RESUMEN
Measuring chemical concentrations at the surface of implanted medical devices is important for elucidating the local biochemical environment, especially during implant infection. Although chemical indicator dyes enable chemical measurements in vitro, they are usually ineffective when measuring through tissue because the background obscures the dye signal and scattering dramatically reduces the spatial resolution. X-ray excited luminescent chemical imaging (XELCI) is a recent imaging modality which overcomes these limitations using a focused X-ray beam to excite a small spot of red light on scintillator-coated medical implants with well-defined location (because X-rays are minimally scattered) and low background. A spectrochemical indicator film placed over the scintillator layer, e.g., a polymer film containing pH-indicator dyes, absorbs some of the luminescence according to the local chemical environment, and this absorption is then detected by measuring the light intensity/spectrum passing through the tissue. A focused X-ray beam is used to scan point-by-point with a spatial resolution mainly limited by the X-ray beam width with minimum increase from X-ray absorption and scattering in the tissue. X-ray resolution, implant surface specificity, and chemical sensitivity are the three key features of XELCI. Here, we study spatial resolution using optically absorptive targets. For imaging a series of lines, the 20-80% knife-edge resolution was â¼285 (±15) µm with no tissue and 475 ± 18 and 520 ± 34 µm, respectively, through 5 and 10 mm thick tissue. Thus, doubling the tissue depth did not appreciably change the spatial resolution recorded through the tissue. This shows the promise of XELCI for submillimeter chemical imaging through tissue.
RESUMEN
Microbial infections associated with implantable medical devices are a major concern in fracture fixation failure. Early diagnosis of such infection will allow successful eradication with antibiotics without an extra cost for a second surgery. Herein, we describe XELCI as a technique with high X-ray resolution, implant specificity, and chemical sensitivity to noninvasively image chemical concentrations near the surface of implanted medical devices. The devices are coated with chemically reporting surfaces. This chemically responsive surface consists of two layers coated on an implantable medical device; a pH-sensitive layer (bromothymol blue or bromocresol green incorporated hydrogel) which is coated over a red-light emitting scintillator (Gd2O2S: Eu) layer for monitoring. A focused X-ray beam irradiates a spot on the implant, and the red light generated by the scintillator (with 620 nm and 700 nm peaks) is transmitted through the sensing layer which alters the spectral ratio depending on the pH. An image is generated by scanning the X-ray beam across the implant and measuring the spectral ratio of light passing through the tissue point-by-point. We used this imaging technique for monitoring implant-associated infections previously on the bone surface of the femur with a modified implantable plate sensor. Now we are studying pH changes that occur from tibial intramedullary rod infections. Two different types of intramedullary rod designs are used in pre-pilot rabbit studies, and we learned that the XELCI technique could be used to monitor any chemical changes that occur not only on the bone surface but also inside the bone. Thus, this enables noninvasive, high spatial resolution, low background local pH imaging to study implant-associated infection biochemistry.
Asunto(s)
Verde de Bromocresol , Luminiscencia , Animales , Conejos , Rayos X , Azul de Bromotimol , Complicaciones Posoperatorias , Antibacterianos , HidrogelesRESUMEN
We describe a pH-indicating material that can be directly implanted or coated on orthopedic implant surfaces to provide high-spatial-resolution pH mapping through tissue by X-ray excited luminescence chemical imaging (XELCI). This is especially useful for detecting local pH changes during treatment of implant-associated infections. The material has two layers: an X-ray scintillator layer with Gd2O2S:Eu in epoxy, which emits 620 and 700 nm light when irradiated with X-rays, and a pH indicator dye layer, which absorbs some of the 620 nm light in a pH-dependent fashion. To acquire each pixel in the image, a focused X-ray beam irradiates a small region of scintillators and the ratio of 620 to 700 nm light is acquired through the tissue. Scanning the X-ray beam across the implant surface generates high-spatial-resolution chemical measurements. Two associated challenges are (1) to make robust sensors that can be implanted in tissue to measure local chemical concentrations specifically for metal orthopedic implants and (2) to conformally coat the implant surface with scintillators and pH indicator dyes in order to make measurements over a large area. Previously, we have physically pressed or glued a pH-sensitive hydrogel sensor onto the surface of an implant, but this is impractical for imaging over large irregular device areas such as an orthopedic plate with holes and edges. Herein, we describe a chemically sensitive and biocompatible XELCI sensor material that can conformally coat the implant surface. A two-part commercial-grade epoxy resin was mixed with Gd2O2S:Eu and adhered to the titanium surface. Sugar and salt particles were added to the surface of the epoxy as it cured to create a roughened surface and increase the surface area. On this roughened surface, a secondary layer of diacrylated polyethylene glycol (PEG) hydrogel, containing a pH sensitive dye, was polymerized. This combination of epoxy-PEG layers was found to adhere well to the metal implant unlike other previously tested polymer surfaces, which delaminated when exposed to water or humidity. The focused X-ray beam enabled 0.5 mm spatial resolution through 1 cm-thick tissue. The pH sensor-coated orthopedic plate was imaged with XELCI, through tissue, with different pH levels to acquire a calibration curve. The plates were also imaged through tissue, with a low pH region on one section due to growth of a Staphylococcus aureus biofilm. A pH sensor-coated stainless-steel rod with two distinct pH regions was inserted in a rabbit tibia specimen, and the pH was imaged through both bone and soft tissue. These studies demonstrate the use of pH sensor-coated orthopedic plates and rods for mapping the local pH through tissue during biofilm formation by XELCI.
Asunto(s)
Materiales Biocompatibles/química , Sustancias Luminiscentes/química , Animales , Materiales Biocompatibles/farmacología , Biopelículas/efectos de los fármacos , Línea Celular , Supervivencia Celular/efectos de los fármacos , Compuestos Epoxi/química , Gadolinio/química , Hidrogeles/química , Concentración de Iones de Hidrógeno , Ratones , Polietilenglicoles/química , Prótesis e Implantes , Conejos , Acero Inoxidable/química , Staphylococcus aureus/fisiología , Tibia/diagnóstico por imagen , Tibia/patología , Titanio/química , Rayos UltravioletaRESUMEN
Implanted medical device-associated infections are a leading cause of fixation failure, and early diagnosis is the key to successful treatment. During infection, acidosis near the implant plays a role in antibiotic resistance and low pH is a potential infection indicator. Herein, we describe a pH sensor which attaches to the implants to noninvasively image local pH with high spatial resolution. The sensor has two layers: a scintillator layer which emits 620 and 700 nm light upon X-ray irradiation and a pH indicator layer containing bromocresol green dye that absorbs 620 nm luminescence in neutral/basic pH and passes 700 nm light at all pHs. We also developed a dedicated imaging system capable of scanning relatively large specimens through thick tissues. A focused X-ray beam irradiates one spot on the sensor, and the 620 to 700 nm peak ratio is measured to determine the local pH; images are acquired by scanning the X-ray beam across the surface and measuring the pH point-by-point. The sensor was covered with varying thickness slices of chicken breast tissue (0-19 mm) to evaluate how the tissue affects the peak intensity and ratio. Thick tissues attenuated both 620 and 700 nm light, with more attenuation at 620 nm than 700 nm. Although this spectral distortion shifted the pH calibration curve, the effect could be corrected for using a scintillator film region with no pH indicator layer as a spectral reference. The sensor was attached to an orthopedic plate affixed to a human cadaveric tibia and imaged through tissue. This approach provides both high spatial resolution from focused X-ray excitation and surface chemical specificity from the indicator dye, providing a tool for imaging local pH through tissue.
Asunto(s)
Luminiscencia , Imagen Óptica/métodos , Dispositivos de Fijación Ortopédica , Humanos , Concentración de Iones de Hidrógeno , Dispositivos de Fijación Ortopédica/microbiología , Propiedades de Superficie , Rayos XRESUMEN
X-ray excited luminescent chemical imaging (XELCI) uses a combination of X-ray excitation to provide high resolution and optical detection to provide chemical sensing. A key application is to detect and study implant-associated infection. The implant is coated with a layer of X-ray scintillators which generate visible near infrared light when irradiated with an X-ray beam. This light first passes through a pH indicator dye-loaded film placed over the scintillator film in order to modulate the luminescence spectrum according to pH. The light then passes through tissue is collected and the spectral ratio measured to determine pH. A focused X-ray beam irradiates a point in the scintillator film, and a pH image is formed point-by-point by scanning the beam across the sample. The sensor and scanning system are described along with preliminary results showing images in rabbit models.