Electrochemical Impedance as an Assessment Tool for the Investigation of the Physical and Mechanical Properties of Graphene-Based Cementitious Nanocomposites.

This investigation explores the potential of electrochemical impedance spectroscopy (EIS) in evaluating graphene-based cementitious nanocomposites, focusing on their physical and structural properties, i.e., electrical resistivity, porosity, and fracture toughness. EIS was employed to study cement mixtures with varying graphene nanoplatelet (xGnP) concentrations (0.05-0.40% per dry cement weight), whereas flexural tests assessed fracture toughness and porosimetry analyses investigated the structural characteristics. The research demonstrated that the electrical resistivity initially decreased with increasing xGnP content, leveling off at higher concentrations. The inclusion of xGnPs correlated with an increase in the total porosity of the cement mixtures, which was indicated by both EIS and porosimetry measurements. Finally, a linear correlation emerged between fracture toughness and electrical resistivity, contributing also to underscore the use of EIS as a potent non-destructive tool for evaluating the physical and mechanical properties of conductive nano-reinforced cementitious nanocomposites.

Cement Composites with Graphene Nanoplatelets and Recycled Milled Carbon Fibers Dispersed in Air Nanobubble Water.

The individual effect of nano- and micro-carbon-based fillers on the mechanical and the electrical properties of cement paste were experimentally examined in this study. The objective of the study was to separately examine the effects of size and morphology (platelets and fibers) of nano- and micro-reinforcement. Three different sizes of Graphene Nanoplatelets (GNPs), at contents of 0.05% and 0.20% and recycled milled carbon fibers (rCFs), at various dosages from 0.1-2.5% by weight of cement, were incorporated into the cementitious matrix. GNPs and rCFs were dispersed in water with air nanobubbles (NBs), an innovative method that, compared to common practice, does not require the use of chemicals or high ultrasonic energy. Compressive and bending tests were performed on GNPs- and rCFs-composites. The four-wire-method was used to evaluate the effect of the conductive fillers on the electrical resistivity of cement paste. The compressive and flexural strength of all the cementitious composites demonstrated a considerable increase compared to the reference specimens. Improvement of 269.5% and of 169% was observed at the compressive and flexural strength, respectively, at the GNPs-cement composites incorporating the largest lateral size GNPs at a concentration of 0.2% by weight of cement. Moreover, the rCFs-cement composites increased their compressive and flexural strength by 186% and 210%, respectively, compared to the reference specimens. The electrical resistivity of GNPs- and rCFs-composite specimens reduced up to 59% and 48%, respectively, compared to the reference specimens, which proves that the incorporation of GNPs and rCFs can create a conductive network within the cementitious matrix.