RESUMEN
The low temperature activity of Fe-loaded zeolites as selective catalytic reduction of NOx by NH3 (NH3 -SCR) catalysts is a critical drawback for practical application. Here, we found unexpected improvement of low temperature activity by our proposed post-synthetic treatment. An Al-rich zeolite beta (Si/Al=5) is employed as the catalyst support, and the parent sample is dealuminated for higher hydrothermal stability, followed by the liquid-mediated stabilization treatment and impregnation. It is found that stabilized samples feature excellent low temperature activity and high N2 selectivity even for a long-term operation, along with the ability to maintain high NOx conversion after aging. The improved SCR activity should be attributed to abundant acid sites in Al-rich framework and better stabilization of monomeric iron species after the stabilization treatment. Furthermore, the low yield of side product N2 O is probably due to the absence of the generation of NH4 NO3 during NH3 -SCR catalyzed by Fe-loaded zeolites.
RESUMEN
Alkaline earth metal cations are ubiquitously present in natural zeolites but less exploited in synthetic zeolites due to their low solubility in water, and hence it remains elusive how they contribute to zeolite formation. Herein, harmotome, a PHI-type zeolite with Ba2+, is readily synthesized from a Ba-containing aluminosilicate glass. This glass-to-zeolite transformation process, in particular the structure-regulating role of Ba2+, is investigated by anomalous X-ray scattering and high-energy X-ray total scattering techniques. The results demonstrate that the steady Ba2+-aluminosilicate interactions not only help prevent the precipitation of barium species under alkaline synthetic conditions, but also dictate the local structures with distinct interatomic distances between the Ba2+ and the surrounding aluminosilicate species throughout the transformation process, which lead to the successful formation of harmotome without detectable impurities. This study highlights the usefulness of the comprehensive X-ray scattering techniques in revealing the formation scheme of the zeolites containing specific metal species. In addition, a promising alternative approach to design and synthesize zeolites with unique compositions and topologies by using well-crafted glasses with suitable metal cation dopants is demonstrated.
RESUMEN
The crystallization mechanism of zeolites remains unclarified to date because of lack of effective techniques in characterizing the local structures of amorphous precursors under synthetic conditions. Herein, in situ high-energy X-ray total scattering measurement with pair distribution function analysis is performed throughout the hydrothermal synthesis of SSZ-13 zeolite to investigate the amorphous-to-crystalline transformation at the sub-nano level in real time. Ordered four-membered rings (4Rs) are dominantly formed during the induction period, prior to the significant increase in the number of symmetric six- and eight-membered rings (6Rs and 8Rs) in the crystal growth stage. These preformed ordered 4Rs contribute to the formation of d6r and cha composite building units containing 6Rs and 8Rs with the assistance of the organic structure-directing agent, leading to the construction of embryonic zeolite crystallites, which facilitate the crystal growth through a particle attachment pathway. This work enriches the toolbox for better understanding the crystallization pathway of zeolites.
Asunto(s)
Zeolitas , Zeolitas/química , Rayos X , Difracción de Rayos X , Cristalización/métodos , Fenómenos FísicosRESUMEN
Interzeolite conversion, which refers to the synthesis of zeolites using a pre-made zeolite as the starting material, has enabled promising outcomes that could not be easily achieved by the conventional synthesis from a mixture of amorphous aluminum and silicon sources. Understanding the mechanism of interzeolite conversion is of particular interest to exploit this synthesis route for the preparation of tailor-made zeolites as well as the discovery of new structures. It has been assumed that the structural similarity between the starting zeolite and the target one is crucial to a successful interzeolite conversion. Nevertheless, an image as to how one type of zeolite evolves into another one remains unclear. In this work, a series of dealuminated FAU zeolites were created through acid leaching and employed as the starting zeolites in the synthesis of AEI zeolite under various conditions. This experimental design allowed us to create a comprehensive diagram of the interzeolite conversion from FAU to AEI as well as to figure out the key factors that enable this kinetically favourable crystallization pathway. Our results revealed different scenarios of the interzeolite conversion from FAU to AEI and pinpointed the importance of the structure of the starting FAU in determining the synthesis outcomes. A prior dealumination was proven effective to modify the structure of the initial FAU zeolite and consequently facilitate its conversion to the AEI zeolite. In addition, this strategy allowed us to directly transfer the knowledge obtained from the interzeolite conversion to a successful synthesis of the AEI zeolite from dealuminated amorphous aluminosilicate precursors. These results offer new insights to the design and fabrication of zeolites via the interzeolite conversion as well as to the understandings of the crystallization mechanisms.
RESUMEN
The crystallization of zeolites, a disorder-to-order transformation of aluminosilicates, has not been thoroughly understood because the nucleation events in the amorphous matrix are difficult to recognize from the diverse structural changes, especially for the dense hydrogel systems. Therefore, relationships between the synthesis conditions, the generated amorphous species, and the crystallization behavior of zeolites remain unclear. Herein, by comparatively investigating the structural evolution of the aluminosilicate matrix in a dense hydrogel system when different Si reactants (fumed silica and silicate solution) are employed, we demonstrate that the reactivity of the reactants and the kinetics of the condensation reaction is critical to the formation of short-range order in an amorphous matrix, which greatly influences the nucleation frequency of zeolites. It was revealed that an amorphous solid containing plentiful Al-rich four-membered rings and Si-rich six-membered rings could be produced when fumed silica gradually reacted with sodium aluminate solution at 80 °C. It is considered that the interaction between these rings promotes the construction of the essential building units of zeolite X (FAU). In contrast, a complex aluminosilicate matrix was formed immediately when sodium silicate solution was mixed with sodium aluminate solution due to the intense condensation reaction. Furthermore, this complex matrix became more stable when the reactant mixture was hydrothermally treated at 80 °C, which significantly impedes the crystallization process. Aging the reactant mixture at ambient temperature before heating, instead, facilitated the formation of short-range order in the amorphous matrix, which increases the nucleation frequency of zeolites.
RESUMEN
Improving the stability of porous materials for practical applications is highly challenging. Aluminosilicate zeolites are utilized for adsorptive and catalytic applications, wherein they are sometimes exposed to high-temperature steaming conditions (â¼1000 °C). As the degradation of high-silica zeolites originates from the defect sites in their frameworks, feasible defect-healing methods are highly demanded. Herein, we propose a method for healing defects to create extremely stable high-silica zeolites. High-silica (SiO2/Al2O3 > 240) zeolites with *BEA-, MFI-, and MOR-type topologies could be stabilized by significantly reducing the number of defect sites via a liquid-mediated treatment without using additional silylating agents. Upon exposure to extremely high temperature (900-1150 °C) steam, the stabilized zeolites retain their crystallinity and micropore volume, whereas the parent commercial zeolites degrade completely. The proposed self-defect-healing method provides new insights into the migration of species through porous bodies and significantly advances the practical applicability of zeolites in severe environments.
RESUMEN
The STW-type zeolite is attractive for developing novel enantioselective syntheses/separation of chiral compounds because it is the only chiral zeolitic microporous material whose enantioenriched synthesis has been achieved. In addition to the conventional industries in which zeolites are used, STW should have diverse industrial applications in the pharmaceutical and food industries. However, the toxic and caustic fluoride required for synthesizing STW severely hinders its commercialization by mass production. Herein, we report the first example of fluoride-free STW synthesis, in which the two roles of fluoride-formation of a zeolitic framework rich in tetravalent T-atoms and promotion of double 4-membered ring unit formation-were substituted by dry gel conversion and Ge addition, respectively. The STW obtained was highly crystalline, with a similar micropore volume and thermal stability as those of original fluoride-based STW. Our approach is promising not only for the fluoride-free synthesis of enantiomeric STW but also for general fluoride-free syntheses.
RESUMEN
Unit-cell-thin zeolitic nanosheets have emerged as fascinating materials for catalysis and separation. The controllability of nanosheet stacking is extremely challenging in the chemistry of two-dimensional zeolitic materials. To date, the organization of zeolitic nanosheets in hydrothermal synthesis has been limited by the lack of tunable control over the guest-host interactions between organic structure-directing agents (OSDAs) and zeolitic nanosheets. A direct synthetic methodology is reported that enables systematic manipulation of the aluminosilicate MWW-type nanosheet stacking. Variable control of guest-host interactions is rationally achieved by synergistically altering the charge density of OSDAs and synthetic silica-to-alumina composition. These finely controlled interactions allow successful preparation of a series of three-dimensional (3D) zeolites, with MWW-layer stacking in wide ranges from variably disorder to fully ordered, leading to tunable catalytic activity in the cracking reaction. These results highlight unprecedented opportunities to modulate zeolitic nanosheets arrangement in 3D zeolites whose structure can be tailored for catalysis and separation.
RESUMEN
Encapsulating metal nanoclusters into zeolites combines the superior catalytic activity of the nanoclusters with high stability and unique shape selectivity of the crystalline microporous materials. The preparation of such bifunctional catalysts, however, is often restricted by the mismatching in time scale between the fast formation of nanoclusters and the slow crystallization of zeolites. We herein demonstrate a novel strategy to overcome the mismatching issue, in which the crystallization of zeolites is expedited so as to synchronize it with the rapid formation of nanoclusters. The concept was demonstrated by confining Pt and Sn nanoclusters into a ZSM-5 (MFI) zeolite in the course of its crystallization, leading to an ultrafast, inâ situ encapsulation within just 5â min. The Pt/Sn-ZSM-5 exhibited exceptional activity and selectivity with stability in the dehydrogenation of propane to propene. This method of ultrafast encapsulation opens up a new avenue for designing and synthesizing composite zeolitic materials with structural and compositional complexity.
RESUMEN
Understanding the properties of zeolites for cation exchange is important because the ion-exchange performance largely determines their suitability in applications such as catalysis and adsorptive separation. We synthesized a Zn(ii)-incorporated mordenite-framework aluminosilicate zeolite (Zn,Al-MOR), in which both Zn and Al are substituted in the framework, and studied its ion-exchange behavior for multivalent cations. For comparison, the original aluminosilicate mordenite (Al-MOR) was also synthesized with a composition adjusted to ensure that its charge density was similar to that of Zn,Al-MOR. While the incorporation of Zn(ii) led to a slower kinetic process, the selectivities and the exchange capacities toward multivalent cations (especially divalent cations) were significantly improved. Herein, we discussed the mechanism responsible for improving the ion-exchange performance in the presence of Zn(ii) and found that the incorporation of Zn(ii) led to a significant improvement in the ion-exchange temperature dependence of the MOR, which led to the ability to enhance ion-exchange capacity through temperature control during actual application. It was also revealed that the presence of Zn(ii) significantly improves selectivity and spontaneity toward the exchange of multivalent cations, Ni2+. Moreover, XRD and nitrogen-adsorption/desorption analyses revealed that the structures of the materials are maintained during the ion exchange, which is indicative of superior structural stability and tolerance to ion exchange.
RESUMEN
The hydrothermal synthesis of zeolites carried out in batch reactors takes a time so long (typically, on the order of days) that the crystallization of zeolites has long been believed to be very slow in nature. We herein present a synthetic process for ZSM-5, an industrially important zeolite, on the order of seconds in a continuous flow reactor using pressurized hot water as a heating medium. Direct mixing of a well-tuned precursor (90 °C) with the pressurized water preheated to extremely high temperature (370 °C) in the millimeter-sized continuous flow reactor resulted in immediate heating to high temperatures (240-300 °C); consequently, the crystallization of ZSM-5 in a seed-free system proceeded to completion within tens of or even several seconds. These results indicate that the crystallization of zeolites can complete in a period on the order of seconds. The subtle design combining a continuous flow reactor with pressurized hot water can greatly facilitate the mass production of zeolites in the future.
RESUMEN
There is broad scientific interest in lamellar zeolitic materials for a large variety of technological applications. The traditional synthetic methods towards two-dimensional (2D) zeolitic precursors have made a great impact in the construction of families of related zeolites; however, the connection between structurally distinct 2D zeolitic precursors is much less investigated in comparison, thereby resulting in a synthetic obstacle that theoretically limits the types of zeolites that can be constructed from each layer. Herein, we report a Ge-recycling strategy for the topotactic conversion between different 2D zeolitic precursors through a three-dimensional (3D) germanosilicate. Specifically, the intermediate germanosilicate can be constructed within 150â min by taking advantage of its structural similarity with the parent lamellar precursor. This process enables the conversion of one 2D zeolite structure into another distinct structure, thus overcoming the synthetic obstacle between two families of zeolitic materials.
RESUMEN
A dedicated apparatus has been developed for studying structural changes in amorphous and disordered crystalline materials substantially in real time. The apparatus, which can be set up on beamlines BL04B2 and BL08W at SPring-8, mainly consists of a large two-dimensional flat-panel detector and high-energy X-rays, enabling total scattering measurements to be carried out for time-resolved pair distribution function (PDF) analysis in the temperature range from room temperature to 873â K at pressures of up to 20â bar. For successful time-resolved analysis, a newly developed program was used that can monitor and process two-dimensional image data simultaneously with the data collection. The use of time-resolved hardware and software is of great importance for obtaining a detailed understanding of the structural changes in disordered materials, as exemplified by the results of commissioned measurements carried out on both beamlines. Benchmark results obtained using amorphous silica and demonstration results for the observation of sulfide glass crystallization upon annealing are introduced.
RESUMEN
Zeolites containing framework heteroatoms (e.g., Ti, Sn, and Hf) with open coordination sites behave as solid-state Lewis acids and exhibit remarkable catalytic properties unachievable with bulk oxides. However, direct evidence confirming the incorporation of such heteroatom species into the zeolite framework is difficult to obtain because of the limited number of analytical methods capable of discerning framework incorporation from extraframework species. In this work, the structural environments of hafnium (Hf) framework and extraframework species added post-synthetically into *BEA zeolites were analyzed using coupled pair distribution function (PDF) and diffuse reflectance (DR) UV-vis measurements. PDF analysis enabled the visualization and identification of framework and extraframework HfOx species, both of which were undetectable by traditional X-ray and neutron diffraction methods. Reactivity data from the aldol condensation of benzaldehyde and acetone confirmed that framework Hf species are responsible for catalytic activity.
RESUMEN
Bimetallic nanoparticle encapsulation in microporous zeolite crystals is a promising route for producing catalysts with unprecedented reaction selectivities. Herein, a novel synthetic approach was developed to produce PtZnx nanoclusters encapsulated inside zeolite micropores by introducing Pt2+ cations into a zincosilicate framework via ion exchange, and subsequent controlled demetallation and alloying with framework Zn. The resulting zeolites featured nanoclusters with sizes of approximately 1â nm, having an interatomic structure corresponding to a PtZnx alloy as confirmed by pair distribution function (PDF) analysis. These materials featured simultaneous shape and substrate specificity demonstrated by the selective production of p-chloroaniline from the competitive hydrogenation of p-chloronitrobenzene and 1,3-dimethyl-5-nitrobenzene.
RESUMEN
We report the first organically synthesized sp-sp3 hybridized porous carbon, OSPC-1. This new carbon shows electron conductivity, high porosity, the highest uptake of lithium ions of any carbon material to-date, and the ability to inhibit dangerous lithium dendrite formation. The new carbon exhibits exceptional potential as anode material for lithium-ion batteries (LIBs) with high capacity, excellent rate capability, long cycle life, and potential for improved safety performance.
RESUMEN
Organic structure-directing agents (OSDAs) have been widely used for the synthesis of zeolites. In most cases, OSDAs are occluded in zeolites as an isolated cation or molecule geometrically fitted within the zeolite cavities. This is not the case for zeolite beta synthesized by using tetraethylammonium (TEA(+)) cation as an OSDA, in which a cluster/aggregate of ca. six TEA(+) cations is occluded intact in the cavity (i.e., the channel intersection) of zeolite beta. The structure direction of TEA(+) in such a nontypical, clustered mode has remained elusive. Here, zeolite beta was hydrothermally synthesized using TEA(+) in the absence of other alkali metal cations in order to focus on the structure-directing behaviors of TEA(+) alone. The solid products formed throughout the hydrothermal synthesis were analyzed by an array of characterization techniques including argon adsorption-desorption, high-energy X-ray total scattering, Raman and solid-state NMR spectroscopy, and high-resolution transmission electron microscopy. It was revealed that the formation of amorphous TEA(+)-aluminosilicate composites and their structural, chemical, and textural evolution toward the amorphous zeolite beta-like structure during the induction period is vital for the formation of zeolite beta. A comprehensive scheme of the formation of zeolite beta is proposed paying attention to the clustered behavior of TEA(+) as follows: (i) the formation of the TEA(+)-aluminosilicate composites after heating, (ii) the reorganization of aluminosilicates together with the conformational rearrangement of TEA(+), yielding the formation of the amorphous TEA(+)-aluminosilicate composites with the zeolite beta-like structure, (iii) the formation of zeolite beta nuclei by solid-state reorganization of such zeolite beta-like, TEA(+)-aluminosilicate composites, and (iv) the subsequent crystal growth. It is anticipated that these findings can provide a basis for broadening the utilization of OSDAs in the clustered mode of structure direction in more effective ways.
RESUMEN
Characteristics of zeolite formation, such as being kinetically slow and thermodynamically metastable, are the main bottlenecks that obstruct a fast zeolite synthesis. We present an ultrafast route, the first of its kind, to synthesize high-silica zeolite SSZ-13 in 10â min, instead of the several days usually required. Fast heating in a tubular reactor helps avoid thermal lag, and the synergistic effect of addition of a SSZ-13 seed, choice of the proper aluminum source, and employment of high temperature prompted the crystallization. Thanks to the ultra-short period of synthesis, we established a continuous-flow preparation of SSZ-13. The fast-synthesized SSZ-13, after copper-ion exchange, exhibits outstanding performance in the ammonia selective catalytic reduction (NH3 -SCR) of nitrogen oxides (NOx ), showing it to be a superior catalyst for NOx removal. Our results indicate that the formation of high-silica zeolites can be extremely fast if bottlenecks are effectively widened.
RESUMEN
The synthesis of zeolites from two-dimensional layered precursors through interlayer crosslinking of the layers is a promising avenue for realizing meticulously designed synthesis routes. However, the presence of defective silanol species in the precursors hinders the achievement of desirable synthesis outcomes. This study focuses on PREFER-a layered precursor for FER-type zeolites-which was synthesized and subjected to a liquid-mediated defect-healing treatment that we recently developed. The defect-healing process involves the use of fluoride compounds for reconstruction and organic pore fillers to stabilize the framework. The effects of the treatment on the structure, composition, and iron insertion behavior of PREFER were examined. Characterization results revealed a reduction in the number of intralayer silanol defects, whereas interlayer silanols were unaffected by the defect-healing treatment. Furthermore, the subsequent alterations observed in the crosslinking behavior with iron atoms indicated that the defect-healing treatment may enhance the insertion of iron species between the layers in more homogeneous environments compared with the untreated precursor. These findings provide valuable insights into the prospects of controlled interlayer linkage in two-dimensional zeolite materials.
RESUMEN
Erionite (ERI) zeolite has recently attracted considerable attention for its application prospect in the selective catalytic reduction of NOx with NH3 (NH3-SCR), provided that the high-silica (Si/Al > 5.5) analog with improved hydrothermal stability can be facilely synthesized. In this work, ERI zeolites with different Si/Al ratios (4.6, 6.4, and 9.1) are synthesized through an ultrafast route, and in particular, a high-silica ERI zeolite with a Si/Al ratio of 9.1 is obtained by using faujasite (FAU) as a starting material. The solid-state 29Si MAS NMR spectroscopic study in combination with a computational simulation allows for figuring out the atomic configurations of the Al species in the three ERI zeolites. It is revealed that the ERI zeolite with the highest Si/Al ratio (ERI-9.1, where the number indicates the Si/Al ratio) exhibits a biased Al occupancy at T1 site, which is possibly due to the presence of a higher fraction of the residual potassium cations in the can cages. In contrast, the Al siting in ERI-4.6 and ERI-6.4 proves to be relatively random.