The enhancement of reactive red 24 adsorption from aqueous solution using agricultural waste-derived biochar modified with ZnO nanoparticles.

In this study, two types of agricultural wastes, sugarcane bagasse (SB) and cassava root husks (CRHs), were used to fabricate biochars. The pristine biochars derived from SB and CRHs (SBB and CRHB, respectively) were modified using ZnO nanoparticles to generate modified biochars (SBB-ZnO and CRHB-ZnO, respectively) for the removal of Reactive Red 24 (RR24) from stimulated wastewater. Batch experiments were performed to evaluate the effects of ZnO nanoparticles' loading ratio, solution pH, contact time, and initial RR24 concentration on the RR24 adsorption capacity of biochars. The RR24 adsorption isotherm and kinetic data on SBB, SBB-ZnO3, CRHB, and CRHB-ZnO3 were analyzed. Results indicate that SB- and CRH-derived biochars with a ZnO nanoparticle loading ratio of 3 wt% could generate maximum adsorption capacities of RR24 thanks to the double growth on the BET surface of modified biochars. The RR24 adsorption capacities of CRHB-ZnO3 and SBB-ZnO3 reached 81.04 and 105.24 mg g-1, respectively, which were much higher than those of pristine CRHB and SBB (66.19 and 76.14, respectively) at an initial RR24 concentration of 250 mg L-1, pH 3, and contact time of 60 min. The adsorption of RR24 onto biochars agreed well with the pseudo-first-order model and the Langmuir isotherm. The RR24 adsorption capacity on modified biochars, which were reused after five adsorption-desorption cycles showed no insignificant drop. The main adsorption mechanisms of RR24 onto biochars were controlled by electrostatic interactions between biochars' surface positively charged functional groups with azo dye anions, pore filling, hydrogen bonding formation, and π-π interaction.

Extraordinary Corrosion Protection from Polymer-Clay Nanobrick Wall Thin Films.

Metals across all industries demand anticorrosion surface treatments and drive a continual need for high-performing and low-cost coatings. Here we demonstrate polymer-clay nanocomposite thin films as a new class of transparent conformal barrier coatings for protection in corrosive atmospheres. Films assembled via layer-by-layer deposition, as thin as 90 nm, are shown to reduce copper corrosion rates by >1000× in an aggressive H2S atmosphere. These multilayer nanobrick wall coatings hold promise as high-performing anticorrosion treatment alternatives to costlier, more toxic, and less scalable thin films, such as graphene, hexavalent chromium, or atomic-layer-deposited metal oxides.