RESUMEN
Here, we report photocatalytic CO2 reduction with water to produce methanol using TiO2-passivated InP nanopillar photocathodes under 532 nm wavelength illumination. In addition to providing a stable photocatalytic surface, the TiO2-passivation layer provides substantial enhancement in the photoconversion efficiency through the introduction of O vacancies associated with the nonstoichiometric growth of TiO2 by atomic layer deposition. Plane wave-density functional theory (PW-DFT) calculations confirm the role of oxygen vacancies in the TiO2 surface, which serve as catalytically active sites in the CO2 reduction process. PW-DFT shows that CO2 binds stably to these oxygen vacancies and CO2 gains an electron (-0.897e) spontaneously from the TiO2 support. This calculation indicates that the O vacancies provide active sites for CO2 absorption, and no overpotential is required to form the CO2(-) intermediate. The TiO2 film increases the Faraday efficiency of methanol production by 5.7× to 4.79% under an applied potential of -0.6 V vs NHE, which is 1.3 V below the E(o)(CO2/CO2(-)) = -1.9 eV standard redox potential. Copper nanoparticles deposited on the TiO2 act as a cocatalyst and further improve the selectivity and yield of methanol production by up to 8-fold with a Faraday efficiency of 8.7%.
RESUMEN
A robust and reliable method for improving the photocatalytic performance of InP, which is one of the best known materials for solar photoconversion (i.e., solar cells). In this article, we report substantial improvements (up to 18×) in the photocatalytic yields for CO2 reduction to CO through the surface passivation of InP with TiO2 deposited by atomic layer deposition (ALD). Here, the main mechanisms of enhancement are the introduction of catalytically active sites and the formation of a pn-junction. Photoelectrochemical reactions were carried out in a nonaqueous solution consisting of ionic liquid, 1-ethyl-3-methylimidazolium tetrafluoroborate ([EMIM]BF4), dissolved in acetonitrile, which enables CO2 reduction with a Faradaic efficiency of 99% at an underpotential of +0.78â V. While the photocatalytic yield increases with the addition of the TiO2 layer, a corresponding drop in the photoluminescence intensity indicates the presence of catalytically active sites, which cause an increase in the electron-hole pair recombination rate. NMR spectra show that the [EMIM](+) ions in solution form an intermediate complex with CO2(-), thus lowering the energy barrier of this reaction.
RESUMEN
Integrating plasmon resonant nanostructures with photocatalytic semiconductors shows great promise for high efficiency photocatalytic water splitting. However, the electrochemical instability of most III-V semiconductors severely limits their applicability in photocatalysis. In this work, we passivate p-type GaP with a thin layer of n-type TiO2 using atomic layer deposition. The TiO2 passivation layer prevents corrosion of the GaP, as evidenced by atomic force microscopy and photoelectrochemical measurements. In addition, the TiO2 passivation layer provides an enhancement in photoconversion efficiency through the formation of a charge separating pn-region. Plasmonic Au nanoparticles deposited on top of the TiO2-passivated GaP further increases the photoconversion efficiency through local field enhancement. These two enhancement mechanisms are separated by systematically varying the thickness of the TiO2 layer. Because of the tradeoff between the quickly decaying plasmonic fields and the formation of the pn-charge separation region, an optimum performance is achieved for a TiO2 thickness of 0.5 nm. Finite difference time domain (FDTD) simulations of the electric field profiles in this photocatalytic heterostructure corroborate these results. The effects of plasmonic enhancement are distinguished from the natural catalytic properties of Au by evaluating similar photocatalytic TiO2/GaP structures with catalytic, non-plasmonic metals (i.e., Pt) instead of Au. This general approach of passivating narrower band gap semiconductors enables a wider range of materials to be considered for plasmon-enhanced photocatalysis for high efficiency water splitting.