Nanoscale heat transport through the hetero-interface of SrRuO3 thin films.

A SrRuO3 thin film has been widely used as a metal electrode in electronic devices based on transition metal oxides, and hence it is important to understand its thermal transport properties to minimize a thermal degradation problem during the device operation. Using the time-domain thermoreflectance measurement technique, we investigate the cross-plane thermal conductivity of the SrRuO3 thin films with a thickness variation from 1 µm to 8 nm. We find that the thermal conductivity is reduced from about 6 W m-1 K-1 for the 1 µm thick film to about 1.2 W m-1 K-1 for the 8 nm thick film, and attribute this behavior to the boundary scattering of thermal carriers which originally have the mean free path of about 20 nm in a bulk state. Also, we observe a clear dip behavior of the thermal conductivity in the intermediate thickness around 30 nm which suggests an existence of a strong scattering source other than the film boundary. We explain this result by considering an additional interfacial scattering at the tetragonal-orthorhombic phase boundary which is formed during the strain relaxation with an increase of the film thickness.

Covalent-bonding-induced strong phonon scattering in the atomically thin WSe2 layer.

In nano-device applications using two-dimensional (2D) van der Waals materials, a heat dissipation through nano-scale interfaces can be a critical issue for optimizing device performances. By using a time-domain thermoreflectance measurement technique, we examine a cross-plane thermal transport through mono-layered (n = 1) and bi-layered (n = 2) WSe2 flakes which are sandwiched by top metal layers of Al, Au, and Ti and the bottom Al2O3 substrate. In these nanoscale structures with hetero- and homo-junctions, we observe that the thermal boundary resistance (TBR) is significantly enhanced as the number of WSe2 layers increases. In particular, as the metal is changed from Al, to Au, and to Ti, we find an interesting trend of TBR depending on the WSe2 thickness; when referenced to TBR for a system without WSe2, TBR for n = 1 decreases, but that for n = 2 increases. This result clearly demonstrates that the stronger bonding for Ti leads to a better thermal conduction between the metal and the WSe2 layer, but in return gives rise to a large mismatch in the phonon density of states between the first and second WSe2 layers so that the WSe2-WSe2 interface becomes a major thermal resistance for n = 2. By using photoemission spectroscopy and optical second harmonic generation technique, we confirm that the metallization induces a change in the valence state of W-ions, and also recovers a non-centrosymmetry for the bi-layered WSe2.