RESUMEN
AIM: Calcium hydroxide (CH) has been considered as a direct pulp capping materials (DPC) for the last decades despite having some limitations. Phosphorylate pullulan (PPL) incorporated with CH (CHPPL) is a novel biomaterial that was introduced as a promising DPC material. Thus, the aim of the study was to evaluate the inflammatory response and mineralized tissue formation (MTF) ability of PPL-based CH formulations on rat molars after DPC. METHODOLOGY: This study consisted of six groups: CH with 1% PPL (CHPPL-1); 3% PPL (CHPPL-3); 5% PPL (CHPPL-5); Dycal and NEX MTA Cement (N-MTA) as the positive control, and no capping materials (NC). One hundred twenty maxillary first molar cavities were prepared on Wistar rats. After capping, all the cavities were restored with 4-META/MMA-TBB resin and pulpal responses were evaluated at days 1, 7, and 28. Kruskal-Wallis followed by Mann-Whitney U-test was performed with a significance level of 0.05. Immunohistochemical expression of IL-6, Nestin, and DMP-1 was observed. RESULTS: At day 1, CHPPL-1, N-MTA, and Dycal exhibited no to mild inflammation, whilst CHPPL-3, CHPPL-5, and NC showed mild to moderate inflammation, and the results were significantly different (p < .05). At day 7, mild to moderate inflammation was observed in CHPPL-1, N-MTA, and Dycal, whereas CHPPL-3, CHPPL-5, and NC exhibited moderate to severe inflammation. Significant differences were observed between CHPPL-1 and N-MTA with NC (p < .05), CHPPL-1 and CHPPL-3 with CHPPL-5 and Dycal (p < .05), and CHPPL-3 with N-MTA (p < .05). A thin layer of mineralized tissue formation (MTF) was observed in all groups. At day 28, CHPPL-1, Dycal, and N-MTA showed no to mild inflammation, whilst CHPPL-3, CHPPL-5, and NC exhibited mild to severe inflammation, and statistically significant difference was detected (p < .05). CHPPL-1, Dycal, and N-MTA exhibited continuous MTF, whilst CHPPL-3, CHPPL-5, and NC had thicker and interrupted MTF. Significant differences were observed between CHPPL-1, CHPPL-3, and N-MTA with NC group (p < .05). Variable expressions of IL-6, Nestin, and DMP-1 indicated differences in the materials' impact on odontoblast-like cell formation and tissue mineralization. CONCLUSIONS: These findings suggest that CHPPL-1 has the potential to minimize pulpal inflammation and promote MTF and had similar efficacy as MTA cement.
Asunto(s)
Hidróxido de Calcio , Recubrimiento de la Pulpa Dental , Glucanos , Materiales de Recubrimiento Pulpar y Pulpectomía , Ratas Wistar , Animales , Glucanos/farmacología , Hidróxido de Calcio/farmacología , Ratas , Materiales de Recubrimiento Pulpar y Pulpectomía/farmacología , Recubrimiento de la Pulpa Dental/métodos , Compuestos de Calcio/farmacología , Compuestos de Aluminio , Combinación de Medicamentos , Masculino , Silicatos/farmacología , Pulpa Dental/efectos de los fármacos , Pulpa Dental/metabolismo , Fosforilación , Óxidos , Diente Molar , MineralesRESUMEN
AIM: To evaluate the dental pulp response to a novel mineral trioxide aggregate containing phosphorylated pullulan (MTAPPL) in rats after direct pulp capping. METHODS: Ninety-six cavities were prepared in the maxillary first molars of 56 male Wistar rats. The dental pulps were intentionally exposed and randomly divided into four groups according to the application of pulp capping materials: MTAPPL; phosphorylated pullulan (PPL); a conventional MTA (Nex-Cem MTA, NCMTA; positive control); and Super-Bond (SB; negative control). All cavities were restored with SB and observed for pulpal responses at 1-, 3-, 7- and 28-day intervals using a histological scoring system. Statistical analysis was performed using Kruskal-Wallis and Mann-Whitney U-test with Bonferroni's correction, and the level of significance was set at 0.05. DMP1 and CD34 antigen were used to evaluate odontoblast differentiation and pulpal vascularization, respectively. RESULTS: On day 1, mild inflammatory cells were present in MTAPPL and NCMTA groups; fewer inflammatory cells were present in the PPL, whereas SB was associated with a mild-to-moderate inflammatory response. A significant difference was observed between PPL and SB (p < .05). No mineralized tissue deposition was observed. On day 3, moderate-to-severe inflammatory cells were present in PPL and SB, whereas MTAPPL and NCMTA had a mild inflammatory response. Initial mineralized tissue deposition was observed in the NCMTA, MTAPPL and SB. A significant difference was observed between MTAPPL and PPL (p < .05). On day 7, a thin layer of mineralized tissue was observed in all tested groups with no or mild inflammatory response. On day 28, no inflammatory response was observed in MTAPPL, whereas NCMTA, PPL and SB had mild inflammatory responses. A significant difference was observed between MTAPPL and SB (p < .05). Complete mineralized tissue barrier formation was observed in MTAPPL, NCMTA and PPL with no significant difference (p > .05). SB exhibited incomplete mineralized tissue barriers, significantly different from NCMTA, MTAPPL and PPL (p < .05). The staining with CD34 was positive in all the groups on all observation days. CONCLUSION: The favourable pulpal responses and induction of mineralized tissue formation associated with MTAPPL indicate its potential application as a direct pulp capping material.
Asunto(s)
Recubrimiento de la Pulpa Dental , Materiales de Recubrimiento Pulpar y Pulpectomía , Compuestos de Aluminio , Animales , Compuestos de Calcio , Pulpa Dental , Combinación de Medicamentos , Glucanos , Masculino , Diente Molar , Óxidos , Materiales de Recubrimiento Pulpar y Pulpectomía/uso terapéutico , Ratas , Ratas Wistar , SilicatosRESUMEN
OBJECTIVE: To evaluate the shade matching ability of a novel supra-nano filled esthetic resin composite employing structural color technology using simplified simulated clinical cavities. Filler morphology and light transmittance characteristics were also evaluated. MATERIALS AND METHODS: One-hundred and twenty frames of resin composite were built in A1, A2, A3, and A4 shades to simulate Class I cavities (diameter = 4 mm, height = 2 mm). For each shaded frame, cavities were filled with three different types of filler containing resin composites (n = 10): supra-nano filled (SN filled) resin composite, microhybrid filled (MH filled) resin composite, and clustered-nano filled (CN filled) resin composite. Color parameters were calculated using CIELAB (â³Eab ) and CIEDE2000 (â³E00 ). Data were analyzed using one-way analysis of variance (ANOVA), followed by Duncan's test (α = .05). Filler morphology and light transmittance characteristics were measured to explore the role of structural color on shade matching. RESULTS: â³Eab and â³E00 of SN filled resin composite were significantly lower in A2, A3, and A4 shades (P < .05). CONCLUSIONS: The SN filled resin composite showed better shade matching with A2, A3, and A4 shades of resin composite frames compared to MH filled resin composite, and CN filled resin composite. CLINICAL SIGNIFICANCE: Universal-shade resin composites, which were expected to match nearly all shades, simplify the restorative procedure. Resin composite, which contained spherical supra-nano filler particles, could contribute most to its shade matching by stimulating structural color. Structural color technology may provide additional benefits for shade matching of resin composites.
Asunto(s)
Caries Dental , Estética Dental , Color , Resinas Compuestas , Humanos , Ensayo de MaterialesRESUMEN
BACKGROUND: This study aimed to evaluate the color matching, light transmittance, and reflectance characteristics of the novel flowable resin composite OCF-001 (OCF). METHODS: Fifty-four resin composite molds were made with simulated class I cavities of A2, A3, and A4 shades by filling the rubber mold interspace with Estelite Sigma Quick (ESQ), Gracefil Putty (GP) and Filtek Supremme Ultra (FSU). After applying the adhesive, three different flowable resin composites (n = 6), OCF, Gracefil LoFlo (GLF), and Supreme Ultra Flowable (SUF), were used to fill the cavities. A colorimeter was used to measure the color parameters (CIEDE2000). The color measurements were taken immediately and after 28 days. Data were analyzed using the nonparametric Kruskal-Wallis (α = 0.05) and Wilcoxon tests. The light transmittance and reflection characteristics were measured with a black background using a spectrophotometer under D65 illumination. RESULTS: The ΔE00, and ΔC of OCF was lower than other tested materials in A2 and A3 shades both immediately and after 28 days. OCF showed the highest transmittance characteristic, and a relatively stable reflectance curve in all the wavelengths. CONCLUSIONS: OCF showed better shade matching with the surrounding shades of A2 and A3, a relative uniform reflectance and higher light transmission properties.
RESUMEN
The purpose of this study was to evaluate the microtensile bond strength (µTBS) and Knoop hardness number (KHN) of a novel experimental light-cured resin cement (HL). Eighteen flat dentin surfaces of human molars were polished using #600 SiC paper and bonded to CAD/CAM resin blocks with the respective resin cements and composites: HL, Panavia V5 (PV), and Clearfil AP-X (AP). All specimens were stored in distilled water at 37 °C for 24 h and 7 days. Scanning electron microscope (SEM) and energy dispersive X-ray (EDX) observations were performed to evaluate filler morphology and to detect the elements. The resin cements had a significant effect on the immediate µTBS (F = 22.59, p < 0.05) and after water storage µTBS (F = 22.83, p < 0.05). Significant differences (p < 0.05) in the KHN between the tested materials were observed, and HL indicated the highest KHN when compared with PV. HL showed a combination of the regular-shaped filler and spherical-shaped filler within the matrix. Silicon was detected in HL from the EDX evaluation. HL exhibited better bonding performance and polymerization, which may have contributed to the improvement of the adhesive strength.
RESUMEN
This study aimed to evaluate the pulpal responses of monkey's pulp after direct pulp capping (DPC) with the novel mineral trioxide aggregate containing phosphorylated pullulan-based material (MTAPPL). Seventy-two teeth were randomly divided into four groups: MTAPPL; Nex-Cem MTA (NX); TheraCal LC (TH); and Dycal (DY). Histopathological changes in the pulps were observed at days 3, 7 and 70. On day 3, mild inflammatory responses were observed in the MTAPPL, no to moderate inflammatory responses in the TH, whereas moderate inflammatory responses in the NX and DY. No mineralized tissue formation (MTF) was observed in all groups. On day 7, no or mild inflammatory responses were observed in all groups. Initial MTF was observed except for DY. No inflammation with complete MTF including presence of odontoblast-like cells was observed in the MTAPPL, NX and TH groups at day 70. These findings indicate that MTAPPL could be an efficient DPC material.
Asunto(s)
Recubrimiento de la Pulpa Dental , Materiales de Recubrimiento Pulpar y Pulpectomía , Compuestos de Aluminio , Compuestos de Calcio , Hidróxido de Calcio , Pulpa Dental , Combinación de Medicamentos , Glucanos , Óxidos , SilicatosRESUMEN
OBJECTIVE: The purpose of this study was to determine the bond stability and the change in interfacial ultra-structure of a conventional glass-ionomer cement bonded to dentin, with and without pre-treatment using a polyalkenoic acid conditioner. METHODS: The occlusal dentin surfaces of six teeth were ground flat. Glass-ionomer cement was bonded to the surfaces either with or without polyalkenoic acid conditioning. The teeth were sectioned into 1-mm2 stick-shaped specimens. The specimens obtained were randomly assigned to two groups with different periods of storage in water: 1 week and 1 year. The micro-tensile bond strength (µTBS) was determined for each storage time. Additional specimens were prepared for Transmission Electron Microscopy (TEM); they were produced with or without prior polyalkenoic acid conditioning in the same way as in the µTBS test. RESULTS: There was no significant difference in µTBS to conditioned dentin and non-conditioned dentin (pâ¯>â¯0.05). The failures appeared to be of a mixed nature, although aging caused more areas of cohesive than adhesive failure in both groups. The TEM observation showed an intermediate layer, a matrix-rich layer and a partially demineralized layer in the polyalkenoic acid conditioned group. SIGNIFICANCE: Aging did not reduce the bond strength of the conventional glass-ionomer cement to dentin with or without the use of a polyalkenoic acid conditioner.