multilayers.

In periodic W/Be multilayers, thickness-dependent microstructural and phase modifications were investigated in W and Be layers. In X-ray diffraction, α-W was predominant for the ultrathin layer of W, while ß-W evolved along with the α-W phase for higher film thickness. For the thicker layers, the thermodynamically metastable ß-W vanished and a single well-defined preferably oriented stable α-W phase was observed. The lattice spacing revealed that these phases exist in the tensile stressed condition. With the increase in thickness of Be layers, the blueshift and narrow linewidth of the transverse optical (TO) phonon mode was observed in Raman scattering studies. However, the TO mode was redshifted and the linewidth was further narrowed consistently with an increase in the thermal annealing temperature of the multilayers. The investigation has quantified an increase in compressive strain and reduction of defects with an increase in thickness of the Be layers. However, for thermally annealed samples, the compressive strain in the Be layers was relaxed and crystalline quality was improved.

Phonon, plasmon and electronic properties of surfaces and interfaces of periodic W/Si and Si/W multilayers.

The phonon and plasmon excitations and electronic properties of interfaces of periodic W/Si and Si/W multilayer structures were investigated. The Boson band originated from quasilocal surface acoustic phonons for ultrathin Si layers, excited by Raman scattering. In confined Si layers, a small fraction of crystalline Si nanoclusters were embedded within a large volume fraction of amorphous Si (a-Si) nanoclusters. The size of the a-Si nanoclusters was smaller for the thinner Si layer in the periodic layers. The plasmon energy in the Si layer was blueshifted with a decrease in the thickness of this layer. This was explained by the size-dependent quantization of plasmon shift. The valence band spectra comprised a substantial fine structure, which is associated with the interaction of valence orbitals of the W and Si atoms at the interface boundaries. For thinner Si layers, the binding interaction of W5d and Si3p states leads to the splitting of the density of states near the Fermi level in the energy range of 1.5-5 eV. However, the energy splitting with two maxima was observed at 0.7 and 2.4 eV for thicker layers. Thus, the results of X-ray photoelectron spectroscopy have indicated that the interface of W/Si multilayers consists of metal-enriched tungsten silicide. Both the atomic structure and the elemental composition of the silicide were modified with a change in the thickness of the Si layers. This novel investigation could be essential for designing nanomirrors with higher reflectivity.