Tailored PCL Scaffolds as Skin Substitutes Using Sacrificial PVP Fibers and Collagen/Chitosan Blends.

Electrospinning is a versatile technique for fabrication of made-on-purpose biomimetic scaffolds. In this study, optimized electrospun fibrous membranes were produced by simultaneous electrospinning of polycaprolactone (PCL) and polyvinylpyrrolidone (PVP), followed by the selective removal of PVP from the PCL/PVP mesh. After aminolysis, a blend of collagen/chitosan was grafted on the surface. Physicochemical characterizations as well as in vitro evaluations were conducted using different methods. Successful cell infiltration into samples was observed. It seems that the positive trend of cell ingress originates from the proper pore size obtained after removal of pvp (from 4.46 µm before immersion in water to 33.55 µm after immersion in water for 24 h). Furthermore, grafting the surface with the collagen/chitosan blend rendered the scaffolds more biocompatible with improved attachment and spreading of keratinocyte cell lines (HaCaT). Viability evaluation through MTT assay for HDF cells did not reveal any cytotoxic effects. Antibacterial assay with Staphylococcus aureus as Gram-positive and Escherichia coli as Gram-negative species corroborated the bactericidal effects of chitosan utilized in the composition of the coated blend. The results of in vitro studies along with physicochemical characterizations reflect the great potentials of the produced samples as scaffolds for application in skin tissue engineering.

Synthesis and characterization of PLGA/collagen composite scaffolds as skin substitute produced by electrospinning through two different approaches.

Skin damage can occur for many reasons, including burns and injuries, which in extreme cases can even lead to death. Different methods such as electrospinning are used to produce scaffolds used in skin tissue engineering. Natural and synthetic polymers were used in this method. It was observed that the use of both natural and synthetic polymers gives better results for cell culturing rather than using of each material solely. In this study, scaffolds of poly(lactic-co-glycolic acid) and collagen were prepared using coating and common solvent methods. The characteristics of samples were evaluated through scanning electron microscopy, porosimetry, mechanical testing, degradation behavior, and in vitro assays. The mechanical and biocompatibility test results of the scaffold prepared by coating method were better than the other one. However, the degradation rate of the common solvent was nearly five times more than coating sample that leads to cytotoxicity in contact with the skin cells.

Physical and mechanical characterization of PLLA interference screws produced by two stage injection molding method.

The purpose of this study was to produce and evaluate different mechanical, physical and in vitro cell culture characteristics of poly(L-lactic) acid (PLLA) interference screws. This work will focus on evaluating the effect of two important parameters on operation of these screws, first the tunnel diameter which is one of the most important parameters during the operation and second the thermal behavior, the main effective characteristic in production process. In this work, PLLA screws were produced by a two-stage injection molding machine. For mechanical assessment of the produced screws, Polyurethane rigid foam was used as cancellous bone and polypropylene rope as synthetic graft to simulate bone and ligament in real situation. Different tunnel diameters including 7-10 mm were evaluated for fixation strength. When the tunnel diameter was changed from 10 to 9 mm, the pull-out force has increased to about 12 %, which is probably due to the aforementioned frictional forces, however, by reducing the tunnel diameter to 8 and 7 mm, the pull-out force reduced to 16 and 50 % for 8 and 7 mm tunnel diameter, respectively. The minimum and maximum pull-out force was obtained 160.57 and 506.86 N for 7 and 9 mm tunnel diameters, respectively. For physicochemical assay, Fourier transform infrared spectroscopy (FTIR), degradation test and differential scanning calorimetry (DSC) were carried out. The crystallinity (Xc) of samples were decreased considerably from 64.3 % before injection to 32.95 % after injection with two different crystallographic forms α' and α. probably due to the fast cooling rate at room temperature. In addition, MTT and cell attachment assays were utilized by MG63 osteoblast cell line, to evaluate the cytotoxicity of the produced screws. The results revealed no cytotoxicity effect.