Fluorescent property of carbon dots extracted from cigarette smoke and the application in bio-imaging.

Cigarette smoke is one of the six major pollution sources in the room air. It contains large number of particles with size less than 10 nm. There exist carbon dots (CDs) in cigarette smoke which have strong fluorescence and with good bio-compatibility and low toxicity. CDs in cigarette smoke can be applied in bio-imaging which has great potential applications in the integration of cancer diagnosis and treatment. In this paper, CDs were extracted from cigarette smoke. Then, sodium borohydride was added to CDs aqueous solution for reduction and the reduced CDs (R-CDs) were used for biological cell imaging. The results indicate that the CDs with the particle size <10 nm in cigarette smoke are self-assembled by the polymerizated polycyclic aromatic hydrocarbons (PAHs) and ammonium nitrite which are disk nano-structure composed of sp2/sp3 carbon and oxygen/nitrogen groups or polymers. Sodium borohydride can reduce the carbonyl group on the surface of CDs to hydroxyl group and increase the ratio of the Na 1s ratio of the CDs from 1.86 to 7.42. The CDs can emit blue fluorescence under ultraviolet irradiation. After reduction, the R-CDS have the intensity of fluorescence 7.2 times than before and the fluorescence quantum yield increase from 6.13% to 8.86%. The photoluminescence (PL) wavelength of R-CDS have red-shift of 7 nm which was due to the increasing of Na element ratio. The onion epidermal cells labeled with R-CDs show that the CDs could pass through the cell wall into the cell and reach the nucleus. The cell wall and the nucleus could be clearly visualized. CDs also shows low toxicity to human bronchial epithelial cells (BEAS-2B) with good biological activity. The obtained results indicate that the CDs and R-CDs have good fluorescent property which could be used as bio-imaging agent.

Preparation and Fluorescent Wavelength Control of Multi-Color Nitrogen-Doped Carbon Nano-Dots.

It is known that, by taking advantage of heteroatom doping, the electronic states and transition channels in carbon nano-dots (CNDs) can be effectively modulated. Thus, the photoluminescence (PL) properties of CNDs can be changed. For potential applications of CNDs as advanced materials for optoelectronic devices, it is important and significant to develop the practical techniques for doping heteroatoms into CNDs. In this work, we synthesize the multi-color fluorescent by using a fast and effective microwave method where the CNDs are nitrogen-doped. We examine the influence of different ratios of the raw materials on the structure and optical properties of N-CNDs. The results show that the prepared N-CNDs can generate blue (445 nm), green (546 nm), and orange (617 nm) fluorescence or PL with the mass ratio of the raw materials at 1:1, 1:2 and 1:3, respectively. We find that the N content in N-CNDs leads to different surface/edge states in n-π∗ domain. Thus, the wavelength of the PL emission from N-CNDs can be tuned via controlling the N concentration doped into the CNDs. Moreover, it is shown that the intensity of the PL from N-CNDs is mainly positively related to the content of C-O groups attached on the surface/edges of the N-CNDs. This study provides an effective experimental method and technical way to improve the fluorescent emission, and to modulate the color of the PL emission from CNDs.