RESUMEN
The paper presents the effect of diamond particle size (varying between 2.5 µm and 20 µm) on the microstructure, density and hardness of WC-Co/diamond composites. The obtained materials contained 30% vol. diamond. The advanced sintering method Pulse Plasma Sintering (PPS) was used for the production of composites. The sintering process was carried out in two stages at a pressure of 50 and 100 MPa and a temperature of 1050 °C. Depending on the size of the diamond particles, composites with a density of 91-99% were obtained. Microstructure studies were performed employing scanning electron microscopy, along with an analysis of the chemical composition in micro-areas. Additionally, the phase composition was investigated by means of X-ray diffraction. In addition, hardness tests were performed. It was found that the size of the diamond particles significantly influenced the microstructure of the tested materials, as well as the density and hardness. As a result of PPS sintering of composites containing the finest diamond particles (2.5-5 µm), the presence of a metastable type of diamond-graphite was found.
RESUMEN
The study aimed to determine the suitability of agricultural lignocellulosic biomass in the form of vine pruning waste for particleboard production. Two variants of particleboards with densities of 650 kg/m3 and 550 kg/m3 containing a varied amount of vine pruning waste (0, 25, 50 and 100%) were evaluated. The strength (MOR, MOE and IB), thickness swelling and water absorption after immersion in water for 2 and 24 h were tested. The results revealed that vine pruning waste affected the board thickening and reduced strength properties. Boards with a 50% share of waste met the minimum requirements of strength properties specified in the EN 312 standard for boards with a density of 650 kg/m3. However, boards with a density of 550 kg/m3 entirely made with vine pruning waste met the minimum requirements of strength properties of the EN 16368 standard. Moreover, the pruned material reduced axial forces during drilling, swelling and water absorption.
RESUMEN
The paper presents the effect of nitrogen ion implantation on the tool life of the tools commonly used in the furniture industry for drilling particleboards. Nitrogen ions with different accelerating voltages of 25, 40, 55, and 70 kV and a fluence of 5 × 1017 cm-2 were implanted into the surface of commercially available high-speed steel (HSS) drills, using the implanters without mass-separated ion beams. The tests were carried out in a computerized numerical control (CNC) machining center used in the furniture industry. Based on the measurements of the direct tool wear indicator (W), the drill wear curves were determined and the relative tool life index, standard deviation, coefficient of variation, and the implantation quality index of tool life were calculated. The studies have shown that the modification of the drill surface layer by the nitrogen ion implantation process increases the tool life. The obtained results allow the research to be the continued in a wider scope.
RESUMEN
This paper presents the possibility of using the Spark Plasma Sintering (SPS) method to obtain WCCo composite materials. Such materials are used as cutting blades for machining wood-based materials. Two series of composites, different in grain size and cobalt content, were analyzed in the paper. The produced materials were characterized using Scanning Electron Microscopy (SEM), X-ray diffraction (XRD), and tribological properties were determined. In addition, preliminary tests were carried out on the durability of the blades made of sintered WCCo composites while machining three-layer chipboard. The results of the microstructure analysis proved that the SPS method makes it possible to obtain solid composites. Phase analysis showed the occurrence of the following phases: WC, Co, and Co3W9C4. The lowest friction coefficient value was found in samples sintered using powder with an average primary particle size of 400 nm (ultrafine).
RESUMEN
WC-Co (tungsten carbide-cobalt) composites are widely used in industry, wear-resistant parts, and cutting tools. As successful tool materials, WC-Co carbides are widely applied in metal cutting, wear applications, chipless forming, stoneworking, wood, and plastic working. These materials are exposed to severe solid particle erosion by sand particles, such as in the wood industry. During the production of furniture with HDF (High Density Fibreboard), MDF (Medium Density Fibreboard), or OSB (Oriented Strand Board), there are observed problems with tool erosion. Contamination, mainly of the HDF by sand, is quite often, which is why all tools used for the machining of such materials are exposed to erosion by sand particles. Although many studies have been performed on the erosion of various metals, and erosion models exist to predict their erosion behavior, the issue is still relevant. The aim of the study was to determine the effect of grain size (submicron, ultrafine) and the manufacturing technology (SPS-Spark Plasma Sintering, conventional) used on the erosive properties of WC-Co sintered carbides. Sinters produced by the SPS method with different sizes of WC grains and commercial samples were used for the tests. Ten two-hour cycles were carried out under medium conditions of quartz sand and quartz sand with 10% SiC added. Used samples were characterised using scanning electron microscopy (SEM) and roughness was determined. Furthermore, erosion studies allowed individuating a wear mechanism as well as the possibility to foresee cutting performance in prospective application.