RESUMEN
STATEMENT OF PROBLEM: Information related to the optical and surface properties, including health compatibility, surface roughness, and esthetics, of 3D-printed dental materials is scarce. PURPOSE: The purpose of this in vitro study was to compare the physical and surface properties of a 3D-printed resin with those of materials used for interim restorations. MATERIAL AND METHODS: A 3D-printed resin (PR) (NextDent C&B MFH; 3D Systems), an autopolymerizing interim material (BA) (Protemp 4; 3M ESPE), and a composite resin (Z350) (Filtek Z350XT; 3M ESPE) were tested for degree of color change (ΔE) (n=7) at different timepoints-24 hours after polishing/baseline (P0), 8 days after polishing (P1), and after artificial aging in water at 60 °C for 24 hours (P2)-by using a CIELab-based colorimeter; flexural strength (σ) (n=10) with a 3-point bend test; Knoop hardness (H) (n=8); and surface roughness (Ra) (n=7) with a profilometer. All specimens were polished 24 hours after polymerization, except for the additional group for surface roughness (BA) without polishing (BANP). A statistical analysis was performed by using 2-way repeated-measures ANOVA followed by the Fischer test for ΔE and 1-way ANOVA followed by the Fisher test for microhardness and surface roughness (α=.05). RESULTS: The Z350 showed the highest values for σ and H, followed by PR. BA showed the lowest results for both tests (P<.05). Considering roughness, the Z350 showed similar values to those of BA but lower than PR; PR showed similar roughness when compared with BA. PR showed the highest color variation among the groups at all timepoints, followed by BA. The Z350 was the most color stable material at all timepoints. CONCLUSIONS: The 3D-printed composite resin had adequate mechanical and surface properties for an interim restorative material. It has the potential to be a low-cost workflow in dentistry, although its color stability could be a concern for long-term use.
Asunto(s)
Pulido Dental , Estética Dental , Color , Resinas Compuestas , Ensayo de Materiales , Impresión Tridimensional , Propiedades de Superficie , Flujo de TrabajoRESUMEN
Dental caries is a significant oral health issue and public health concern. Currently conceptualized as a dynamic and multifactorial process, caries is a continuum of disease stages, during which tooth damage may be reversed or controlled, depending on lesion progression. The International Caries Detection and Assessment System, when used in conjunction with the Lesion Activity Assessment (ICDAS-LAA), reflects the dynamic caries process and allows the classification of cavitated lesions according to their severity and progression, which is essential to selecting the appropriate treatment. This case report describes the diagnosis and treatment of a patient who had caries in the past and in whom old lesions remained untreated. The ICDAS-LAA was used to assess caries accurately and guide treatment decisions. The patient maintained a dietary journal for 2 weeks to help establish her risk of developing caries. Treatment involved a minimally invasive dentistry approach, which consisted of remineralization via fluoride applications, placement of a composite resin restoration, microabrasion, and periodic maintenance. During the 28-month follow-up period, rigorous control of caries risk factors was achieved, and the results were satisfactory, demonstrating the effectiveness of the ICDAS-LAA in diagnosing and managing carious lesions.
Asunto(s)
Atención Odontológica/tendencias , Caries Dental , Caries Dental/diagnóstico , Caries Dental/terapia , Femenino , Estudios de Seguimiento , Humanos , Factores de Riesgo , DienteRESUMEN
This systematic review provides an update on the effect of nanofibers as reinforcement on resin-based dental materials. A bibliographic search was conducted in MEDLINEPubMed, Embase, Web of Science, Scopus, BVS (LILACS, BBO e IBECS), Cochrane, LIVIVO, and gray literature (BDTD) to identify relevant articles up to May 2021. In vitro studies that evaluated and compared the mechanical properties of nanofibers resin-based composite materials, were eligible. No publication year or language restriction was applied, and methodological quality was assessed using two methods. In a total of 6100 potentially eligible studies, 81 were selected for full-text analysis and 35 were included for qualitative analysis. Of the 35 included studies, a total of 29 studies evaluated the flexural strength (FS) of the materials. These groups were distinguished according to the resin-based materials tested and nanofiber types. Most of the studies evaluated materials composed of glass fibers and demonstrated higher values of FS when compared to resin-based materials without nanofibers. The incorporation of nanofibers into resin-based dental materials improved the mechanical properties compared to resin-based materials without nanofibers, suggesting better performance of these materials in high-stressbearing application areas. Further clinical studies are required to confirm the efficacy of resin-based materials with nanofibers.
RESUMEN
We assessed the effect of a new coating material based on resin-modified glass-ionomer with calcium (Ca) in inhibiting the demineralization of underlying and adjacent areas surrounding caries-like lesions in enamel. The measures used were surface hardness (SH) and cross-sectional hardness (CSH). Thirty-six bovine enamel specimens (3 × 6 × 2 mm) were randomly allocated into three groups (n = 12): No treatment (NT); resin-modified glass-ionomer with Ca (Clinpro XT Varnish, 3M ESPE) (CL), and fluoride varnish (Duraphat, Colgate) (DU). The specimens were subjected to alternated immersions in demineralizing (6 h) and remineralizing solutions (18 h) for 7 days. SH measurements were conducted at standard distances of 150, 300, and 450 µm from the treatment area. CSH evaluated the mean hardness profile over the depth of the enamel surface and at standard distances from the materials. The energy-dispersive X-ray spectroscopy analysis was conducted to evaluate the demineralization bands created on the sublayer by % of calcium (Ca), phosphorus (P), and fluoride (F). Ca/P weight ratio was also calculated. Based on SH and CSH measurements, there was no difference between groups at the distances 150 µm (p = 0.882), 300 µm (p = 0.995), and 450 µm (p = 0.998). Up to 50 µm depth (at 150 µm from the treatment area), CL showed better performance than DU ( p< 0.05). NT presented higher loss of Ca and P than CL and DU (p < 0.05). There was no significant difference in the % of F ion among the three groups. The new coating material was similar to F varnish in attenuating enamel demineralization.
Asunto(s)
Calcio/química , Esmalte Dental/efectos de los fármacos , Cementos de Ionómero Vítreo/química , Cementos de Resina/química , Desmineralización Dental/prevención & control , Animales , Cariostáticos/química , Bovinos , Fluoruros Tópicos/química , Pruebas de Dureza , Concentración de Iones de Hidrógeno , Ensayo de Materiales , Distribución Aleatoria , Valores de Referencia , Reproducibilidad de los Resultados , Fluoruro de Sodio/química , Espectrometría por Rayos X , Propiedades de Superficie/efectos de los fármacos , Factores de TiempoRESUMEN
This study aimed to evaluate the polymerization properties of bulk-fill materials (low and high-viscosity) by using high-intensity continuous light and intermittent photo-activation in terms of polymerization shrinkage stress and degree of conversion (DC). The following Bulk-fill and Conventional nanofilled resin composites were evaluated: Filtek Z350XT Flow (3M/ESPE), SureFil SDR Flow (Dentsply), Filtek Bulk Fill Flow (3M/ESPE), Filtek Z350XT (3M/ESPE) and Filtek Bulk Fill Posterior (3M/ESPE). A LED device (DB 685, Dabi Atlante) was used for both protocols: continuous uniform and intermittent photo-activation (light-on and light-off cycles) with identical radiant exposure (14 J/cm2). The polymerization shrinkage stress (n=6) was evaluated by inserting a single increment of 12 mm3 between two stainless steel plates (6×2 mm) adapted to a Universal Testing Machine (UTM), at different times. Measurements were recorded after photo-activation. The degree of conversion was evaluated by Fourier transformed infrared spectroscope (FTIR) with an attenuated total reflectance (ATR) accessory (n=5). Data were analyzed by three-way ANOVA and Tukey's HSD (α=0.05) tests. Bulk Fill Posterior presented higher shrinkage stress values when photo-activated with the intermittent technique (p<0.05). The intermittent photo-activation increased the degree of conversion for the low-viscosity bulk-fills (p<0.05). Therefore, the use of modulated photo-activation (intermittent) must be indicated with caution since its use can influence the shrinkage stress and degree of conversion of composites, which varies according to the resin formulations.
Asunto(s)
Resinas Compuestas , Ensayo de Materiales , Polimerizacion , ViscosidadRESUMEN
OBJECTIVE: This study aims to evaluate the influence of the light activation of simplified adhesives on the shear bond strength of resin cements to a glass-ceramic. Three factors were evaluated: (1) cement in two levels (light cured and dual cured); (2) adhesive in two levels (Single Bond 2 and Single Bond Universal), and (3) light activation in two levels (yes or no). MATERIALS AND METHODS: Thirty-two 1-mm thick slices of a leucite-reinforced glass-ceramic (IPS Empress CAD) were divided into eight groups according to adhesive (Single Bond 2 or Single Bond Universal), cement (AllCem Veneer or AllCem), and light activation of the adhesive before application of the cement (yes or no). Ceramic surfaces were etched for 60 s with 5% hydrofluoric acid, and adhesives were applied. Four cement cylinders were made over each ceramic slice (n = 16) and then submitted to shear bond strength tests. STATISTICAL ANALYSIS: Data were analyzed with three-way ANOVA and Tukey (α = 0.05). RESULTS: There were significant differences between adhesives (P < 0.0001) and no differences between cements (P = 0.0763) and light activation (P = 0.4385). No interaction effect occurred (P = 0.05). Single Bond 2 showed higher bond strength than Single Bond Universal. CONCLUSIONS: The light activation of the adhesive before the application of the resin cement did not influence the bond strength.
RESUMEN
As resinas Bulk fill surgiram com o intuito de facilitar a restauração de cavidades profundas. A fotoativação adequada é extremamente importante para que a resina bulk fill ofereça propriedades mecânicas satisfatórias e, longevidade na restauração. Este estudo avaliou a influência da espessura do incremento na microdureza Knoop (KHN) de três resinas bulk fill (n = 5). Cinquenta amostras foram divididas de acordo com o material (Filtek Z250, Filtek One Bulk Fill e Filtek Bulk Fill Flow), espessura (2mm e 4 mm) e tempo de fotoativação (20 e 40s) - Z2502mm20s, Z2502mm40s, One2mm20s, One2mm40s, One4mm20s, One4mm40s, Flow2mm20s, Flow2mm40s, Flow4mm20s e Flow4mm40s. As análises KHN foram realizadas no topo e na base de cada amostra. Os dados foram submetidos à ANOVA a 1 critério e ao Teste de Tukey (p< 0,05). A média e desvio padrão (+/-) dos seguintes grupos foram (Z2502mm20s) 0,85 (+/- 0,01); (Z2502mm40s) 0,92 (+/- 0,01); (One2mm20s) 1,05 (+/- 0,08); (One2mm40s) 0,95 (+/- 0,04); (One4mm20s) 0,93 (+/- 0,04); (One4mm40s) 0,97 (+/ - 0,04); (Flow2mm20s) 0,92 (+/- 0,05); (Flow2mm40s) 0,89 (+/- 0,04); (Flow4mm20s) 0,79 (+/- 0,04) e (Flow4mm40s) 0,90 (+/- 0,03). Os grupos da Filtek One Bulk apresentaram um valor significativamente maior, demonstrando uma polimerização suficiente mesmo na base de incrementos com 4 mm. Concluiu-se que o aumento na espessura do incremento de resinas bulk fill não afetou negativamente a fotoativação(AU)
Bulk fill composites emerged, allowing the restoration of deep cavities easily. Appropriate lightcuring is crucial to bulk fill composite presents satisfactory mechanical properties and restoration longevity. This study evaluated the influence of thickness increment on Knoop microhardness (KHN) of three dental bulk fill composites (n=5). Fifty samples were divided according to composite (Filtek Z250, Filtek One Bulk Fill and Filtek Bulk Fill Flow), thickness (2mm and 4 mm) and time lightcuring (20 and 40 s) - Z2502mm20s, Z2502mm40s, One2mm20s, One2mm40s, One4mm20s, One4mm40s, Flow2mm20s, Flow2mm40s, Flow4mm20s e Flow4mm40s. KHN analysis were performed on the top and the base of each specimen. Data were subjected to one-way ANOVA and Tukey test (p< 0,05). The mean and standard deviation (+/-) of following groups were (Z2502mm20s) 0,85(+/-0,01); (Z2502mm40s) 0,92(+/- 0,01); (One2mm20s) 1,05(+/-0,08); (One2mm40s) 0,95(+/-0,04); (One4mm20s) 0,93 (+/-0,04); (One4mm40s) 0,97(+/-0,04); (Flow2mm20s) 0,92(+/- 0,05); (Flow2mm40s) 0,89(+/-0,04); (Flow4mm20s) 0,79(+/-0,04) e (Flow4mm40s) 0,90(+/-0,03) Filtek One Bulk groups present significantly higher value, demonstrating sufficient polymerization even on the base of 4 mm increments. It was concluded that the increase in the thickness increment of Bulk fill composites did not negatively affect the lightcure(AU)
Asunto(s)
Resinas Compuestas , Pruebas de Dureza , Materiales Dentales , PolimerizacionRESUMEN
Abstract We assessed the effect of a new coating material based on resin-modified glass-ionomer with calcium (Ca) in inhibiting the demineralization of underlying and adjacent areas surrounding caries-like lesions in enamel. The measures used were surface hardness (SH) and cross-sectional hardness (CSH). Thirty-six bovine enamel specimens (3 × 6 × 2 mm) were randomly allocated into three groups (n = 12): No treatment (NT); resin-modified glass-ionomer with Ca (Clinpro XT Varnish, 3M ESPE) (CL), and fluoride varnish (Duraphat, Colgate) (DU). The specimens were subjected to alternated immersions in demineralizing (6 h) and remineralizing solutions (18 h) for 7 days. SH measurements were conducted at standard distances of 150, 300, and 450 µm from the treatment area. CSH evaluated the mean hardness profile over the depth of the enamel surface and at standard distances from the materials. The energy-dispersive X-ray spectroscopy analysis was conducted to evaluate the demineralization bands created on the sublayer by % of calcium (Ca), phosphorus (P), and fluoride (F). Ca/P weight ratio was also calculated. Based on SH and CSH measurements, there was no difference between groups at the distances 150 µm (p = 0.882), 300 µm (p = 0.995), and 450 µm (p = 0.998). Up to 50 µm depth (at 150 µm from the treatment area), CL showed better performance than DU ( p< 0.05). NT presented higher loss of Ca and P than CL and DU (p < 0.05). There was no significant difference in the % of F ion among the three groups. The new coating material was similar to F varnish in attenuating enamel demineralization.
Asunto(s)
Animales , Bovinos , Calcio/química , Cementos de Resina/química , Esmalte Dental/efectos de los fármacos , Cementos de Ionómero Vítreo/química , Valores de Referencia , Fluoruro de Sodio/química , Espectrometría por Rayos X , Propiedades de Superficie/efectos de los fármacos , Factores de Tiempo , Ensayo de Materiales , Cariostáticos/química , Distribución Aleatoria , Fluoruros Tópicos/química , Reproducibilidad de los Resultados , Desmineralización Dental/prevención & control , Pruebas de Dureza , Concentración de Iones de HidrógenoRESUMEN
Abstract This study aimed to evaluate the polymerization properties of bulk-fill materials (low and high-viscosity) by using high-intensity continuous light and intermittent photo-activation in terms of polymerization shrinkage stress and degree of conversion (DC). The following Bulk-fill and Conventional nanofilled resin composites were evaluated: Filtek Z350XT Flow (3M/ESPE), SureFil SDR Flow (Dentsply), Filtek Bulk Fill Flow (3M/ESPE), Filtek Z350XT (3M/ESPE) and Filtek Bulk Fill Posterior (3M/ESPE). A LED device (DB 685, Dabi Atlante) was used for both protocols: continuous uniform and intermittent photo-activation (light-on and light-off cycles) with identical radiant exposure (14 J/cm2). The polymerization shrinkage stress (n=6) was evaluated by inserting a single increment of 12 mm3 between two stainless steel plates (6×2 mm) adapted to a Universal Testing Machine (UTM), at different times. Measurements were recorded after photo-activation. The degree of conversion was evaluated by Fourier transformed infrared spectroscope (FTIR) with an attenuated total reflectance (ATR) accessory (n=5). Data were analyzed by three-way ANOVA and Tukey's HSD (α=0.05) tests. Bulk Fill Posterior presented higher shrinkage stress values when photo-activated with the intermittent technique (p<0.05). The intermittent photo-activation increased the degree of conversion for the low-viscosity bulk-fills (p<0.05). Therefore, the use of modulated photo-activation (intermittent) must be indicated with caution since its use can influence the shrinkage stress and degree of conversion of composites, which varies according to the resin formulations.
Resumo O presente estudo teve como objetivo avaliar as propriedades de polimerização de materiais bulk-fill (baixa e alta viscosidade) utilizando luz contínua de alta intensidade e fotoativação intermitente em relação ao estresse de contração de polimerização e grau de conversão (DC). As seguintes resinas compostas Bulk-fill e nanohíbridas convencionais foram avaliadas: Filtek Z350XT Flow (3M/ESPE), SureFil SDR Flow (Dentsply), Filtek Bulk Fill Flow (3M/ESPE), Filtek Z350XT (3M/ESPE) e Filtek Bulk Fill Posterior (3M/ESPE). Um dispositivo de LED (DB 685, Dabi Atlante) foi utilizado nos dois protocolos: fotoativação contínua e intermitente contínua (ciclos de liga e desliga) com exposição idêntica (14 J/cm2). A tensão de contração de polimerização (n=6) foi avaliada através da inserção de um incremento único de 12 mm3 entre duas placas de aço inoxidável (6×2 mm) adaptadas a uma Máquina de Ensaio Universal (UTM), em tempos diferentes. As medições foram registradas após a fotoativação. O grau de conversão foi avaliado por FTIR-ATR (n=5). Os dados foram analisados pelos testes ANOVA a três fatores e teste de Tukey (α=0,05). A resina Bulk Fill Posterior apresentou maiores valores de tensão de contração quando fotoativadas com a técnica intermitente (p<0,05). A fotoativação intermitente aumentou o grau de conversão nas resinas bulk-fill de baixa viscosidade (p<0,05). Portanto, o uso de fotoativação modulada (intermitente) deve ser indicado com cautela, uma vez que seu uso pode influenciar a tensão de contração e o grau de conversão dos compósitos, o que varia de acordo com as formulações da resina.
Asunto(s)
Ensayo de Materiales , Resinas Compuestas , Viscosidad , PolimerizacionRESUMEN
This case report illustrates a conservative technique for reintervention on anterior composite restorations in a young patient with composite veneers. The treatment incorporated the use of photos and digital planning to establish a harmonious smile design. In order to conserve the dental tissues, existing resin composites restorations in maxillary anterior teeth were carefully removed to minimize enamel reduction, followed by a study of color and shade of teeth considering factors such as hue, chroma, luminosity, opacity, translucency and light effects. Eight direct veneers were built up with resin composite taking the optical properties of the material into account and their influence on the thickness of the layers that create specific light effects when superimposed on each other. To obtain excellent results with a predictable working protocol, nanohybrid composite systems facilitate good aesthetics, avoiding more invasive treatment in an economic manner.(AU)
O presente relato de caso ilustra uma técnica conservadora para a re-intervenção em restaurações diretas de resina composta em pacientes jovens. O tratamento consistiu em fotos e planejamento digital para obtenção de um desenho digital do sorriso individual e harmonioso. De acordo com os princípios de máxima conservação da estrutura dentária, as restaurações existentes nos dentes superiores anteriores foram criteriosamente removidas para minimizar a redução do esmalte, seguido do estudo de cor e sombra dos dentes considerando fatores como matiz, croma, valor, opacidade, translucidez e efeitos de luz. Oito facetas diretas foram realizadas em resina composta considerando as propriedades ópticas do material e a influência destas na espessura das camadas de resina para criar efeitos de luz singulares quando sobrepostas. Para a execução de uma odontologia estética e consciente, em associação a um protocolo de trabalho previsível, os sistemas de resinas compostas nanohibridas possibilitam resultados estéticos satisfatórios, evitando tratamentos mais invasivos de maneira economicamente viável.(AU)
Asunto(s)
Humanos , Resinas Compuestas , Materiales Dentales , Microabrasión del Esmalte , Estética Dental , Blanqueamiento de DientesRESUMEN
The presence of diastema, between anterior teeth, distorts a pleasing smile by concentrating the observers attention on the spaces. The patients needs and expectations must be considered in the process of treatment planning to ensure satisfaction with the treatment out comes. There are many forms of therapy that can be used for diastema closure. A carefully developed diagnosis, which includes a determination of the causal element sand advanced treatment planning, allows the mostappropriate treatment to be selected for each case. The aim of this paper is to present a multidisciplinary approach as a solution to multiple diastemata in the anterior region using gingival tissue recontouring and direct adhesive restorations, with minimumwear of the dental structure, after the orthodontic intervention, discussing the minimal intervention toobtain imperceptive and aesthetic final restoration. Thirty-six months after the treatment was carriedout, the final aesthetic was maintained with all dental element details and gingival tissue harmony, without recurrence of periodontal pockets and the preservation of the tooth color and shape...
A presença de diastemas, entre dentes anteriores, distorce um sorriso agradável, concentrando a atenção do observador para os espaços. As necessidades e expectativas do paciente devem ser consideradas no processo de planejamento para garantir a satisfação no resultado do tratamento. Existem muitas formas de tratamento que podem ser utilizadas para o fechamento de diastemas. Um diagnóstico desenvolvido cuidadosamente, que inclui a determinação dos elementos causais e planejamento avançado do tratamento, permite as eleção do tratamento mais adequado para cada caso. O objetivo deste artigo é apresentar uma abordagem multidisciplinar como solução para diastemas multiplos na região anterior usando o recontorno gengival e restaurações adesivas diretas, com mínimo desgaste da estrutura dental, após a intervenção ortodôntica discutindo a intervenção mínima para a obtenção de restaurações finais estéticas e imperceptiveis. Trinta e seis meses após o tratamento foi avaliado, a estética final foi mantida com os detalhes do elemento dental e harmonia tecido gengival, sem recorrência de bolsas periodontais e preservando a cor e forma dos dentes...
Asunto(s)
Humanos , Resinas Compuestas , Diastema , GingivoplastiaRESUMEN
A busca por padrães estticos ideais contribuiu para o advento de procedimentos restauradores que possibilitam a mimetizaÆo do natural e a introduÆo do conceito de harmonia do sorriso atendendo s exigncias dos pacientes. A presena de diastemas anteriores m£ltiplos constitui um desafio Odontologia, tendo em vista o aspecto negativo que agrega a desproporÆo do sorriso e a esttica facial. Sendo assim, o presente caso objetiva descrever a tcnica operat¢ria do fechamento de diastemas em resina composta atravs de embasamento te¢rico cient¡fico para a resoluÆo do caso. O caso descrito relata a reabilitaÆo esttica de diastemas anteriores por meio de procedimentos restauradores diretos em resina composta promovendo a preservaÆo da estrutura dent ria, mimetizaÆo do natural, restabelecimento das corretas proporães dentais e reduÆo do tempo cl¡nico necess rio, alcanando resultados estticos de excelncia. A realizaÆo de uma tcnica padronizada e bem fundamentada em resina composta para o fechamento de diastemas proporciona resultados cl¡nicos estticos satisfat¢rios e previs¡veis.
The indreasing serach for aesthetic standards has collaborated for the advent of restorative procedures that allow a natural apearence and has lauched concept of harmonic smile, meeting patients expectations. Considered as a negative aspect of smile and facial aesthetics the presence of multiple anterior diastemas is very chalenging. This case report aims to describe the technique of the diastema closure with composite resin considering the scientific literature for the resolution of the case. In this study the is described the aesthetic rehabilitation of anterior distaemas through of direct restorative procedures with composite resin and preservation of tooth structure, mimicking natural teeth, reestablishment of dental proportions and reduced clinical time, achieving excellent aesthetic results. The implementation of a standardized and wellgrounded technique using composite for diastema closure provides clinical and aesthetic satisfactory and predictable results.
Asunto(s)
Humanos , Femenino , Adulto Joven , Resinas Compuestas , Diastema/cirugía , Estética Dental , Satisfacción del PacienteRESUMEN
Os avanços tecnológicos e os inúmeros achados biológicos que a ciência proporciona oferecem importantes conhecimentos e opções de tratamentos ao cirurgião-dentista, principalmente no campo dos materiais para enxerto, através da identificação de substâncias com capacidade de desempenhar a função desejada sem induzir toxicidade tecidual, gerando respostas celulares benéfcas que venham a otimizar a terapia proposta. Dentre estes materiais, as proteínas morfogenéticas ósseas (BMPs), pertencentes ao grupo dos fatores de crescimento beta TGF-β,vem ganhando grande destaque nas pesquisas, pois são capazes de induzir a neoformação tecidual. O presente trabalho propôs a discussão sobre o mecanismo de ação das BMPs, a fm de explicar sua aplicabilidade clínica e as perspectivas futuras na Odontologia.